US4359567A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermooxidatively stable articulated p-benzobisoxazole and p-benzobisthiazole polymers
Assignee: United States Department of the Air Force
•
Filing: 1981-10-02
•
Granted: 1982-11-16
•
Expires: 2001-10-02
Abstract
Abstract Articulated p-benzobisoxazole and p-benzobisthiazole polymers which contain a limited number of 3,3'-biphenyl or 2,2'-bipyridyl segments are synthesized, with inherent viscosities as high as 14 dl/g being recorded. The 3,3'-biphenyl or 2,2'-bipyridyl segments in the p-benzobisoxazole and p-benzobisthiazole polymers impart flexibility to the polymers without adversely affecting the thermooxidative stability. While the resultant articulated polymers exhibit liquid crystalline behavior in methanesulfonic acid and form strong cast films from that solvent, they also exhibit thermooxidative stability comparable to other p-benzobisthiazole and p-benzobisoxazole polymers. The resultant films are useful for the fabrication of high strength laminates to be used in severe environment structural applications.
Inventors
- 👤 Robert C. Evers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 04:33
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/22; C08G75/00; C08G75/32
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
64 words
A thermooxidatively stable articulated polymer consisting essentially of recurring units having one of the following formulae: ##STR45## wherein Ar is a phenylene radical, Ar' is selected from the group consisting of biphenylene and bipyridylene radicals, and wherein the molar proportion of a ranges from about 0.80 to 0.97, b ranges from about 0.03 to 0.20, and the sum of a and b equals one.
Claim 2
Dependent Claim
64 words
A thermooxidatively stable articulated polymer consisting essentially of recurring units having one of the following formulae: ##STR45## wherein Ar is a phenylene radical, Ar' is selected from the group consisting of biphenylene and bipyridylene radicals, and wherein the molar proportion of a ranges from about 0.80 to 0.97, b ranges from about 0.03 to 0.20, and the sum of a and b equals one.
Claim 3
Dependent Claim
14 words
A polymer according to claim 1, comprising p-benzobisoxazole wherein Ar' is chosen from ##STR46##
Claim 4
Dependent Claim
14 words
A polymer according to claim 1, comprising p-benzobisthiazole wherein Ar' is chosen from ##STR47##
Claim 5
Independent Claim
126 words
A method for preparing a thermooxidatively stable articulated polymer consisting essentially of recurring units having one of the following formulae: ##STR48## wherein Ar is a phenylene radical, Ar' is selected from the group consisting of biphenylene and bipyridylene radicals, and wherein the molar proportion of a ranges from 0.80 to 0.97, b ranges from 0.03 to 0.20, and the sum of a plus b equals one, comprising: combining one of 2,5-diamino-1,4-benzenedithiol dihydrochloride and 4,6-diamino-resorcinol dihydrochloride, with an equimolar amount of the combination of terephthalic acid and one of 3,3'-biphenyl dicarboxylic acid chloride, 3,3'-biphenyl dicarboxylic acid and 2,2'-bipyridyl-4,4'-dicarboxylic acid chloride, in the presence of polyphosphoric acid, wherein the molar ratio of said terephthalic acid to said Ar' moieties is in the approximate range of 0.80:0.20 to 0.97:0.03.
Claim 6
Independent Claim
126 words
A method for preparing a thermooxidatively stable articulated polymer consisting essentially of recurring units having one of the following formulae: ##STR48## wherein Ar is a phenylene radical, Ar' is selected from the group consisting of biphenylene and bipyridylene radicals, and wherein the molar proportion of a ranges from 0.80 to 0.97, b ranges from 0.03 to 0.20, and the sum of a plus b equals one, comprising: combining one of 2,5-diamino-1,4-benzenedithiol dihydrochloride and 4,6-diamino-resorcinol dihydrochloride, with an equimolar amount of the combination of terephthalic acid and one of 3,3'-biphenyl dicarboxylic acid chloride, 3,3'-biphenyl dicarboxylic acid and 2,2'-bipyridyl-4,4'-dicarboxylic acid chloride, in the presence of polyphosphoric acid, wherein the molar ratio of said terephthalic acid to said Ar' moieties is in the approximate range of 0.80:0.20 to 0.97:0.03.
Claim 7
Dependent Claim
41 words
A method according to claim 4 including heating the combination of ingredients in the presence of polyphosphoric acid to form a viscous reaction mixture, cooling the viscous reaction mixture and washing the viscous reaction mixture with water to extract the polymer.
Claim 8
Dependent Claim
85 words
The method of claim 4 wherein said diamino compound and said terephthalic acid are mixed with polyphosphoric acid and the resulting mixture is heated to a temperature in the range of about 70° to 130° C. for a period of about 3 to 24 hours, said difunctional 3,3'-biphenyl or 2,2'-bipyridyl monomer is thereafter added to the reaction mixture, and the resulting mixture is heated to a temperature in the range of about 150° to 225° C. for a period of about 36 to 96 hours.
References Cited (Backward Citations)
US3313783A
Cited
US4084048A
Cited
US4064109A
Cited
US4115367A
Cited
US4142037A
Cited
US4147858A
Cited
US4229566A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-15 | 1986-05-17 | 1986-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-15 | 1990-05-17 | 1990-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-15 | 1994-05-17 | 1994-11-16 | $7700.00 | Window Closed / Lapsed |