Flexible printed circuit base board and method for producing the same
Assignee: Sumitomo Bakelite Co Ltd
•
Filing: 1979-06-13
•
Granted: 1982-10-12
•
Expires: 1999-06-13
Abstract
Abstract There are disclosed a flexible printed circuit base board produced as an elemental material suitable for a flexible printed circuit board by coating a heat-resistant resin composition composed of a heat-resistant resin having a heterocyclic ring and an epoxy resin dissolved in an organic solvent on a metal foil and drying it to form a film directly on said foil, and a method for producing the same. Said flexible printed circuit base board is more excellent in heat resistance, flame retardancy, adhesiveness, electric insulation, and heat deterioration characteristics than the conventional base board obtained by integrating a heat-resistant film and a metal foil through an adhesive. These properties are of great importance in practical applications of the printed circuit base board. As compared with the conventional products, the production is easy, and hence, the present base board can be produced at a low cost. This base board is not only usable for various types of flexible printed circuit boards but also the film per se obtained from the base board can be used in a field in which a film is used.
Inventors
- 👤 Sigenori Yamaoka
- 👤 Akinobu Kusuhara
- 👤 Toshinaga Endo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:55
CPC Classifications
H; H05; H05K; H05K1/00; C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/42; C08G59/4246; C08G59/4269; C08L; C08L63/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0346; H05K1/0353; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/31504; Y10T428/31511; Y10T428/31525; Y10T428/31529; Y10T428/31678; Y10T428/31681; Y10T428/31721; Y10T428/31725
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
129 words
A method for producing a flexible printed circuit base board, characterized by coating an organic solvent solution of a second heat-resistant resin consisting essentially of the reaction product of (1) a first heat-resistant resin having a molecular weight of at least about 5,000 and a heterocylic ring, selected from the group consisting of polyimide, polyesterimide, polyhydantoin, polyimidazopyrrolone, polybenzimidazole and polyparabanic acid imide, these having in their molecule groups reactive with epoxy group, with (2) an epoxy resin having at least two epoxy groups in the molecule, on a metal foil having good electrical conductivity and a thickness of 1 to 150μ; and drying and curing the same to form a flexible cured film of said resin composition having a thickness of 0.5 to 300μ on said metal foil surface.
Claim 2
Independent Claim
129 words
A method for producing a flexible printed circuit base board, characterized by coating an organic solvent solution of a second heat-resistant resin consisting essentially of the reaction product of (1) a first heat-resistant resin having a molecular weight of at least about 5,000 and a heterocylic ring, selected from the group consisting of polyimide, polyesterimide, polyhydantoin, polyimidazopyrrolone, polybenzimidazole and polyparabanic acid imide, these having in their molecule groups reactive with epoxy group, with (2) an epoxy resin having at least two epoxy groups in the molecule, on a metal foil having good electrical conductivity and a thickness of 1 to 150μ; and drying and curing the same to form a flexible cured film of said resin composition having a thickness of 0.5 to 300μ on said metal foil surface.
Claim 3
Dependent Claim
37 words
A method for producing a flexible printed circuit base board according to claim 1, wherein the epoxy resin containing at least two epoxy groups in the molecule has a molecular weight of not less than about 800.
Claim 4
Dependent Claim
66 words
A method for producing a flexible printed circuit base board according to claim 1 or 2, wherein a resin composition consisting of 100 parts by weight of a heat-resistant resin having a molecular weight of not less than about 5,000 and a heterocyclic ring and 0.1 to 30 parts by weight of an epoxy resin containing at least two epoxy groups in the molecule is used.
Claim 5
Dependent Claim
47 words
A method according to claim 1 wherein said organic solvent solution of said second resin composition is formed by first heating while agitating to effect reaction between said first resin and said epoxy resin; and the resultant second resin composition is then admixed with said organic solvent.
Claim 6
Dependent Claim
48 words
A method according to claim 4 wherein said solvent is selected from the group consisting of dimethylacetamide, dimethylformamide, dimethylsulfoxide, N-methylpyrrolidone, γ-butyrolactone, caprolactone, pyridine, piperidine, phenol, cresol, dichloromethane, dioxane, tetrahydrofuran, toluene, xylene, solvent naphtha, ketones including acetone, methyl ethyl ketone, alcohols including methyl alcohol, ethyl alcohol, and mixtures thereof.
Claim 7
Dependent Claim
24 words
A method according to claim 4 wherein said organic solvent solution of said second resin composition comprises 5-70% by weight of said resin composition.
Claim 8
Dependent Claim
28 words
A method according to claim 4 wherein said first heat-resistant resin and said epoxy resin are agitated at 15° to 150° C. for thirty minutes to ten hours.
Claim 9
Dependent Claim
27 words
A method according to claim 7 wherein said drying and curing is effected at a temperature of 50° to 450° C. for two minutes to twenty-five hours.
Claim 10
Dependent Claim
140 words
A flexible printed circuit base board consisting essentially of a metal foil having good electrical conductivity and a thickness of 1 to 150μ; and a flexible film of a cured resin consisting essentially of the reaction product of a heat-resistant resin having a molecular weight of at least about 5,000 and a heterocyclic ring, selected from the group consisting of polyimide, polyesterimide, polyhydantoin, polyimidazopyrrolone, polybenzimidazole and polyparabanic acid imide, these having in their molecule groups reactive with epoxy group, and an epoxy resin containing at least two epoxy groups in the molecule, said film having a thickness of 0.5 to 300μ, said metal foil and said resin film being bonded directly to each other through no adhesive, and wherein said metal foil is selected from the group consisting of copper foil, aluminum foil, nicrome foil, nickel foil, and titanium foil.
Claim 11
Dependent Claim
140 words
A flexible printed circuit base board consisting essentially of a metal foil having good electrical conductivity and a thickness of 1 to 150μ; and a flexible film of a cured resin consisting essentially of the reaction product of a heat-resistant resin having a molecular weight of at least about 5,000 and a heterocyclic ring, selected from the group consisting of polyimide, polyesterimide, polyhydantoin, polyimidazopyrrolone, polybenzimidazole and polyparabanic acid imide, these having in their molecule groups reactive with epoxy group, and an epoxy resin containing at least two epoxy groups in the molecule, said film having a thickness of 0.5 to 300μ, said metal foil and said resin film being bonded directly to each other through no adhesive, and wherein said metal foil is selected from the group consisting of copper foil, aluminum foil, nicrome foil, nickel foil, and titanium foil.
Claim 12
Dependent Claim
15 words
A flexible printed circuit base board according to claim 9 wherein said foil is metal-plated.
Claim 13
Dependent Claim
25 words
A flexible printed circuit base board according to claim 9 wherein said metal foil surface in contact with said film of cured resin is roughened.
Claim 14
Dependent Claim
28 words
A flexible printed circuit base board according to claim 9 wherein said heat-resistant resin having a heterocyclic ring is selected from the group consisting of polyimide, and polyesterimide.
Claim 15
Dependent Claim
24 words
A flexible printed circuit base board according to claim 9 wherein said said heat-resistant resin has a molecular weight of about 5,000 to 200,000.
Claim 16
Dependent Claim
22 words
A flexible printed circuit base board according to claim 13 wherein said heat-resistant resin has a molecular weight of 8,000 to 100,000.
Claim 17
Dependent Claim
24 words
A flexible printed circuit base board according to claim 13 wherein said epoxy resin has a molecular weight of from about 800 to 10,000.
Claim 18
Dependent Claim
48 words
A flexible printed circuit base board according to claim 9 wherein said flexible cured resin film further contains a small amount of at least one adjuvant selected from the group consisting of a flexibility-imparting agent, an anti-oxidant, a filler, a coloring material, a flame retardant, and mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-11 | 1986-04-12 | 1986-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-11 | 1990-04-12 | 1990-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-11 | 1994-04-12 | 1994-10-12 | $7700.00 | Window Closed / Lapsed |