Fabrication of electroluminescent semiconductor device utilizing selective etching and epitaxial deposition
Assignee: Uniphase Opto Holdings Inc
•
Filing: 1980-04-18
•
Granted: 1982-07-27
•
Expires: 2000-04-18
Abstract
Abstract An electroluminescent semiconductor device such as a semiconductor laser has epitaxial monocrystalline layers (3 to 6), including an active layer (4), grown on a substrate (2). The epitaxial layers are etched in the presence of an etching mask (8) to form nonplanar mirror surfaces (9) which in the longitudinal direction bound active regions (10). To form flat and parallel mirrors (12) an epitaxial monocrystalline protective layer (11) is grown from the gaseous phase on the mirror surfaces after etching. The etching can be carried out in two stages using different etchants. With the first etchant the etched layers taken on a swallow-tail profile and then with the second etchant they take on a concave profile.
Inventors
- 👤 Rudolf P. Tijburg
- 👤 Teunis van Dongen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:42
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/80; H10H20/84; H10H20/81; H10H20/811; H10H20/822; H10H20/824; Y; Y10; Y10S; Y10S438/00; Y10S438/978
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
95 words
A method of manufacturing a semiconductor laser device, which comprises: providing a semiconductor substrate having a major surface; growing a plurality of monocrystalline epitaxial layers, including an active layer, on said major surface; providing an etching mask on top of said monocrystalline epitaxial layers; etching the masked monocrystalline epitaxial layers to form a plurality of epitaxial layer segments having nonplanar mirror surfaces which bound segments of said active layer in the lateral direction; and then growing epitaxial monocrystalline protective layers having substantially planar and parallel surfaces on said nonplanar mirror surfaces from the gaseous phase.
Claim 2
Independent Claim
95 words
A method of manufacturing a semiconductor laser device, which comprises: providing a semiconductor substrate having a major surface; growing a plurality of monocrystalline epitaxial layers, including an active layer, on said major surface; providing an etching mask on top of said monocrystalline epitaxial layers; etching the masked monocrystalline epitaxial layers to form a plurality of epitaxial layer segments having nonplanar mirror surfaces which bound segments of said active layer in the lateral direction; and then growing epitaxial monocrystalline protective layers having substantially planar and parallel surfaces on said nonplanar mirror surfaces from the gaseous phase.
Claim 3
Dependent Claim
27 words
A method as claimed in claim 1, in which the monocrystalline epitaxial layers are etched in a direction selected from the [011] direction and the [010] direction.
Claim 4
Dependent Claim
64 words
A method as claimed in claim 1 or 2, in which the active layer comprises a material selected from the materials gallium arsenide and gallium aluminum arsenide, and the layers situated above and below the active layer comprise gallium aluminum arsenide of mutually opposite conductivity types and having an aluminum content which is at least 25 atom% larger than that of the active layer.
Claim 5
Dependent Claim
28 words
A method as claimed in claim 3, in which the protective layer comprises isolating gallium aluminum arsenide having an aluminum content which exceeds that of the active layer.
Claim 6
Dependent Claim
25 words
A method as claimed in claim 1, in which, viewed in the laterial direction, the monocrystalline epitaxial layers are etched to obtain concave mirror surfaces.
Claim 7
Dependent Claim
44 words
A method as claimed in claim 5, wherein the monocrystalline epitaxial layers are etched to obtain said concave surfaces by first etching with a first etchant to obtain a swallow-tail profile and then nonpreferentially etching with a second etchant to obtain said concave surfaces.
References Cited (Backward Citations)
US3887404A
Cited
US3824493A
Cited
US3865646A
Cited
US4121177A
Cited
US4144503A
Cited
US4178564A
Cited
US4171234A
Cited
US4137107A
Cited
US4230997A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-26 | 1986-01-25 | 1986-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-26 | 1990-01-25 | 1990-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-26 | 1994-01-25 | 1994-07-27 | $7700.00 | Window Closed / Lapsed |