High strength aggregate for concrete
Assignee: WR Grace and Co Conn
•
Filing: 1981-02-17
•
Granted: 1982-06-22
•
Expires: 2001-02-17
Abstract
Abstract Concretes containing a hydratable cementitious binder such as Portland cement and a high strength aggregate material are described. The high strength aggregate material is produced from hydrated cementitious compositions which contain relatively low proportions of Portland cement and relatively high proportions of a select fly ash component. The high strength aggregate material is produced by mixing the aforementioned Portland cement and fly ash components with water and allowing such to hydrate. The hydrated aggregate product may then be reduced in size (e.g. by crushing) and screened prior to combination with the cementitious binder to produce concrete compositions. Concretes can be prepared with such aggregate which have at least comparable compressive strengths to concrete prepared using conventional crushed stone aggregate.
Inventors
- 👤 Vance H. Dodson
- 👤 Lawrence R. Roberts
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 14:13
CPC Classifications
C; C04; C04B; C04B18/00; C04B18/02; C04B18/021; Y; Y10; Y10S; Y10S106/00; Y10S106/01; Y10S588/00; Y10S588/901
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
127 words
A cementitious concrete composition comprising a mixture of solid, particulate aggregate material of high strength and a cementitious binder therefor, said aggregate being comprised of particles of a hydrated mixture of Portland cement and fly ash wherein said Portland cement and fly ash are present in a weight ratio of from 1 part cement to at least one part ash, said fly ash upon analysis having a total calcium oxide content greater than about 10 percent by weight, the total additive amount of SiO 2 , Al 2 O 3 and Fe 2 O 3 present in said fly ash being less than about 80 percent by weight, said fly ash further not having been first treated to promote activity prior to mixture with said Portland cement.
Claim 2
Dependent Claim
127 words
A cementitious concrete composition comprising a mixture of solid, particulate aggregate material of high strength and a cementitious binder therefor, said aggregate being comprised of particles of a hydrated mixture of Portland cement and fly ash wherein said Portland cement and fly ash are present in a weight ratio of from 1 part cement to at least one part ash, said fly ash upon analysis having a total calcium oxide content greater than about 10 percent by weight, the total additive amount of SiO 2 , Al 2 O 3 and Fe 2 O 3 present in said fly ash being less than about 80 percent by weight, said fly ash further not having been first treated to promote activity prior to mixture with said Portland cement.
Claim 3
Dependent Claim
26 words
The concrete composition of claim 1 wherein said ratio of cement to fly ash is from 1 part cement to at least 1.5 parts fly ash.
Claim 4
Dependent Claim
21 words
The concrete composition of claim 1 wherein said aggregate comprises particles the diameter of which is less than about three inches.
Claim 5
Dependent Claim
25 words
The concrete composition of claim 1 wherein said aggregate is present in an amount greater than about 50 percent by volume of the total composition.
Claim 6
Dependent Claim
19 words
The concrete composition of claim 1 to which is additionally added sufficient water to render the dry mixture plastic.
Claim 7
Dependent Claim
30 words
A dense, hard, hydrated concrete mass produced by addition of water to a dry mixture of the components of claim 1 and thereafter allowing the resulting wet mixture to harden.
Claim 8
Dependent Claim
44 words
The composition of claim 1 wherein said fly ash exhibits the following chemical analysis: ______________________________________
APPROXIMATE
COMPONENTS % BY WEIGHT
______________________________________
SiO.sub.2 24.1-43.1
Al.sub.2 O.sub.3 14.3-27.5
Fe.sub.2 O.sub.3 4.2-9.5
SiO.sub.2 + Al.sub.2 O.sub.3 + Fe.sub.2 O.sub.3
47.9-72.4
CaO 16.8-29.6
MgO 3.7-8.5
SO.sub.3 1.6-6.4
______________________________________
Claim 9
Dependent Claim
43 words
The concrete composition of claim 1 wherein said calcium oxide content is greater than about 15 percent by weight, and said total additive amount of Si 2 O, Al 2 O 3 and Fe 2 O 3 is less than about 75 percent.
Claim 10
Dependent Claim
11 words
The composition of claim 1 wherein said binder is Portland cement.
Claim 11
Dependent Claim
45 words
The composition of claim 1 wherein said aggregate is a particulate product produced by first mixing said Portland cement, said fly ash and water and allowing such mixture to hydrate, and thereafter reducing the size of the hydrated product to a desired particle size range.
Claim 12
Independent Claim
156 words
The method of producing a solid, particulate material of high strength and suitable for use as an aggregate in cementitious concrete compositions, said method comprising the steps of preparing mixtures of Portland cement, fly ash and water and thereafter causing hydration of such mixtures and recovering the hydrated product in the form of solid particles having a diameter of less than about three inches, said Portland cement and fly ash being present in said mixtures in a weight ratio of from 1 part cement to at least 1 part ash, said fly ash upon analysis having a total calcium oxide content greater than about 10 percent by weight, the total additive amount of SiO 2 , Al 2 O 3 and Fe 2 O 3 present in said fly ash being less than about 80 percent by weight, said fly ash further not having been first treated to promote activity prior to incorporation in said mixture.
Claim 13
Independent Claim
156 words
The method of producing a solid, particulate material of high strength and suitable for use as an aggregate in cementitious concrete compositions, said method comprising the steps of preparing mixtures of Portland cement, fly ash and water and thereafter causing hydration of such mixtures and recovering the hydrated product in the form of solid particles having a diameter of less than about three inches, said Portland cement and fly ash being present in said mixtures in a weight ratio of from 1 part cement to at least 1 part ash, said fly ash upon analysis having a total calcium oxide content greater than about 10 percent by weight, the total additive amount of SiO 2 , Al 2 O 3 and Fe 2 O 3 present in said fly ash being less than about 80 percent by weight, said fly ash further not having been first treated to promote activity prior to incorporation in said mixture.
Claim 14
Dependent Claim
39 words
The method of claim 11 comprising the steps of preparing said mixtures of said cement, ash and water, forming said wet mixtures into solid, hydrated products, and thereafter reducing the size of the hydrated products to a desired value.
Claim 15
Dependent Claim
14 words
The method of claim 12 wherein said reduction in size is accomplished by crushing.
Claim 16
Dependent Claim
30 words
The method of claim 11 wherein pellets of said mixtures of said cement, ash and water are caused to be produced which are thereafter hydrated to form solid hardened particles.
Claim 17
Dependent Claim
31 words
The method of claim 11 wherein said mixtures of said cement, ash and water are shaped by extrusion and the extruded shapes thereafter reduced in size before or after hydration thereof.
Claim 18
Independent Claim
23 words
The method of any of the claims 11 through 15 wherein the recovered hydrated product is screened to produce a desired particle size.
References Cited (Backward Citations)
US2414734A
Cited
US2948947A
Cited
US3030222A
Cited
US3192060A
Cited
US3245812A
Cited
US3328180A
Cited
US3634115A
Cited
US3852084A
Cited
US3717490A
Cited
US3802899A
Cited
US3957528A
Cited
US4018619A
Cited
DE2547908A1
Cited
US4018617A
Cited
US4101332A
Cited
US4210457A
Cited
US4240952A
Cited
US4250134A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-21 | 1985-12-21 | 1986-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-21 | 1989-12-21 | 1990-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-21 | 1993-12-21 | 1994-06-22 | $7700.00 | Window Closed / Lapsed |