Method of making concrete from fly ash

Assignee: EJ EAGLETON
•
Filing: 1979-01-15
•
Granted: 1980-12-23
•
Expires: 1999-01-15
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract In a method of making concrete of the Portland Cement type wherein a quantity of cementitious material, such as Portland Cement, is mixed with a quantity of aggregate, generally sand and rock in varying proportions and water; and, wherein, the resulting mixture is stirred or mixed for an appropriate length of time consistent with acceptable practices in the concrete industry after which the mix is poured and allowed to set, the improvement which is characterized by the employment of fly ash as the major ingredient in the cementitious material. The improvement also includes the adding of gypsum to the initial mix in an amount equal to about 2% by weight of the fly ash and, thereafter, adding in and mixing a quantity of calcium chloride equal to about 3% by weight of the fly ash. As an added feature, a quantity of organic material, such as a latex emulsion, can be added to the initial mix to improve the flow characteristics of the concrete mix and to improve the physical characteristics of the ultimate concrete.

Inventors

  • 👤 Clarence E. Hulbert, Jr.
  • 👤 Liang-Tseng Fan
  • 👤 Mufit Akinc

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-29 20:50
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B28/04; C04B7/00; C04B7/24; C04B7/26; Y; Y02; Y02P; Y02P40/00; Y02P40/10; Y02W; Y02W30/00; Y02W30/50; Y02W30/91; Y10; Y10S; Y10S106/00; Y10S106/01

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 77 words
A method of making concrete which comprises the steps of mixing together a quantity of a cementitous material which includes fly ash as a major ingredient therein, a quantity of aggregate, a quantity of gypsum equal to about 2% by weight of the fly ash and water to form an initial mix, thereafter adding calcium chloride in an amount equal to about 3% by weight of the fly ash, further mixing and pouring the same to set.
Claim 2
Independent Claim 77 words
A method of making concrete which comprises the steps of mixing together a quantity of a cementitous material which includes fly ash as a major ingredient therein, a quantity of aggregate, a quantity of gypsum equal to about 2% by weight of the fly ash and water to form an initial mix, thereafter adding calcium chloride in an amount equal to about 3% by weight of the fly ash, further mixing and pouring the same to set.
Claim 3
Dependent Claim 89 words
A method of making concrete as set forth in claim 1 which comprises the steps of mixing together 140 parts by weight of Portland Cement, 560 parts of fly ash, 1000 parts of sand, 2000 parts of rock, 11 parts of gypsum and 160 parts of water, mixing the above ingredients together, adding to the above ingredients 173 parts of a calcium chloride solution obtained by mixing 16 parts of calcium chloride with about 157 parts of water, further mixing the resulting mixture and pouring the same to set.
Claim 4
Dependent Claim 34 words
A method of making concrete as set forth in claim 2 which includes adding to the initial mix approximately 10 parts by weight of a latex emulsion formed from styrene and 1, 3 butadiene.
Claim 5
Dependent Claim 88 words
A method of making concrete as set forth in claim 1 which includes mixing together 140 parts by weight of Portland Cement, 560 parts of fly ash, 1200 parts of sand, 1800 parts of rock, 11 parts of gypsum, and 160 parts of water, mixing the above ingredients together, adding to the above mix 173 parts of a calcium chloride solution prepared by mixing together 16 parts of calcium chloride with approximately 157 parts of water, further mixing the above resulting mixture and pouring the same to set.
Claim 6
Dependent Claim 34 words
A method of making concrete as set forth in claim 4 which includes adding to the initial mix approximately 10 parts by weight of a latex emulsion formed from styrene and 1, 3 butadiene.
Claim 7
Dependent Claim 31 words
A method of making concrete as set forth in claim 1 wherein the cementitous material includes approximately 20% by weight of Portland Cement and approximately 80% by weight of fly ash.

References Cited (Backward Citations)

US2752261A Cited
GB940692A Cited
US3565548A Cited
US3895953A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1983-12-23 1984-06-23 1984-12-23 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1987-12-23 1988-06-23 1988-12-23 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1991-12-23 1992-06-23 1992-12-23 $7700.00 Window Closed / Lapsed