Single mode fibre and method of making
Assignee: Nortel Networks Ltd
•
Filing: 1980-10-29
•
Granted: 1982-06-22
•
Expires: 2000-10-29
Abstract
Abstract Single mode optical fibre for operation in the wavelength range 1.5 to 1.7 microns is made by depositing a cladding glass layer and then a core glass layer upon the bore of a silica substrate tube. The bore of the coated tube is then collapsed to form a solid cross-section optical fibre preform. The cladding glass has an index matching that of silica and either contains no oxide of phosphorus or the minimal amount to provide a low enough deposition temperature and high enough deposition rate to provide an acceptably low diffusion of hydroxyl groups from the material of the substrate tube. Optionally the deposition of the cladding may be preceded by the deposition of a diffusion barrier layer which may contain a higher proportion of oxide of phosphorus.
Inventors
- 👤 Philip W. Black
- 👤 John Irven
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:19
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03C; C03C13/00; C03C13/04; C03C13/045; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/24; Y; Y10; Y10S; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
94 words
A method of making an optical fiber preform suitable for use in the manufacture of single mode optical fiber, comprising the steps of: despositing, by vapor reaction, on the bore of a silica substrate tube, a layer of fluorine doped silica cladding glass containing at least 0.5 mole % germania and having a refractive index not exceeding that of pure silica; depositing, by vapor reaction, on said layer of cladding glass, a layer of germania doped silica core glass; and, collapsing the bore of the tube to form a solid cross-section optical fiber preform.
Claim 2
Independent Claim
94 words
A method of making an optical fiber preform suitable for use in the manufacture of single mode optical fiber, comprising the steps of: despositing, by vapor reaction, on the bore of a silica substrate tube, a layer of fluorine doped silica cladding glass containing at least 0.5 mole % germania and having a refractive index not exceeding that of pure silica; depositing, by vapor reaction, on said layer of cladding glass, a layer of germania doped silica core glass; and, collapsing the bore of the tube to form a solid cross-section optical fiber preform.
Claim 3
Dependent Claim
23 words
A method as claimed in claim 1 wherein the cladding glass contains oxide of phosphorus in an amount not exceeding 0.5 mole %.
Claim 4
Dependent Claim
49 words
A method as claimed in claim 2 wherein a diffusion barrier layer is deposited on the substrate tube and then the cladding layer is deposited, said diffusion barrier layer having a higher mole percentage of oxide of phosphorus than is present in the subsequently deposited layer and cladding glass.
Claim 5
Dependent Claim
22 words
A method as claimed in claim 3 wherein the refractive index of the diffusion barrier layer matches that of the cladding glass.
Claim 6
Independent Claim
27 words
A method as claimed in any one of claims 1, 2, 3, or 4 wherein the refractive index of the cladding glass matches that of pure silica.
Claim 7
Dependent Claim
22 words
A method as claimed in claim 3 or 4 wherein the germania doped silica core glass additionally includes fluorine as a dopant.
Claim 8
Dependent Claim
30 words
A method as claimed in claim 3 wherein the diffusion barrier layer includes a transitional region in which the composition is graded to the material of the cladding glass layer.
Claim 9
Dependent Claim
16 words
A solid cross-section optical fiber preform made by the method claimed in claim 1 or 3.
Claim 10
Dependent Claim
14 words
A single mode optical fiber drawn from a preform as claimed in claim 8.
Claim 11
Independent Claim
209 words
A method of making an optical fiber preform suitable for use in the manufacture of single mode optical fiber, comprising the steps of: depositing on the bore of a silica substrate tube a diffusion barrier layer containing an oxide of phosphorus, depositing, by vapor reaction, on said diffusion barrier layer a layer of fluorine doped silica cladding glass containing at least 0.5 mole % of an oxide of an element for which the fundamental vibrational absorption of the bond between oxygen and that element lies at a longer wavelength that that of the bond between oxygen and silicon, and oxide of phorphorus in an amount not exceeding 0.5 mole %, the mole percent of said oxide of phosphorus in said diffusion barrier layer being higher than that of said cladding glass, said cladding glass having a refractive index not exceeding that of pure silica; depositing, by vapor reaction, on said layer of cladding glass, a layer of silica core glass containing an oxide of an element for which the fundamental vibrational absorption of the bond between oxygen and that element lies at a longer wavelength than that of the bond between oxygen and silicon; and collapsing the bore of the tube to form a solid cross-section optical fiber preform.
Claim 12
Independent Claim
209 words
A method of making an optical fiber preform suitable for use in the manufacture of single mode optical fiber, comprising the steps of: depositing on the bore of a silica substrate tube a diffusion barrier layer containing an oxide of phosphorus, depositing, by vapor reaction, on said diffusion barrier layer a layer of fluorine doped silica cladding glass containing at least 0.5 mole % of an oxide of an element for which the fundamental vibrational absorption of the bond between oxygen and that element lies at a longer wavelength that that of the bond between oxygen and silicon, and oxide of phorphorus in an amount not exceeding 0.5 mole %, the mole percent of said oxide of phosphorus in said diffusion barrier layer being higher than that of said cladding glass, said cladding glass having a refractive index not exceeding that of pure silica; depositing, by vapor reaction, on said layer of cladding glass, a layer of silica core glass containing an oxide of an element for which the fundamental vibrational absorption of the bond between oxygen and that element lies at a longer wavelength than that of the bond between oxygen and silicon; and collapsing the bore of the tube to form a solid cross-section optical fiber preform.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-21 | 1985-12-21 | 1986-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-21 | 1989-12-21 | 1990-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-21 | 1993-12-21 | 1994-06-22 | $7700.00 | Window Closed / Lapsed |