Low temperature fired dielectric ceramic composition and method of making same
Assignee: Tam Ceramics LLC
•
Filing: 1981-05-01
•
Granted: 1982-06-15
•
Expires: 2001-05-01
Abstract
Abstract Low temperature fired dielectric ceramic compositions are prepared by firing, at temperatures between about 1000° C. and about 1150° C., a base ceramic preparation comprising barium titanate, strontium titanate, barium zirconate, titanium dioxide and manganese dioxide mixed with a glass frit comprising zinc oxide, silicon dioxide, boron oxide, lead oxide, bismuth tioxide, and cadmium oxide. The resulting dielectric ceramic composition is useful to form multilayer ceramic capacitors.
Inventors
- 👤 Charles E. Hodgkins
- 👤 Mark J. Giermek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:52
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; C04B35/4684; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1236; H01G4/1245
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
175 words
A dielectric ceramic composition formed from about 92 to about 96.5 percent by weight of a base ceramic preparation which base ceramic preparation consists essentially of from about 72 to about 80 weight percent barium titanate, from about 6 to about 15 weight percent strontium titanate, from about 6 to about 15 weight percent barium zirconate, from about 0.4 to about 0.8 weight percent titanium dioxide, and from about 0.1 to about 0.4 weight percent manganese dioxide, wherein the combined weight percent of strontium titanate and barium zirconate is from about 20 to about 28 percent by weight; and from about 3.5 to about 8 percent by weight of a glass frit which consists essentially of from about 5 to about 10 weight percent zinc oxide, from about 5 to about 10 weight percent silicon dioxide, from about 9 to about 15 percent boron oxide, from about 35 to about 45 weight percent lead oxide, from about 15 to about 25 percent bismuth trioxide, and from about 10 to about 19 weight percent cadmium oxide.
Claim 2
Dependent Claim
175 words
A dielectric ceramic composition formed from about 92 to about 96.5 percent by weight of a base ceramic preparation which base ceramic preparation consists essentially of from about 72 to about 80 weight percent barium titanate, from about 6 to about 15 weight percent strontium titanate, from about 6 to about 15 weight percent barium zirconate, from about 0.4 to about 0.8 weight percent titanium dioxide, and from about 0.1 to about 0.4 weight percent manganese dioxide, wherein the combined weight percent of strontium titanate and barium zirconate is from about 20 to about 28 percent by weight; and from about 3.5 to about 8 percent by weight of a glass frit which consists essentially of from about 5 to about 10 weight percent zinc oxide, from about 5 to about 10 weight percent silicon dioxide, from about 9 to about 15 percent boron oxide, from about 35 to about 45 weight percent lead oxide, from about 15 to about 25 percent bismuth trioxide, and from about 10 to about 19 weight percent cadmium oxide.
Claim 3
Dependent Claim
199 words
A dielectric ceramic composition formed by sintering at a temperature between about 1000° C. and about 1150° C. a mixture of (a) about 92 to about 96.5 weight percent of a base ceramic composition consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 72 to about 80 weight percent barium titanate, from about 6 to about 15 weight percent strontium titanate, from about 6 to about 15 weight percent barium zirconate, from about 0.4 to about 0.8 weight percent titanium dioxide, and from about 0.1 to about 0.4 weight percent manganese dioxide, wherein the combined weight percent of strontium titanate and barium zirconate is from about 20 to about 28 percent by weight; and (b) from about 3.5 to about 8 weight percent of a glass frit consisting essentially of from about 5 to about 10 weight percent zinc oxide, from about 5 to about 10 weight percent silicon dioxide, from about 9 to about 15 weight percent boron oxide, from about 35 to about 45 percent lead oxide, from about 15 to about 25 weight percent bismuth trioxide, and from about 10 to about 19 weight percent cadmium oxide.
Claim 4
Dependent Claim
199 words
A dielectric ceramic composition formed by sintering at a temperature between about 1000° C. and about 1150° C. a mixture of (a) about 92 to about 96.5 weight percent of a base ceramic composition consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 72 to about 80 weight percent barium titanate, from about 6 to about 15 weight percent strontium titanate, from about 6 to about 15 weight percent barium zirconate, from about 0.4 to about 0.8 weight percent titanium dioxide, and from about 0.1 to about 0.4 weight percent manganese dioxide, wherein the combined weight percent of strontium titanate and barium zirconate is from about 20 to about 28 percent by weight; and (b) from about 3.5 to about 8 weight percent of a glass frit consisting essentially of from about 5 to about 10 weight percent zinc oxide, from about 5 to about 10 weight percent silicon dioxide, from about 9 to about 15 weight percent boron oxide, from about 35 to about 45 percent lead oxide, from about 15 to about 25 weight percent bismuth trioxide, and from about 10 to about 19 weight percent cadmium oxide.
Claim 5
Dependent Claim
127 words
A dielectric ceramic composition in accordance with claim 2 wherein the base ceramic preparation consists essentially of from about 74 to about 76 weight percent barium titanate, from about 12 to about 13 weight percent strontium titanate, from about 11.5 to about 12.5 weight percent barium zirconate, from about 0.5 to about 0.7 weight percent titanium dioxide, and from about 0.1 to about to about 0.3 weight percent manganese dioxide; and the glass frit consists essentially of from about 7 to about 8 weight percent zinc oxide, from about 13 to about 14 weight percent boron oxide, from about 39 to about 40 weight percent lead oxide, from about 15.5 to about 16.5 weight percent bismuth, and from about 15.5 to about 16.5 weight percent cadmium oxide.
Claim 6
Dependent Claim
91 words
A dielectric ceramic composition in accordance with claim 2 wherein the base ceramic preparation consists essentially of about 74.5 weight percent barium titanate, about 12.7 weight percent strontium titanate, about 12.0 weight percent barium zirconate, about 0.6 weight percent titanium dioxide, and about 0.2 weight percent manganese dioxide; and the glass frit consists essentially of about 7.4 percent zinc oxide, about 7.9 weight percent silicon dioxide, about 13.6 weight percent boron oxide, about 39.5 weight percent lead oxide, about 15.8 weight percent bismuth trioxide, and about 15.8 weight percent cadmium oxide.
Claim 7
Dependent Claim
56 words
A dielectric ceramic composition in accordance with claim 3 wherein the base ceramic preparation consists essentially of about 93 percent to about 96 percent of the total weight of the dielectric ceramic composition and the glass frit consists essentially of about 4 percent to about 7 percent of the total weight of the dielectric ceramic composition.
Claim 8
Dependent Claim
48 words
A dielectric ceramic composition in accordance with claim 4 wherein the base ceramic preparation consists essentially of about 95.5 percent of the total weight of the dielectric ceramic composition, and the glass frit consists essentially of about 4.5 percent of the total weight of the dielectric ceramic composition.
Claim 9
Dependent Claim
17 words
A dielectric ceramic composition in accordance with claim 2 wherein the dielectric constant is greater than 5000.
Claim 10
Dependent Claim
47 words
A dielectric ceramic composition in accordance with claim 2 wherein the dielectric constant of the dielectric ceramic composition changes from its value at 25° C. by increasing less than 22 percent and decreasing less than 56 percent in the temperature range between -30° C. and 85° C.
Claim 11
Independent Claim
205 words
A method of making a dielectric ceramic composition which comprises: (a) mixing a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 72 to about 80 weight percent barium titanate, from about 6 to about 15 weight percent strontium titanate, from about 6 to about 15 weight percent barium zirconate, from about 0.4 to about 0.8 weight percent titanium dioxide, and from about 0.1 to about 0.4 weight percent manganese dioxide, wherein the combined weight percent of strontium titanate and barium zirconate is from about 20 to about 28 percent by weight; (b) milling said base ceramic preparation with a glass frit consisting essentially of from about 5 to about 10 weight percent zinc oxide, from about 5 to about 10 weight percent silicon dioxide, from about 9 to about 15 weight percent boron oxide, from about 35 to about 45 weight percent lead oxide, from about 15 to about 25 weight percent bismuth trioxide, and from about 15 to about 20 weight percent cadmium oxide; and (c) firing the mixture of said base ceramic preparation and said glass frit at a temperature between about 1000 degrees centigrade and about 1150 degrees centigrade.
Claim 12
Independent Claim
205 words
A method of making a dielectric ceramic composition which comprises: (a) mixing a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 72 to about 80 weight percent barium titanate, from about 6 to about 15 weight percent strontium titanate, from about 6 to about 15 weight percent barium zirconate, from about 0.4 to about 0.8 weight percent titanium dioxide, and from about 0.1 to about 0.4 weight percent manganese dioxide, wherein the combined weight percent of strontium titanate and barium zirconate is from about 20 to about 28 percent by weight; (b) milling said base ceramic preparation with a glass frit consisting essentially of from about 5 to about 10 weight percent zinc oxide, from about 5 to about 10 weight percent silicon dioxide, from about 9 to about 15 weight percent boron oxide, from about 35 to about 45 weight percent lead oxide, from about 15 to about 25 weight percent bismuth trioxide, and from about 15 to about 20 weight percent cadmium oxide; and (c) firing the mixture of said base ceramic preparation and said glass frit at a temperature between about 1000 degrees centigrade and about 1150 degrees centigrade.
Claim 13
Dependent Claim
147 words
A method in accordance with claim 9 wherein the base ceramic preparation consists essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 74 to about 76 weight percent barium titanate, from about 12 to about 13 weight percent strontium titanate, from about 11.5 to about 12.5 weight percent barium zirconate, from about 0.5 to about 0.7 weight percent titanium dioxide and from about 0.1 to about 0.3 weight percent manganese dioxide; and the glass frit consists essentially of from about 7 to about 8 weight percent zinc oxide, from about 7.5 to about 8.5 weight percent silicon dioxide, from about 13 to about 14 weight percent boron oxide, from about 39 to about 40 weight percent lead oxide, from about 15.5 to about 16.5 weight percent bismuth trioxide, and from about 15.5 to about 16.5 weight percent cadmium oxide.
Claim 14
Dependent Claim
103 words
A method in accordance with claim 9 wherein the base ceramic preparation consists essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 74.5 weight percent barium titanate, about 12.7 weight percent strontium titanate, about 12.0 weight percent barium zirconate, about 0.6 weight percent titanium dioxide, and about 0.2 weight percent manganese dioxide; and the glass frit consists essentially of about 7.4 weight percent zinc oxide, about 7.9 weight percent silicon dioxide, about 13.6 weight percent boron oxide, about 39.5 weight percent lead oxide, about 15.8 weight percent bismuth trioxide, and about 15.8 weight percent cadmium oxide.
Claim 15
Dependent Claim
41 words
A method in accordance with claim 9 wherein the dielectric ceramic composition consists essentially of from about 92 to about 96.5 weight percent of the base ceramic preparation and from about 3.5 to about 8 weight percent of the glass frit.
Claim 16
Dependent Claim
41 words
A method in accordance with claim 10 wherein the dielectric ceramic composition consists essentially of from about 93 to about 96 weight percent of the base ceramic preparation and from about 4 to about 7 weight percent of the glass frit.
Claim 17
Dependent Claim
33 words
A method in accordance with claim 11 wherein the dielectric ceramic composition consists essentially of about 95.5 weight percent of the base ceramic preparation and about 4.5 weight percent of the glass frit.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-14 | 1985-12-14 | 1986-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-14 | 1989-12-14 | 1990-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-14 | 1993-12-14 | 1994-06-15 | $7700.00 | Window Closed / Lapsed |