Process for preparation of compositions of bitumen polymers and products
Assignee: Koch Enterprises Inc
•
Filing: 1981-06-29
•
Granted: 1982-05-18
•
Expires: 2001-06-29
Abstract
Abstract A method of preparation of polymer-asphalt (bitumen) compositions which comprises mixing, with agitation, at a temperature of 130 DEG to 230 DEG C., 80 to 98% by weight of an asphalt having a penetration between 30 to 220, and 2 to 20% by weight of a polyblock copolymer of a styrene-carboxylated conjugated diene having a mean molecular weight of 30,000 to 300,000, and maintaining this mixture for at least 2 hours at this temperature, then adding 0.1 to 3% of elemental sulfur, based on the asphalt, while maintaining the same conditions of agitation and temperature for at least 20 minutes, the carboxylated conjugated diene sequence being selected from the group consisting of carboxylated polybutadiene and carboxylated polyisoprene.
Inventors
- 👤 Paul Maldonado
- 👤 Daniele Eber
- 👤 Trung Kiet Phung
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:48
CPC Classifications
C; C08; C08L; C08L95/00
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
130 words
A method of preparing a polymer-asphalt composition which comprises forming a mixture at a temperature of 130 to 230° C., comprising 80 to 98% by weight of an asphalt having a penetration between 30 and 220, and 2 to 20% by weight of a polyblock styrene-carboxylated conjugated diene copolymer having a molecular weight between 30,000 and 300,000, maintaining the mixture for at least two hours at a temperature of 130 to 230° C., then adding to said mixture 0.1 to 3by weight of elemental sulfur, based on the asphalt in said mixture, while agitating the mixture and maintaining the temperature of 130 to 230° C. for at least 20 minutes to form said composition, the conjugated diene block being selected from the group consisting of carboxylated butadiene and carboxylated isoprene.
Claim 2
Independent Claim
130 words
A method of preparing a polymer-asphalt composition which comprises forming a mixture at a temperature of 130 to 230° C., comprising 80 to 98% by weight of an asphalt having a penetration between 30 and 220, and 2 to 20% by weight of a polyblock styrene-carboxylated conjugated diene copolymer having a molecular weight between 30,000 and 300,000, maintaining the mixture for at least two hours at a temperature of 130 to 230° C., then adding to said mixture 0.1 to 3by weight of elemental sulfur, based on the asphalt in said mixture, while agitating the mixture and maintaining the temperature of 130 to 230° C. for at least 20 minutes to form said composition, the conjugated diene block being selected from the group consisting of carboxylated butadiene and carboxylated isoprene.
Claim 3
Dependent Claim
54 words
A method according to claim 1, wherein the copolymers added to the asphalt are polystyrene-carboxylated polybutadiene copolymers having a proportion of polystyrene from about 15 to 25% by weight, a molecular weight ranging from 70,000 to 90,000 and a proportion of carboxyl groups ranging from 0.05 to 0.1% by weight based on the polymer.
Claim 4
Dependent Claim
63 words
A method according to claim 1, wherein 100 parts of 80-100 asphalt is mixed with 10 parts of a carboxylated isoprene-styrene copolymer having a mean molecular weight of 80,000 and an isoprene/styrene ratio by weight of 3.0 at about 170° C. for about 3 hours, about 0.2 parts of elemental sulfur is than added, and agitation is continued for about one half hour.
Claim 5
Dependent Claim
12 words
The produce obtained according to the method of claim 1 or 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-17 | 1985-11-16 | 1986-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-17 | 1989-11-16 | 1990-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-17 | 1993-11-16 | 1994-05-18 | $7700.00 | Window Closed / Lapsed |