Thermoplastic elastomeric blend of rubber and bituminous material
Assignee: UNIROYAL Inc A NJ CORP
•
Filing: 1976-02-05
•
Granted: 1978-12-12
•
Expires: 1996-02-05
Abstract
Abstract A novel thermoplastic, elastomeric material is obtained by curing under shear conditions (e.g. in a high shear internal mixer) a blend of vulcanizable rubber (e.g. SBR, EPDM) and a bituminous material (e.g., asphalt) in the presence of a rubber vulcanizing agent (e.g. sulfur or peroxide). The product has a unique combination of elastomeric and thermoplastic properties. It can be processed by conventional thermoplastic methods at elevated temperatures (e.g. extrusion, calendering, vacuum forming) and at normal temperatures possesses good elastomeric properties without the need for subsequent vulcanization. If desired, the material can be re-processed.
Inventors
- 👤 Alister F. Matheson
- 👤 Douglas J. Tosh
- 👤 Mitchell Borr
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:06
CPC Classifications
C; C08; C08L; C08L21/00; C08L23/00; C08L23/02; C08L23/16; C08L95/00; C08L9/00; C08L9/06
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
162 words
A method of converting into a thermoplastic elastomer an unsaturated vulcanizable rubber comprising providing an intimately mixed blend of (A) 100 parts by weight of said unsaturated vulcanizable rubber with (B) from 125 to 250 parts by weight of bituminous material by masticating the said unsaturated vulcanizable rubber and bituminous material together at elevated temperature, and further masticating said intimately mixed blend under dynamic shearing conditions in an internal mixer in the presence of (C) a curative for said unsaturated vulcanizable rubber in amount sufficient to cure the rubber, the said dynamic shearing of the intimately mixed blend in the presence of the curative being continued for a time and at a temperature sufficient to dynamically cure the rubber, whereby the bend is converted into a thermoplastic elastomer which is characterized by the ability to be thermoformed thereafter without cure into useful shaped articles having elastomeric properties, and by the ability to be re-processed, the said rubber (A) being ethylene-propylene-non-conjugated diene terpolymer.
Claim 2
Independent Claim
162 words
A method of converting into a thermoplastic elastomer an unsaturated vulcanizable rubber comprising providing an intimately mixed blend of (A) 100 parts by weight of said unsaturated vulcanizable rubber with (B) from 125 to 250 parts by weight of bituminous material by masticating the said unsaturated vulcanizable rubber and bituminous material together at elevated temperature, and further masticating said intimately mixed blend under dynamic shearing conditions in an internal mixer in the presence of (C) a curative for said unsaturated vulcanizable rubber in amount sufficient to cure the rubber, the said dynamic shearing of the intimately mixed blend in the presence of the curative being continued for a time and at a temperature sufficient to dynamically cure the rubber, whereby the bend is converted into a thermoplastic elastomer which is characterized by the ability to be thermoformed thereafter without cure into useful shaped articles having elastomeric properties, and by the ability to be re-processed, the said rubber (A) being ethylene-propylene-non-conjugated diene terpolymer.
References Cited (Backward Citations)
GB875947A
Cited
US3265765A
Cited
US3751389A
Cited
US3963659A
Cited
US3853799A
Cited
US3803066A
Cited
US3758643A
Cited
US3833528A
Cited
US3806558A
Cited
US3873483A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-11 | 1982-06-12 | 1982-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-11 | 1986-06-12 | 1986-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-11 | 1990-06-12 | 1990-12-12 | $7700.00 | Window Closed / Lapsed |