Production of bitumen compositions containing ethylene-α-olefin rubber
Assignee: Huels AG
•
Filing: 1975-04-25
•
Granted: 1976-06-15
•
Expires: 1995-04-25
Abstract
Abstract Homogeneous thermoplastic bituminous compositions containing up to 25 parts by weight of ethylene-α-olefin rubber, e.g. ethylene-propylene rubber, saturated or unsaturated, exhibit improved properties for all asphalt applications, e.g. pipe coating, roads, roofing, etc. The compositions are produced by heating and agitating the bitumen and rubber at above 170° C., preferably 180°-240° C., or by subjecting the rubber to premastication before admixture with the bitumen at lower temperatures. Cross-linkable rubbers can be cross-linked in the bituminous compositions to yield high tensile strength final products.
Inventors
- 👤 Gerhard Binder
- 👤 Harald Blumel
- 👤 Helmut Krol
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:53
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/005; C08L; C08L95/00; C08J2395/00
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
185 words
A process for the production of a homogeneous thermoplastic composition consisting essentially of on a 100 parts by weight basis about 75-99.5 parts bitumen and about 0.5-25 parts of an ethylene-α-olefin rubber having a Mooney viscosity (ML-4) of 35-90 and comprising on a mol basis 45-75% ethylene and 25-55% of propylene and having cross linkable double bonds said process comprising the steps of: premasticating the ethylene-α-olefin rubber and during said premasticating adding a small amount of bitumen to obtain preliminary homogenization; adding a small amount of bitumen to the premasticated rubber and masticating the resultant mixture to disperse the bitumen as a dispersed phase into the rubber as a continuous phase and continuing the mastication to form a homogeneous mixture; and adding additional bitumen either in incremental batches, or gradually in a continuous manner and at a rate such that each charge of bitumen is first homogeneously mixed before adding additional bitumen, and changing the type of added bitumen from a less viscous type to a more viscous type during the step of adding same, and continuing the mastication to produce the homogeneous thermoplastic composition.
Claim 2
Dependent Claim
185 words
A process for the production of a homogeneous thermoplastic composition consisting essentially of on a 100 parts by weight basis about 75-99.5 parts bitumen and about 0.5-25 parts of an ethylene-α-olefin rubber having a Mooney viscosity (ML-4) of 35-90 and comprising on a mol basis 45-75% ethylene and 25-55% of propylene and having cross linkable double bonds said process comprising the steps of: premasticating the ethylene-α-olefin rubber and during said premasticating adding a small amount of bitumen to obtain preliminary homogenization; adding a small amount of bitumen to the premasticated rubber and masticating the resultant mixture to disperse the bitumen as a dispersed phase into the rubber as a continuous phase and continuing the mastication to form a homogeneous mixture; and adding additional bitumen either in incremental batches, or gradually in a continuous manner and at a rate such that each charge of bitumen is first homogeneously mixed before adding additional bitumen, and changing the type of added bitumen from a less viscous type to a more viscous type during the step of adding same, and continuing the mastication to produce the homogeneous thermoplastic composition.
Claim 3
Dependent Claim
20 words
A process according to claim 2, further comprising employing mineral or inorganic fillers, carbon black, or sulfur in said compositions.
Claim 4
Dependent Claim
39 words
A process according to claim 1, wherein per 100 parts by weight of bitumen-rubber there are employed up to 100 parts by weight of filler, 100 parts by weight of carbon black and/or 20 parts by weight of sulfur.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-15 | 1979-12-15 | 1980-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-15 | 1983-12-15 | 1984-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-15 | 1987-12-15 | 1988-06-15 | $7700.00 | Window Closed / Lapsed |