US4324705A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for recovering materials from scrapped film
Assignee: Fujifilm Holdings Corp
•
Filing: 1980-06-12
•
Granted: 1982-04-13
•
Expires: 2000-06-12
Abstract
Abstract A process for recovering materials from scrapped film is described which comprises separating coating layers and a film base from a scrapped film having at least one coating layer on a plastic film base in a sheet or web form, wherein the improvement comprises: impregnating the coating layers of said scrapped film with a strong alkaline solution and stripping the coating layers by means of high pressure jet water to separate said coating layers from the film base before the coating layers are dissolved in or separated from the film base by said alkaline solution.
Inventors
- 👤 Kunihira Seto
- 👤 Kyoichi Naruo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 15:05
CPC Classifications
B; B29; B29B; B29B17/00; B29B17/02; G; G03; G03C; G03C11/00; G03C11/24; B29B2017/0213; B29B2017/0293; B29B2017/0296; B29B17/04; B29B2017/0424; B29B2017/0428; B29L; B29L2007/00; B29L2007/008; B29L2009/00; B29L2009/005; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
120 words
A process for recovering materials from scrapped photographic film which comprises separating coating layers and a film base from a scrapped photographic film having at least one coating layer on a plastic film base, wherein the improvement comprises: impregnating the coating layers of said scrapped film with a strong alkaline solution having a pH of at least 9.0 at 25° C. and stripping the coating layers by means of high pressure jet water having a temperature of from about 5° to 95° C. and a pressure of from about 3 to 50 kg/cm 2 to separate said coating layers from the film base before the coating layers are dissolved in or separated from the film base by said alkaline solution.
Claim 2
Dependent Claim
120 words
A process for recovering materials from scrapped photographic film which comprises separating coating layers and a film base from a scrapped photographic film having at least one coating layer on a plastic film base, wherein the improvement comprises: impregnating the coating layers of said scrapped film with a strong alkaline solution having a pH of at least 9.0 at 25° C. and stripping the coating layers by means of high pressure jet water having a temperature of from about 5° to 95° C. and a pressure of from about 3 to 50 kg/cm 2 to separate said coating layers from the film base before the coating layers are dissolved in or separated from the film base by said alkaline solution.
Claim 3
Dependent Claim
24 words
A process for recovering materials from a scrapped film as in claim 1, wherein said coating layers include at least one photographic emulsion layer.
Claim 4
Dependent Claim
30 words
A process for recovering materials from a scrapped film as in claim 1, wherein said alkaline solution is formed from an alkali metal hydroxide or an alkaline earth metal hydroxide.
Claim 5
Dependent Claim
43 words
A process for recovering materials from a scrapped film as in claim 3, wherein said alkaline solution is an aqueous solution of from 5 to 10 wt% caustic soda or caustic potash heated to a temperature of from about 80° to 90° C.
Claim 6
Dependent Claim
41 words
A process for recovering materials from a scrapped film as in claim 1, wherein the high pressure jet water has a temperature of from about 15° to 50° C. and a pressure of from about 3 to 50 kg/cm 2 .
Claim 7
Dependent Claim
77 words
A process for recovering materials from a scrapped film as in claim 1 including a photographic emulsion layer and an adhesive subbing layer for adhering said photographic emulsion layer to said film base, wherein said photographic emulsion layer is removed by application of a jet water at from 3 to 10 kg/cm 2 , and said adhesive subbing layer is subsequently removed by application of a jet of water at from 10 to 50 kg/cm 2 .
Claim 8
Dependent Claim
82 words
A process for recovering materials from a scrapped film as in claim 5 comprising a photographic film including a photographic emulsion layer and an adhesive subbing layer for adhering said photographic emulsion layer to said film base, wherein said photographic emulsion layer is removed by application of a jet of water of from 3 to 10 kg/cm 2 , and said adhesive subbing layer is subsequently removed by application of a jet of water at from 20 to 40 kg/cm 2 .
Claim 9
Dependent Claim
56 words
A process for recovering materials from a scrapped film as in claim 1, or 2, wherein the coating layers are impregnated with said alkaline solution by dipping the film for about 1 to 60 seconds in a 5 to 10 wt% aqueous solution of caustic soda heated to from about 70° C. to about 95° C.
Claim 10
Dependent Claim
55 words
A process for recovering materials from a scrapped films as in claims 1 or 2, wherein the alkaline solution is an aqueous solution of an alkali metal hydroxide, an aqueous solution of an alkaline earth metal hydroxide, a glycol solution of an alkali metal hydroxide or a glycol solution of an alkaline earth metal hydroxide.
Claim 11
Dependent Claim
49 words
A process for recovering materials from a scrapped films as in claim 9, wherein said alkaline solution is an aqueous or glycol solution of from 5 to 10 wt% alkali metal hydroxide or alkaline earth metal hydroxide heated to a temperature of from about 70° C. to 95° C.
Claim 12
Dependent Claim
47 words
A process for recovering materials from a scrapped films as in claim 10, wherein said alkaline solution is an aqueous solution of from 5 to 10 wt% alkali metal hydroxide or alkaline earth metal hydroxide heated to a temperature of from about 70° C. to 95° C.
Claim 13
Dependent Claim
62 words
A process for recovering materials from a scrapped films as in claim 1 or 2, wherein the coating layers are impregnated with said alkaline solution by dipping the film for about 1 to 60 seconds in a 5 to 10 wt% aqueous solution of alkali metal hydroxide or alkaline earth metal hydroxide heated to from about 70° C. to about 95° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-12 | 1985-10-12 | 1986-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-12 | 1989-10-12 | 1990-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-12 | 1993-10-12 | 1994-04-13 | $7700.00 | Window Closed / Lapsed |