Recovery of silver and other valuable constituents from polyester based photographic film
Assignee: Horizons Research Inc
•
Filing: 1977-04-05
•
Granted: 1978-03-14
•
Expires: 1997-04-05
Abstract
Abstract Scrap photographic film comprising at least a four component system involving a polyalkyleneterephthalate film base, an adhesive or subbing layer utilizing a terpolymer consisting chiefly of polyvinylidenechloride and a gelatin layer containing metallic silver or a compound thereof and a variety of contaminants such as causal dirt, dyes and the like is broken down for recovery of the valuable constituents therein including the silver, the polyvinylidenechloride terpolymer, and the polyesters by treating the chopped photographic film at an elevated temperature with a solvent for both the polyester and polyvinylidenechloride values in which solvent both the gelatin and silver values are insoluble, under conditions chosen to insure the quantitative recovery of the silver values.
Inventors
- 👤 Arthur H. Gerber
- 👤 Eugene Wainer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:52
CPC Classifications
C; C08; C08J; C08J11/00; C08J11/04; C08J11/06; C08J11/08; C08J3/00; C08J3/12; C08J3/14; G; G03; G03C; G03C11/00; G03C11/24; C08J2367/00; C08J2367/02; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/582; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
208 words
A process for recovery of the silver content of photographic film scrap containing more than one non-water soluble polymeric material at least a portion of which is polyester, said film scrap comprising a non-water soluble polymeric base selected from the group consisting of polyesters and cellulose acetate; a non-water soluble polymeric subbing layer including a chlorine containing polymer and a gelatine layer containing metallic silver or silver halide; 1. contacting the photographic film scrap with a first solvent for the non-water soluble polymeric material at a temperature above that at which said non-water soluble polymeric material dissolves; 2. filtering the resulting hot solution for removal of silver and contaminants in the photographic film scrap which are insoluble in said first solvent; 3. calcining the insoluble materials separated in Step 2 in order to recover the silver values therein; 4. cooling the hot filtrate derived from Step 2, thereby precipitating the polyester contained therein and recovering the polyester in powdered form by filtration of the cooled filtrate; 5. treating the cooled filtrate from Step 4 with a second solvent in which the polyester is insoluble, said first solvent is soluble and the other non-water soluble polymeric materials are also soluble, and removing any residual polyester which precipitates by filtration;
Claim 2
Dependent Claim
208 words
A process for recovery of the silver content of photographic film scrap containing more than one non-water soluble polymeric material at least a portion of which is polyester, said film scrap comprising a non-water soluble polymeric base selected from the group consisting of polyesters and cellulose acetate; a non-water soluble polymeric subbing layer including a chlorine containing polymer and a gelatine layer containing metallic silver or silver halide; 1. contacting the photographic film scrap with a first solvent for the non-water soluble polymeric material at a temperature above that at which said non-water soluble polymeric material dissolves; 2. filtering the resulting hot solution for removal of silver and contaminants in the photographic film scrap which are insoluble in said first solvent; 3. calcining the insoluble materials separated in Step 2 in order to recover the silver values therein; 4. cooling the hot filtrate derived from Step 2, thereby precipitating the polyester contained therein and recovering the polyester in powdered form by filtration of the cooled filtrate; 5. treating the cooled filtrate from Step 4 with a second solvent in which the polyester is insoluble, said first solvent is soluble and the other non-water soluble polymeric materials are also soluble, and removing any residual polyester which precipitates by filtration;
Claim 3
Dependent Claim
74 words
partitioning the filtrate by addition of a third solvent in which the chlorine containing polymers originally present in said scrap are insoluble and in which the non-chlorine containing polymers originally present in said scrap are soluble and removing precipitated polymers by filtration; 7. recovering said non-chlorine containing polymers by adding a fourth solvent in which said non-chlorine containing polymers are insoluble; and 8. filtering the product of Step 7 and recovering the precipitated polymers.
Claim 4
Dependent Claim
74 words
partitioning the filtrate by addition of a third solvent in which the chlorine containing polymers originally present in said scrap are insoluble and in which the non-chlorine containing polymers originally present in said scrap are soluble and removing precipitated polymers by filtration; 7. recovering said non-chlorine containing polymers by adding a fourth solvent in which said non-chlorine containing polymers are insoluble; and 8. filtering the product of Step 7 and recovering the precipitated polymers.
Claim 5
Dependent Claim
44 words
The process of claim 1 in which the non-water soluble polymers present in said scrap comprise a polyethylene terephthalate base and a terpolymer subbing layer comprising a major amount of vinylidenechloride, a minor amount of methylmethacrylate, and a still lesser amount of itaconic acid.
Claim 6
Dependent Claim
49 words
The process of claim 1 in which the first solvent is selected from the group consisting of: aryl ethers, phenones, esters of dicarboxylic acids, pyrollidones, lactones, pyrolles, amides and mixtures thereof in which the solvents of said group do not contain halogens, amine side groups, or doubly bonded sulphur.
Claim 7
Dependent Claim
24 words
The process of claim 1 wherein said first solvent contacts the scrap for not more than 15 minutes in Step 1 of said process.
Claim 8
Dependent Claim
24 words
The process of claim 1 wherein said first solvent contacts the scrap for not more than 5 minutes in Step 1 of said process.
Claim 9
Dependent Claim
44 words
The process of claim 1 wherein the solution of the non-water soluble polymers is complete, the resulting mixture is digested at said temperature for at least an additional 10 minutes to complete precipitation and consolidation of the silver containing portions of the film scrap.
Claim 10
Dependent Claim
30 words
The process of claim 1 including heating the photographic film scrap to 150° C for at least 10 minutes and then adding the heated film scrap to said first solvent.
Claim 11
Dependent Claim
36 words
The process of claim 1 wherein the temperature at which the film scrap is contacted with said first solvent is below the boiling point of said solvent but at a temperature not less than 165° C.
Claim 12
Dependent Claim
83 words
The process of claim 1 wherein the polyester product is obtained in a particle size range of 10 to 100 microns by cooling the first filtrate in Step 4 of claim 1 to a precipitating temperature above room temperature, but not below a temperature range of 65° C to 150° C, maintaining the mixture at said precipitating temperature for a period of 20 to 40 minutes, cooling to a temperature of 20° to 25° C and separating out the precipitated polyester by filtration.
Claim 13
Dependent Claim
55 words
The process of claim 1 where the polyester product is obtained in a particle size range of less than 10 microns by rapid cooling of the first hot filtrate in Step 4 of said process, to a precipitating temperature in the range of 0° C to -10° C, separating out the precipitated polyester by filtration.
Claim 14
Dependent Claim
30 words
The process of claim 1 wherein the relative viscosity of the recovered polyester powder precipitate is not less than the relative viscosity of the polyester in the starting raw material.
Claim 15
Dependent Claim
14 words
The process of claim 1 where the second solvent is a higher alkyl ketone.
Claim 16
Dependent Claim
24 words
The process of claim 1 where the third solvent is selected from the group consisting of lower aliphatic alcohols and liquid straight chain hydrocarbons.
Claim 17
Dependent Claim
11 words
The process of claim 1 wherein the fourth solvent is water.
Claim 18
Dependent Claim
41 words
The process of claim 1 wherein the materials in the scrap photographic film insoluble in the first solvent include at least one member of the group consisting of silver, silver compounds, gelatin, cellulose fibers, antimony compounds, siliceous compounds and casual dirt.
Claim 19
Dependent Claim
36 words
The process of claim 1 wherein the silver content and the first solvent-soluble but water-insoluble polymers are recovered separately in yields in excess of 99% of the content of these materials in the original raw material.
Claim 20
Dependent Claim
20 words
The process of claim 1 where the solvents used are recovered by fractional distillation for recycle use in said process.
References Cited (Backward Citations)
US3836486A
Cited
US3701741A
Cited
US3696058A
Cited
US3935169A
Cited
US3873314A
Cited
US3929466A
Cited
US3912664A
Cited
US4009048A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-13 | 1981-09-12 | 1982-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-13 | 1985-09-12 | 1986-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-13 | 1989-09-12 | 1990-03-14 | $7700.00 | Window Closed / Lapsed |