Method for removing a scale from a superalloy surface
Assignee: General Electric Co
•
Filing: 1980-06-06
•
Granted: 1982-03-02
•
Expires: 2000-06-06
Abstract
Abstract A method for removing scale, particularly oxide scale, from a surface of a high temperature alloy, the surface having been exposed to high temperature conditions, employs an aqueous alkaline hydroxide solution in contact with the scale in an autoclave. The solution is heated in the autoclave in a non-oxidizing atmosphere at a temperature in the range of about 200°-340° C. while providing relative movement between the solution and the scale. Thereafter, the scale reaction product is flushed from the surface to remove the alkaline solution.
Inventors
- 👤 Pritam L. Ahuja
- 👤 Marcus P. Borom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:39
CPC Classifications
C; C23; C23G; C23G1/00; C23G1/14; C23G1/20; C23G1/19
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
183 words
A method of removing scale from a surface of an internal passage within an article of a high temperature superalloy based on at least one element from the group consisting of Co and Ni, the scale being selected from the group consisting of oxides, silicates, sulfides and their combinations and being the corrosion products resulting from the surface having been exposed to strenuous environmental conditions at high temperature, comprising the steps of: providing an aqueous alkaline hydroxide solution comprising about 20-75 weight percent of a hydroxide selected from the group consisting of NaOH, KOH and their mixtures; immersing the surface in the hydroxide solution within a sealed autoclave in the presence of a non-oxidizing atmosphere; heating the hydroxide solution in the autoclave at a temperature in the range from about 200 to a maximum of 340 C. for a time sufficient to react the solution with the scale to form a scale reaction product while providing relative movement between the solution and the scale within the internal passage; and then flushing the scale reaction product and the alkaline solution from the internal passage.
Claim 2
Independent Claim
183 words
A method of removing scale from a surface of an internal passage within an article of a high temperature superalloy based on at least one element from the group consisting of Co and Ni, the scale being selected from the group consisting of oxides, silicates, sulfides and their combinations and being the corrosion products resulting from the surface having been exposed to strenuous environmental conditions at high temperature, comprising the steps of: providing an aqueous alkaline hydroxide solution comprising about 20-75 weight percent of a hydroxide selected from the group consisting of NaOH, KOH and their mixtures; immersing the surface in the hydroxide solution within a sealed autoclave in the presence of a non-oxidizing atmosphere; heating the hydroxide solution in the autoclave at a temperature in the range from about 200 to a maximum of 340 C. for a time sufficient to react the solution with the scale to form a scale reaction product while providing relative movement between the solution and the scale within the internal passage; and then flushing the scale reaction product and the alkaline solution from the internal passage.
Claim 3
Dependent Claim
32 words
The method of claim 1 in which: the hydroxide comprises about 30-40 weight percent of the aqueous solution; and the temperature in the autoclave is in the range of about 230°-330° C.
References Cited (Backward Citations)
US2796366A
Cited
US3121026A
Cited
US3126301A
Cited
US4073662A
Cited
US4134777A
Cited
US4188237A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-01 | 1985-08-31 | 1986-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-01 | 1989-08-31 | 1990-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-01 | 1993-08-31 | 1994-03-02 | $7700.00 | Window Closed / Lapsed |