Abstract An improvement to an adsorbent comprising a crystalline aluminosilicate used in a process for separating a component from a feed mixture comprising an aqueous solution of a mixture of different components, such as a mixture of saccharides. There is an undesirable tendency for the silicon constituent of the crystalline aluminosilicate to dissolve in the aqueous system. The adsorbent has incorporated in it a binder material comprising a water permeable organic polymer which substantially reduces the undesirable dissolution. The adsorbent is manufactured by mixing together powder of the crystalline aluminosilicate, powders of the organic polymer binder, and a liquid organic solvent, forming the mixture into discrete formations, preferably by extruding the mixture into an extrudate, and drying the formations. The improvement comprises spheronizing those formations prior to drying them.
A method for the preparation of a crystalline aluminosilicate adsorbent which comprises the steps of: (a) mixing together a powdered crystalline aluminosilicate, a powdered binder comprising a water permeable organic polymer and a liquid organic solvent to form a malleable mixture; (b) forming said malleable mixture into discrete formations; (c) then spheronizing said formations; and (d) thereafter removing said solvent from the resultant spheres to produce hard, dry spherical particles.
Claim 2
Independent Claim
70 words
A method for the preparation of a crystalline aluminosilicate adsorbent which comprises the steps of: (a) mixing together a powdered crystalline aluminosilicate, a powdered binder comprising a water permeable organic polymer and a liquid organic solvent to form a malleable mixture; (b) forming said malleable mixture into discrete formations; (c) then spheronizing said formations; and (d) thereafter removing said solvent from the resultant spheres to produce hard, dry spherical particles.
Claim 3
Dependent Claim
22 words
The method of claim 1 further characterized in that the forming of said malleable mixture in step (b) is effected by extrusion.
Claim 4
Dependent Claim
23 words
The method of claim 1 further characterized in that said hard dry formations of step (d) are broken into particles of desired sizes.
Claim 5
Dependent Claim
21 words
The method of claim 1 further characterized in that said water permeable organic polymer comprises a cellulose ester or cellulose nitrate.
Claim 6
Dependent Claim
24 words
The method of claim 1 further characterized in that said crystalline aluminosilicate is selected from the group consisting of X zeolites and Y zeolites.
Claim 7
Dependent Claim
29 words
The method of claim 5 further characterized in that said aluminosilicate contains cations at exchangeable cationic sites selected from the group consisting of alkali metals and alkali earth metals.
Claim 8
Dependent Claim
10 words
Speroidal adsorbent particles prepared by the method of claim 1.