Technique to reduce the zeolite molecular sieve solubility in an aqueous system
Assignee: Honeywell UOP LLC
•
Filing: 1979-06-15
•
Granted: 1981-02-03
•
Expires: 1999-06-15
Abstract
Abstract An improved adsorbent comprising a crystalline aluminosilicate, method of manufacture of the adsorbent and improved process for separating a component from a feed mixture comprising an aqueous solution of a mixture of different components, such as a mixture of saccharides. In the process the mixture is contacted with the adsorbent, which selectively adsorbs a component from the feed mixture. The adsorbed component is then recovered by contacting the adsorbent with a desorbent material such as water to effect the desorption of the adsorbed component from the adsorbent. There is an undesirable tendency for the silicon constituent of the crystalline aluminosilicate to dissolve in the aqueous system. The improvement to the adsorbent and process comprises the incorporation of a binder material in the adsorbent comprising a water permeable organic polymer which substantially reduces the undesirable dissolution. The adsorbent is manufactured by mixing together powder of the crystalline aluminosilicate, powders of the organic polymer binder, and a liquid organic solvent, extruding the mixture into an extrudate and drying the extrudate.
Inventors
- 👤 Santi Kulprathipanja
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 00:19
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/16; B01J20/18; B01J20/183
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
102 words
A method for the manufacture of an adsorbent comprising crystalline aluminosilicate and a water permeable organic polymer binder suitable for use in a process for the separation of a component from a feed mixture comprising an aqueous solution of a mixture of components, which method comprises: (a) mixing together a powder of said crystalline aluminosilicate, a powder of said binder and a liquid organic solvent to form a malleable mixture; (b) forming said malleable mixture into discrete formations; (c) removing said solvent from said formations to obtain hard dry formations; and (d) breaking said hard dry formations into particles of desired sizes.
Claim 2
Independent Claim
102 words
A method for the manufacture of an adsorbent comprising crystalline aluminosilicate and a water permeable organic polymer binder suitable for use in a process for the separation of a component from a feed mixture comprising an aqueous solution of a mixture of components, which method comprises: (a) mixing together a powder of said crystalline aluminosilicate, a powder of said binder and a liquid organic solvent to form a malleable mixture; (b) forming said malleable mixture into discrete formations; (c) removing said solvent from said formations to obtain hard dry formations; and (d) breaking said hard dry formations into particles of desired sizes.
Claim 3
Dependent Claim
46 words
The method of claim 1 further characterized in that in step (a) powders of said crystalline aluminosilicate and said binder are first mixed together to obtain a powder mixture, and said liquid organic solvent is then added to said powder mixture to obtain said malleable mixture.
Claim 4
Dependent Claim
46 words
The method of claim 1 further characterized in that in step (a) said powder of said binder is first dissolved in said organic solvent to obtain a solution, and said powder of said crystalline aluminosilicate is then added to said solution to obtain said malleable mixture.
Claim 5
Dependent Claim
39 words
The method of claim 1 further characterized in that in step (c) said solvent is removed from said formations by first washing said formations with water and then drying said formations at a temperature not exceeding about 100° C.
Claim 6
Dependent Claim
31 words
The method of claim 1 further characterized in that in step (c) said solvent is removed from said formations by drying said formations at a temperature not exceeding about 100° C.
Claim 7
Dependent Claim
38 words
The method of claim 1 further characterized in that in step (d) said desired sizes of said particles is such that said particles will pass through a No. 16 screen and be retained on a No. 80 screen.
Claim 8
Dependent Claim
21 words
The method of claim 1 further characterized in that said water permeable organic polymer comprises a cellulose ester or cellulose nitrate.
Claim 9
Dependent Claim
24 words
The method of claim 1 further characterized in that said crystalline aluminosilicate is selected from the group consisting of X zeolites and Y zeolites.
Claim 10
Dependent Claim
37 words
The method of claim 8 further characterized in that cations at exchangeable cationic sites on said crystalline aluminosilicate in said particles are exchanged with cations selected from the group consisting of alkali metals and alkaline earth metals.
Claim 11
Dependent Claim
29 words
The method of claim 1 further characterized in that the content of said organic polymer in said particles is from about 3.0 wt. % to about 50.0 wt. %.
Claim 12
Dependent Claim
26 words
The method of claim 1 further characterized in that said liquid organic solvent comprises p-dioxane, methyl-ethyl ketone, ethyl acetone, acetone, chloroform, benzyl alcohol, cyclohexanone, or formamide.
Claim 13
Dependent Claim
18 words
The method of claim 1 further characterized in that in step (b) said forming is effected by extrusion.
Claim 14
Dependent Claim
9 words
An adsorbent prepared by the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-03 | 1984-08-04 | 1985-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-03 | 1988-08-04 | 1989-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-03 | 1992-08-04 | 1993-02-03 | $7700.00 | Window Closed / Lapsed |