Thin-film silicon solar cell with metal boride bottom electrode
Assignee: Johns Hopkins University
•
Filing: 1980-08-04
•
Granted: 1982-02-02
•
Expires: 2000-08-04
Abstract
Abstract The invention relates to an improved thin film semiconductor p-n junction device and its method of fabrication, utilizing vacuum deposition techniques, whereby continuous/batch processing may be utilized, capable of mass producing p-n junction devices; e.g. solar cells, with large surface areas and good operating efficiency and at low cost. A novel feature of the proposed device and its method of fabrication is the formation of the bottom electrode of the device, located between the nonconducting substrate and the overlying silicon semiconductor layer, as a metal boride region which possesses several characteristics particularly necessary to the fabrication of thin film silicon solar cells for example, having improved structural and operating properties, as well as good operating efficiency.
Inventors
- 👤 Charles Feldman
- 👤 Harry K. Charles
- 👤 Frank G. Satkiewicz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:35
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/20; H10F77/206; H10F77/211; H10F71/00; H10F71/121; H10F71/137; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/547; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S148/00; Y10S148/006; Y10S148/12
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
127 words
A method for producing a thin film p-n junction device comprising the steps of: vacuum depositing a first layer of transition metal on an electrically nonconducting substrate material, vacuum depositing a second layer of boron (B) overlying said first layer, heating the materials at a temperature and for a time sufficient to cause the transition metal and the (B) to form a transition metal boride layer, vacuum depositing p-type silicon (Si) on said transition metal boride layer at a substrate temperature between 900°-1300° centigrade and at a rate between 500-5000 Angstroms per minute to a thickness of between 10-30 μm, doping the (Si) with an n-type material to form a p-n junction, and attaching separate electrode means to said n-type material and said metal boride layer respectively.
Claim 2
Independent Claim
127 words
A method for producing a thin film p-n junction device comprising the steps of: vacuum depositing a first layer of transition metal on an electrically nonconducting substrate material, vacuum depositing a second layer of boron (B) overlying said first layer, heating the materials at a temperature and for a time sufficient to cause the transition metal and the (B) to form a transition metal boride layer, vacuum depositing p-type silicon (Si) on said transition metal boride layer at a substrate temperature between 900°-1300° centigrade and at a rate between 500-5000 Angstroms per minute to a thickness of between 10-30 μm, doping the (Si) with an n-type material to form a p-n junction, and attaching separate electrode means to said n-type material and said metal boride layer respectively.
Claim 3
Dependent Claim
41 words
The method specified in claim 1 wherein (B) is deposited in a layer of sufficient thickness to create an excess of (B) upon the formation of the metal boride region, said excess (B) diffusing into the (Si) to produce p-type (Si).
Claim 4
Dependent Claim
25 words
The method specified in claim 1 further including the additional step of depositing (B) simultaneously with the (Si) to achieve p-type doping of the (Si).
Claim 5
Dependent Claim
30 words
The method specified in claim 3 wherein the additional step of depositing (B) dopes the (Si) to approximately 10 17 -10 19 atoms of (B) per cubic centimeter of (Si).
Claim 6
Dependent Claim
31 words
The method of claim 3 wherein the additional step of depositing (B) simultaneously with the (Si) is controlled to produce a more concentrated deposition of (B) adjacent the metal boride layer.
Claim 7
Dependent Claim
27 words
The method of claim 1 wherein the step of doping the (Si) with an n-type material comprises subjecting the (Si) to phosphorous (P) from a gaseous source.
Claim 8
Dependent Claim
22 words
The method specified in claim 1 wherein the n-type (Si) material is formed by simultaneous deposition of (Si) and said n-type dopant.
Claim 9
Dependent Claim
40 words
The method specified in claim 1 wherein the electrode means are configured to produce minimum interference to light impinging upon the device and further including the additional step of vacuum depositing an anti-reflective coating to maximize light entering the device.
Claim 10
Dependent Claim
40 words
The method specified in claim 1 wherein the step of heating the materials to form the metal boride region is conducted at approximately 900° C. for between fifteen and one hundred twenty minutes in a vacuum or an inert gas.
Claim 11
Independent Claim
131 words
A method of producing a thin film semiconductor p-n junction device comprising the steps of: forming on an electrically nonconductive substrate material a first electrode means comprising a layer of transition metal boride by vacuum depositing separate layers of said transition metal and boron (B) and reacting said layers for a time sufficient to form said transition metal boride layer, vacuum depositing on the thus formed transition metal boride layer a bottom layer of silicon doped to create one type majority carrier, forming on said bottom layer of silicon a top layer of silicon doped to create the opposite type of majority carrier, forming a second electrode means connected to said top silicon layer, and connecting separate terminal means to said second electrode means and said transition metal boride layer respectively.
Claim 12
Independent Claim
131 words
A method of producing a thin film semiconductor p-n junction device comprising the steps of: forming on an electrically nonconductive substrate material a first electrode means comprising a layer of transition metal boride by vacuum depositing separate layers of said transition metal and boron (B) and reacting said layers for a time sufficient to form said transition metal boride layer, vacuum depositing on the thus formed transition metal boride layer a bottom layer of silicon doped to create one type majority carrier, forming on said bottom layer of silicon a top layer of silicon doped to create the opposite type of majority carrier, forming a second electrode means connected to said top silicon layer, and connecting separate terminal means to said second electrode means and said transition metal boride layer respectively.
Claim 13
Dependent Claim
23 words
The method specified in claim 10 wherein said bottom silicon layer comprises p-type silicon and said top layer of silicon comprises n-type silicon.
References Cited (Backward Citations)
US3914856A
Cited
US4113532A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-01 | 1985-08-03 | 1986-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-01 | 1989-08-03 | 1990-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-01 | 1993-08-03 | 1994-02-02 | $7700.00 | Window Closed / Lapsed |