Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
298 words
In a process for the production of a chemically blended composition of non-elastomeric ethylene resins in a multiplicity of steps in the presence of a catalyst composed of a transition metal catalyst component and an organometallic compound, which comprises (a) a step of forming (i) an ethylene polymer or an ethylene/alpha-olefin copolymer having an alpha-olefin content of up to 15% by weight, said polymer or copolymer (i) having an intrinsic viscosity [η] of 0.3 to 3, and (b) a step of forming (ii) an ethylene/alpha-olefin copolymer having an alpha-olefin content of 0.2 to 30% by weight which is more than that of the polymer or copolymer (i), said copolymer (ii) having an intrinsic viscosity [η] of 1 to 12 which is at least 1.5 times that of the polymer or copolymer (i), said step (a) being performed first and then step (b) being performed in the presence of the product of step (a), or step (b) being performed first and then step (a) being performed in the presence of the product of step (b); the improvement wherein in steps (a) and (b), ethylene is polymerized or copolymerized with the alpha-olefin (1) in the presence of a catalyst composed of (A) a highly active titanium catalyst component containing titanium, magnesium and halogen and being capable of yielding an ethylene polymer in an amount of at least 250 g/millimole of a titanium atom.hr.kg/cm 2 of ethylene pressure and (B) an organoaluminum compound, (2) so that the weight ratio of the polymer or copolymer (i) formed in step (a) to the copolymer (ii) formed in step (b) is (30--less than 60): (above 40-70), and (3) so that the resulting chemically blended composition has an intrinsic viscosity [η] of 1 to 6 and an alpha-olefin content of 0.2 to 20% by weight.
Claim 2
Dependent Claim
298 words
In a process for the production of a chemically blended composition of non-elastomeric ethylene resins in a multiplicity of steps in the presence of a catalyst composed of a transition metal catalyst component and an organometallic compound, which comprises (a) a step of forming (i) an ethylene polymer or an ethylene/alpha-olefin copolymer having an alpha-olefin content of up to 15% by weight, said polymer or copolymer (i) having an intrinsic viscosity [η] of 0.3 to 3, and (b) a step of forming (ii) an ethylene/alpha-olefin copolymer having an alpha-olefin content of 0.2 to 30% by weight which is more than that of the polymer or copolymer (i), said copolymer (ii) having an intrinsic viscosity [η] of 1 to 12 which is at least 1.5 times that of the polymer or copolymer (i), said step (a) being performed first and then step (b) being performed in the presence of the product of step (a), or step (b) being performed first and then step (a) being performed in the presence of the product of step (b); the improvement wherein in steps (a) and (b), ethylene is polymerized or copolymerized with the alpha-olefin (1) in the presence of a catalyst composed of (A) a highly active titanium catalyst component containing titanium, magnesium and halogen and being capable of yielding an ethylene polymer in an amount of at least 250 g/millimole of a titanium atom.hr.kg/cm 2 of ethylene pressure and (B) an organoaluminum compound, (2) so that the weight ratio of the polymer or copolymer (i) formed in step (a) to the copolymer (ii) formed in step (b) is (30--less than 60): (above 40-70), and (3) so that the resulting chemically blended composition has an intrinsic viscosity [η] of 1 to 6 and an alpha-olefin content of 0.2 to 20% by weight.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein the polymerization or copolymerization in steps (a) and (b) is carried out under slurry polymerization conditions.
Claim 4
Dependent Claim
31 words
The process of claim 1 wherein the weight ratio of the polymer or copolymer (i) formed in step (a) to the copolymer (ii) formed in step (b) is 40-55 to 45-60.
Claim 5
Dependent Claim
34 words
The process of claim 1 wherein an ethylene/alpha-olefin copolymer is formed in step (a) and has an alpha-olefin content of up to 10% by weight and an intrinsic viscosity [η] of 0.4 to 2.5.
Claim 6
Dependent Claim
35 words
The process of claim 1 wherein the copolymer (ii) formed in step (b) has an intrinsic viscosity [η] of 1.5 to 10 which is at least 2 times that of the polymer or copolymer (i).
Claim 7
Dependent Claim
58 words
The process of claim 1 wherein said highly active titanium catalyst component has a titanium content of from about 0.2 to about 18% by weight, and a halogen/titanium mole ratio of from about 4 to about 300, and a specific surface area of at least about 10m 2 /g, the titanium being in the tetravalent or trivalent state.
Claim 8
Dependent Claim
62 words
The process of claim 6 wherein said highly active titanium catalyst component further comprises an electron donor selected from the group consisting of aliphatic carboxylic acids, aromatic carboxylic acids, aliphatic carboxylic acid esters, aromatic carboxylic acid esters, aliphatic ethers, alicyclic ethers, aliphatic ketones, aromatic ketones, aliphatic aldehydes, aliphatic alcohols, aliphatic acid amides, water, aliphatic nitriles, aromatic nitriles, aliphatic amines and aromatic amines.
Claim 9
Dependent Claim
99 words
The process of claim 6 wherein the titanium of the highly active titanium catalyst component is derived from a tetravalent titanium compound of the formula Ti(OR) 4-m X m , wherein R represents a hydrocarbon radical containing 1 to 12 carbon atoms, X is halogen, and 0≦m≦4; and wherein the magnesium of the highly active titanium catalyst component is derived from a magnesium compound selected from the group consisting of magnesium chloride, magnesium bromide, magnesium iodide, magnesium fluoride, magnesium hydroxide, magnesium oxide, magnesium hydroxyhalides, alkoxymagnesiums, alkoxy magnesium halides, aryloxy magnesiums, aryloxymagnesium halides, and alkyl magnesium halides, or mixtures thereof.