Process for carburizing ferrous metals
Assignee: Air Products and Chemicals Inc
•
Filing: 1980-04-22
•
Granted: 1981-12-22
•
Expires: 2000-04-22
Abstract
Abstract A process for carburizing steel in a furnace under an atmosphere derived from the decomposition of an oxygenated hydrocarbon containing up to three carbon atoms, no more than one carbon to carbon bond, and a carbon to oxygen ratio of from 1 to 2 such as alcohols, aldehydes, ethers, esters and mixtures thereof. The oxygenated hydrocarbon injected into the furnace produces an atmosphere under which an initial rapid stage of carburization takes place. After the initial rapid stage of carburization gaseous nitrogen is blended into the oxygenated hydrocarbon atmosphere throughout the remainder of the process with a concurrent reduction in the rate of injection of oxygenated hydrocarbon while maintaining volumetric flow through the furnace during the entire carburizing cycle. During the entire carburizing cycle, the carbon potential of the furnace atmosphere can be controlled by addition of a hydrocarbon gas enriching or carburizing agent.
Inventors
- 👤 Jelle H. Kaspersma
- 👤 Robert J. Peartree
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:21
CPC Classifications
C; C23; C23C; C23C8/00; C23C8/06; C23C8/08; C23C8/20; C23C8/22
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
221 words
A method of carburizing a ferrous article comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature in excess of 1500° F. (816° C.); b. injecting into the furnace an oxygenated hydrocarbon containing up to three carbon atoms, no more than one carbon to carbon bond, a carbon to oxygen ratio of from 1 to 2 and a boiling point no greater than 100° C., said oxygenated hydrocarbon selected from the group consisting of alcohols, aldehydes, esters, ethers and mixtures thereof to react and form a carburizing atmosphere in said furnace; c. establishing and maintaining a rate of injection of said oxygenated hydrocarbon and adding a hydrocarbon gas to maintain a carbon potential of between 0.8 and 1.1% in said furnace atmosphere for at least that portion of the total carburizing process where rapid carburizing occurs; d. subsequently reducing the rate of oxygenated hydrocarbon injection while maintaining a total injection rate by injecting nitrogen into said furnace to maintain said furnace atmosphere at a carbon potential similar to that for a conventional carburizing atmosphere and for a period of time to complete carburization of said articles to the desired case depth; and e. discharging said articles from said furnace and cooling at a rate determined by the desired physical properties of said article.
Claim 2
Independent Claim
221 words
A method of carburizing a ferrous article comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature in excess of 1500° F. (816° C.); b. injecting into the furnace an oxygenated hydrocarbon containing up to three carbon atoms, no more than one carbon to carbon bond, a carbon to oxygen ratio of from 1 to 2 and a boiling point no greater than 100° C., said oxygenated hydrocarbon selected from the group consisting of alcohols, aldehydes, esters, ethers and mixtures thereof to react and form a carburizing atmosphere in said furnace; c. establishing and maintaining a rate of injection of said oxygenated hydrocarbon and adding a hydrocarbon gas to maintain a carbon potential of between 0.8 and 1.1% in said furnace atmosphere for at least that portion of the total carburizing process where rapid carburizing occurs; d. subsequently reducing the rate of oxygenated hydrocarbon injection while maintaining a total injection rate by injecting nitrogen into said furnace to maintain said furnace atmosphere at a carbon potential similar to that for a conventional carburizing atmosphere and for a period of time to complete carburization of said articles to the desired case depth; and e. discharging said articles from said furnace and cooling at a rate determined by the desired physical properties of said article.
Claim 3
Dependent Claim
25 words
A method according to claim 1 wherein said furnace is maintained at a temperature of between 1550° F. (816° C.) and 1900° F. (1038° C.).
Claim 4
Dependent Claim
27 words
A method according to claim 1 wherein said oxygenated hydrocarbon is selected from the group consisting of methanol, ethanol, acetaldehyde, dimethylether, methyl formate, methlacetate and mixtures thereof.
Claim 5
Dependent Claim
12 words
A method according to claim 1 wherein said oxygenated hydrocarbon is methanol.
Claim 6
Dependent Claim
12 words
A method according to claim 1 wherein said oxygenated hydrocarbon is ethanol.
Claim 7
Dependent Claim
12 words
A method according to claim 1 wherein said oxygenated hydrocarbon is acetaldehyde.
Claim 8
Dependent Claim
12 words
A method according to claim 1 wherein said oxygenated hydrocarbon is dimethylether.
Claim 9
Dependent Claim
13 words
A method according to claim 1 wherein said oxygenated hydrocarbon is methyl formate.
Claim 10
Dependent Claim
12 words
A method according to claim 1 wherein said oxygenated hydrocarbon is methylacetate.
Claim 11
Dependent Claim
42 words
A method according to claim 1 wherein prior to charging said furnace the liquid equivalent of from three to five volume changes per hour of oxygenated hydrocarbon is sprayed into said furnace to condition said furnace atmosphere resulting from previous carburizing runs.
Claim 12
Dependent Claim
51 words
A method according to claim 1 wherein said reduced rate of injection of oxygenated hydrocarbon is accomplished by injecting a ratio of from 2 to 1 to 10 to 1 nitrogen to oxygenated hydrocarbon to a total volume flow equal to the volume of oxygenated hydrocarbon injected in said preceding step.
Claim 13
Dependent Claim
18 words
A method according to claim 11 wherein said ratio of nitrogen to oxygenated hydrocarbon is 2 to 1.
Claim 14
Independent Claim
210 words
A method of carburizing a ferrous article comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature of between 1500° F. (816° C.) and 1900° F. (1043° C.); b. injecting into the furnace an oxygenated hydrocarbon having from 1 to 3 carbon atoms, no more than one carbon to carbon bond and selected from the group consisting essentially of methanol, ethanol, acetaldehyde, dimethylether, methyl formate, methylacetate and mixtures thereof to react and form a carburizing atmosphere in said furnace; c. establishing and maintaining a rate of injection of said oxygenated hydrocarbon and adding thereto a hydrocarbon gas to maintain a carbon potential of between 0.8 and 1.1% in said furnace atmosphere for at least that portion of the total carburizing process where rapid carburizing occurs; d. subsequently reducing the rate of oxygenated hydrocarbon injection while maintaining a total injection rate by injecting nitrogen into said furnace to maintain said furnace atmosphere at a carbon potential in said furnace similar to that for a conventional carburizing atmosphere and for a period of time to complete carburization of said articles to the desired case depth; and e. discharging said articles from said furnace and cooling at a rate determined by the desired physical properties.
Claim 15
Independent Claim
210 words
A method of carburizing a ferrous article comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature of between 1500° F. (816° C.) and 1900° F. (1043° C.); b. injecting into the furnace an oxygenated hydrocarbon having from 1 to 3 carbon atoms, no more than one carbon to carbon bond and selected from the group consisting essentially of methanol, ethanol, acetaldehyde, dimethylether, methyl formate, methylacetate and mixtures thereof to react and form a carburizing atmosphere in said furnace; c. establishing and maintaining a rate of injection of said oxygenated hydrocarbon and adding thereto a hydrocarbon gas to maintain a carbon potential of between 0.8 and 1.1% in said furnace atmosphere for at least that portion of the total carburizing process where rapid carburizing occurs; d. subsequently reducing the rate of oxygenated hydrocarbon injection while maintaining a total injection rate by injecting nitrogen into said furnace to maintain said furnace atmosphere at a carbon potential in said furnace similar to that for a conventional carburizing atmosphere and for a period of time to complete carburization of said articles to the desired case depth; and e. discharging said articles from said furnace and cooling at a rate determined by the desired physical properties.
Claim 16
Dependent Claim
12 words
A method according to claim 13 wherein said oxygenated hydrocarbon is methanol.
Claim 17
Dependent Claim
42 words
A method according to claim 13 wherein prior to charging said furnace the liquid equivalent of from three to five volume changes per hour of oxygenated hydrocarbon is sprayed into said furnace to condition said furnace atmosphere resulting from previous carburizing runs.
Claim 18
Dependent Claim
33 words
A method according to claim 13 wherein said rapid carburization is effected by injection of said oxygenated hydrocarbons to maintain a furnace atmosphere of about two-thirds hydrogen and one-third carbon monoxide by volume.
Claim 19
Dependent Claim
51 words
A method according to claim 13 wherein said reduced rate of injection of oxygenated hydrocarbon is accomplished by injecting a ratio of from 2 to 1 to 10 to 1 nitrogen to oxygenated hydrocarbon to a total volume flow equal to the volume of oxygenated hydrocarbon injected in said preceding step.
Claim 20
Dependent Claim
18 words
A method according to claim 17 wherein said ratio of nitrogen to oxygenated hydrocarbon is 2 to 1.
Claim 21
Dependent Claim
18 words
A method according to claim 17 wherein said ratio of nitrogen to oxygenated hydrocarbon is 9 to 1.
Claim 22
Independent Claim
167 words
A method of carburizing a ferrous article comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature in excess of 1500° F. (816° C.); b. injecting methanol into the furnace to react and form a carburizing atmosphere in said furnace; c. establishing and maintaining a rate of injection of a hydrocarbon gas to maintain a carbon potential of between 0.8 and 1.1% in said furnace atmosphere for at least that portion of the total carburizing process where rapid carburizing occurs; d. subsequently reducing the rate of methanol injection while maintaining a total injection rate by injecting nitrogen into said furnace to maintain said furnace atmosphere at a carbon potential in said furnace similar to that for a conventional carburizing atmosphere and for a period of time to complete carburization of said articles to the desired case depth; and e. discharging said articles from said furnace and cooling at a rate determined by the desired physical properties of said article.
Claim 23
Independent Claim
167 words
A method of carburizing a ferrous article comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature in excess of 1500° F. (816° C.); b. injecting methanol into the furnace to react and form a carburizing atmosphere in said furnace; c. establishing and maintaining a rate of injection of a hydrocarbon gas to maintain a carbon potential of between 0.8 and 1.1% in said furnace atmosphere for at least that portion of the total carburizing process where rapid carburizing occurs; d. subsequently reducing the rate of methanol injection while maintaining a total injection rate by injecting nitrogen into said furnace to maintain said furnace atmosphere at a carbon potential in said furnace similar to that for a conventional carburizing atmosphere and for a period of time to complete carburization of said articles to the desired case depth; and e. discharging said articles from said furnace and cooling at a rate determined by the desired physical properties of said article.
Claim 24
Dependent Claim
25 words
A method according to claim 20 wherein said furnace is maintained at a temperature of between 1550° F. (816° C.) and 1900° F. (1043° C.).
Claim 25
Dependent Claim
21 words
A method according to claim 20 where gaseous ammonia is also added to the furnace in order to carbonitride the parts.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-21 | 1985-06-22 | 1985-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-21 | 1989-06-22 | 1989-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-21 | 1993-06-22 | 1993-12-22 | $7700.00 | Window Closed / Lapsed |