Method of producing a glass article having a graded refractive index profile of a parabolic nature
Assignee: Individual
•
Filing: 1979-01-29
•
Granted: 1981-11-24
•
Expires: 1999-01-29
Abstract
Abstract A method of producing a glass article having a graded refractive index profile of a parabolic nature is disclosed. The method comprises soaking a preform having a porous matrix with interconnected pores into a stuffing solution containing at least one index modifying dopant of predetermined solubility in the stuffing solution for a time interval to fill the pores with the dopant solution, precipitating the dopant into the porous matrix approximately uniformly throughout, soaking the preform into a solvent solution having a solubility for the dopant lower than the solubility of the dopant in the stuffing solution for a time interval sufficient to cause substantially all of the dopant to redissolve and for diffusion to take place out of the porous matrix in such a way that the dopant concentration decreases as a function of radial distance from the central axis, precipitating the dopant in the porous matrix by reducing the temperature of the preform to a level such that the dopant is precipitated out of solution, removing the solvent and where necessary decomposition products from the preform, and heating to consolidate the preform to produce a glass article having a graded refractive index profile of the parabolic nature.
Inventors
- 👤 Pedro B. Macedo
- 👤 Joseph H. Simmons
- 👤 Shigeo Murai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:00
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03C; C03C23/00; C03C23/0095
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
202 words
A method of producing a glass article having a graded refractive index profile of a near parabolic nature, comprising: (a) soaking a preform having a porous matrix with interconnected pores in a stuffing solution containing at least one index modifying dopant of predetermined solubility in the stuffing solution for a time interval to fill the pores with the dopant solution; (b) precipitating the dopant into the porous matrix approximately uniformly throughout; (c) soaking the preform into a solvent solution having a solubility for the dopant lower than said predetermined solubility of the dopant in the stuffing solution for a time interval sufficient to cause substantially all of the dopant to redissolve and for diffusion to take place out of the porous matrix in such a way that the dopant concentration decreases as a function of radial distance from the central axis; (d) precipitating the dopant in the porous matrix by reducing the temperature of the preform to a level such that the dopant is precipitated out of solution; (e) removing the solvent and where necessary decomposition products from the preform; and (f) heating to consolidate the preform to produce a glass article having a graded refractive index profile of the parabolic nature.
Claim 2
Independent Claim
202 words
A method of producing a glass article having a graded refractive index profile of a near parabolic nature, comprising: (a) soaking a preform having a porous matrix with interconnected pores in a stuffing solution containing at least one index modifying dopant of predetermined solubility in the stuffing solution for a time interval to fill the pores with the dopant solution; (b) precipitating the dopant into the porous matrix approximately uniformly throughout; (c) soaking the preform into a solvent solution having a solubility for the dopant lower than said predetermined solubility of the dopant in the stuffing solution for a time interval sufficient to cause substantially all of the dopant to redissolve and for diffusion to take place out of the porous matrix in such a way that the dopant concentration decreases as a function of radial distance from the central axis; (d) precipitating the dopant in the porous matrix by reducing the temperature of the preform to a level such that the dopant is precipitated out of solution; (e) removing the solvent and where necessary decomposition products from the preform; and (f) heating to consolidate the preform to produce a glass article having a graded refractive index profile of the parabolic nature.
Claim 3
Dependent Claim
29 words
A method as defined in claim 1, wherein the solubility of the solvent solution for the dopant in step (c) is between 0.5 to 0.9 of said predetermined solubility.
Claim 4
Dependent Claim
24 words
A method as defined in claim 1, wherein the temperature of the solvent solution in step (c) is between 55° C. and 85° C.
Claim 5
Dependent Claim
29 words
A method as defined in claim 1, wherein the soaking time in step (c) for a rod radius r' millimeters is between 10×(r'/4) 2 minutes and 180×(r'/4) 2 minutes.
Claim 6
Dependent Claim
27 words
A method as defined in claim 1, wherein the dopant in step (b) is precipitated in a solvent solution different from the solvent solution of step (c).
Claim 7
Dependent Claim
28 words
A method as defined in claim 1, wherein the solvent solution in step (c) is a low molecular weight alcohol having less than five carbon atoms in water.
Claim 8
Dependent Claim
17 words
A method as defined in claim 6, wherein the solvent solution is ethanol or propanol in water.
Claim 9
Dependent Claim
18 words
A method as defined in claim 7, wherein the solvent solution is 20 to 60% ethanol in water.
Claim 10
Dependent Claim
20 words
A method as defined in claim 3, wherein the temperature of the solvent solution is between 65° and 75° C.
Claim 11
Dependent Claim
20 words
A method as defined in claim 4, wherein the soaking time is between 30 minutes and 90 X(4'/4) 2 minutes.
Claim 12
Dependent Claim
20 words
A method as defined in claim 10, wherein the soaking time is between 45 minutes and 90 X(r'/4) 2 minutes.
Claim 13
Dependent Claim
31 words
A method as defined in claim 1, wherein the soaking time is within the range between 10 minutes less than and 20 minutes more than the dissolution time of the dopant.
Claim 14
Dependent Claim
17 words
A method as defined in claim 1, wherein the solvent in step (d) is ethanol or propanol.
Claim 15
Dependent Claim
93 words
A method as defined in claim 13, wherein the preform is soaked in the solvent solution of step (d) until its temperature has equilibrated at 0° C. and until the solvent has diffused thoroughly into the porous matrix, and further comprising the steps of subsequently soaking the preform in a solvent solution having a solubility of about 0.3 g/100 ml of solution at about room temperature until a very thin clad appears, cooling the solution to about 0° C., and returning the preform to solvent solution of step (d) for about 16 hours.
Claim 16
Dependent Claim
22 words
A method as defined in claim 1, further comprising heating the glass article to soften it and pulling it into a fiber.
Claim 17
Dependent Claim
27 words
A method as defined in claim 1, further comprising heating the glass article to soften it and pulling it into a rod of 1-3 mm in diameter.
References Cited (Backward Citations)
US2522524A
Cited
US3938974A
Cited
US3859073A
Cited
US4110093A
Cited
US4110096A
Cited
US4061486A
Cited
US4073579A
Cited
US4188198A
Cited
US4225330A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-23 | 1985-05-25 | 1985-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-23 | 1989-05-25 | 1989-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-23 | 1993-05-25 | 1993-11-24 | $7700.00 | Window Closed / Lapsed |