Ophthalmic lens with locally variable index of refraction and method of making same
Assignee: American Optical Corp
•
Filing: 1976-06-09
•
Granted: 1978-02-14
•
Expires: 1996-06-09
Abstract
Abstract Ophthalmic lenses with locally variable indices of refraction produced from microporous glass bodies diffused with inorganic salts and rendered transparent by heat treatment. Local variations in refractive index result from differences in concentrations of the salts produced by controlled diffusion and/or selective leaching after impregnation of the porous bodies.
Inventors
- 👤 Emil W. Deeg
- 👤 David A. Krohn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:15
CPC Classifications
G; G02; G02C; G02C7/00; G02C7/02; G02C7/04; G02C7/041; C; C03; C03C; C03C23/00; C03C23/008
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
185 words
The method of making an ophthalmic lens having locally variable index of refraction comprising the steps of: shaping a piece of microporous glass to the configuration desired of a blank from which said lens may be formed, said blank being greater in size than desired of said lens; placing a side of said blank in contact with a solution of an inorganic salt to cause at least partial filling of a preselected portion of said blank with said solution by capillary forces of open pores of said glass; removing said blank from said salt solution and causing evaporation of the solvent of said solution from said pores and precipitation of said salt in said preselected portion of said blank; heating the thus dried blank to a temperature and for a period of time sufficient to close said pores and render said blank transparent with local variations of its composition in said portion containing said precipitated salt, said variations in composition causing corresponding variations in refractive index, and grinding and polishing said heat-treated blank to the meniscus shape, size and surface finish of an ophthalmic lens.
Claim 2
Independent Claim
185 words
The method of making an ophthalmic lens having locally variable index of refraction comprising the steps of: shaping a piece of microporous glass to the configuration desired of a blank from which said lens may be formed, said blank being greater in size than desired of said lens; placing a side of said blank in contact with a solution of an inorganic salt to cause at least partial filling of a preselected portion of said blank with said solution by capillary forces of open pores of said glass; removing said blank from said salt solution and causing evaporation of the solvent of said solution from said pores and precipitation of said salt in said preselected portion of said blank; heating the thus dried blank to a temperature and for a period of time sufficient to close said pores and render said blank transparent with local variations of its composition in said portion containing said precipitated salt, said variations in composition causing corresponding variations in refractive index, and grinding and polishing said heat-treated blank to the meniscus shape, size and surface finish of an ophthalmic lens.
Claim 3
Dependent Claim
96 words
The method according to claim 1 wherein said preselected portion of said blank is caused to become completely filled with said solution of said salt and, following said step of causing evaporation of said solvent, said preselected portion of said dried blank is placed in contact with a substantially pure leaching medium for said salt to effect leaching thereof; said leaching step being terminated by removal of said blank from said leaching medium when resulting localized variations in densities of said precipitated salt substantially correspond to locally variable index of refractive effects desired in said lens.
Claim 4
Dependent Claim
52 words
The method according to claim 1 wherein filling of said preselected portion of said blank by capillary forces of open pores in said glass is assisted by application of a partial vacuum to at least a portion of a side of said blank opposite to that placed in contact with said solution.
Claim 5
Dependent Claim
48 words
The method according to claim 2 wherein said complete filling of said preselected portion of the blank by capillary forces is assisted by application of a partial vacuum to at least a portion of a side of said blank opposite to that placed in contact with said solution.
Claim 6
Dependent Claim
14 words
The method according to claim 1 wherein said solution includes a colored inorganic salt.
Claim 7
Dependent Claim
14 words
The method according to claim 2 wherein said solution includes a colored inorganic salt.
Claim 8
Dependent Claim
25 words
The method according to claim 2 wherein said blank is completely immersed in said substantially pure leaching medium for the duration of said leaching step.
Claim 9
Dependent Claim
8 words
The product of the process of claim 1.
References Cited (Backward Citations)
SU189988A1
Cited
US901659A
Cited
US1483509A
Cited
US1630724A
Cited
US1865691A
Cited
US2355746A
Cited
US2336227A
Cited
US3486808A
Cited
US3542535A
Cited
US3650598A
Cited
US3857689A
Cited
US3802761A
Cited
US3938974A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-13 | 1981-08-15 | 1982-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-13 | 1985-08-15 | 1986-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-13 | 1989-08-15 | 1990-02-14 | $7700.00 | Window Closed / Lapsed |