Process for activating plastic surfaces for metallization thereof by treatment with a complex forming solution
Assignee: Licentia Patent Verwaltungs GmbH
•
Filing: 1980-04-07
•
Granted: 1981-11-03
•
Expires: 2000-04-07
Abstract
Abstract Plastic surfaces are activated for the reception of adherent metal coatings by depositing noble metal nuclei thereon, the noble metal nuclei being deposited by a multistep process including the steps of mechanically roughening the surface, treating the roughened surface with a complex-former solution, thereafter treating the surface with a solution of a noble metal complex salt so as to exchange the noble metal complex for the complex deposited by the initial complex-former solution, and converting the noble metal complex to form metal nuclei.
Inventors
- 👤 Herbert Kunzig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:18
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; C23C18/28; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
93 words
A process for activating a plastic surface with noble metal nuclei for subsequent metallization, which comprises: (a) roughening the plastic surface to be metallized, by mechanical, nonoxidative means; (b) treating the mechanically, nonoxidatively roughened plastic surface with a complex-former solution to deposit a complex on the plastic surface; (c) treating the resulting plastic surface with a solution of a noble metal complex salt so that the complex deposited by the complex-former solution is exchanged for a noble metal complex on the plastic surface; and (d) converting the noble metal complex to metal nuclei.
Claim 2
Dependent Claim
93 words
A process for activating a plastic surface with noble metal nuclei for subsequent metallization, which comprises: (a) roughening the plastic surface to be metallized, by mechanical, nonoxidative means; (b) treating the mechanically, nonoxidatively roughened plastic surface with a complex-former solution to deposit a complex on the plastic surface; (c) treating the resulting plastic surface with a solution of a noble metal complex salt so that the complex deposited by the complex-former solution is exchanged for a noble metal complex on the plastic surface; and (d) converting the noble metal complex to metal nuclei.
Claim 3
Dependent Claim
48 words
The process as defined in claim 1 wherein said noble metal complex is converted to noble metal nuclei by first converting said noble metal complex to a noble metal hydroxide and then treating said noble metal hydroxide with an alkali formaldehyde solution or an acid stannous chloride solution.
Claim 4
Dependent Claim
38 words
The process as defined in claims 1 or 2 wherein the roughening of the plastic surface is effected by means of a blast of glass balls wherein the glass balls have a diameter of about 120 to 250μ.
Claim 5
Dependent Claim
26 words
The process as defined in claim 3 wherein said noble metal complex is converted to said noble metal nuclei by means of chemical or photochemical reduction.
Claim 6
Dependent Claim
44 words
The process as defined in claim 3 wherein a glass fiber reinforced plastic is employed and wherein before the roughened plastic surface is treated with the complex-former solution, the plastic is treated with a conditioner so as to attain wettability of the glass fibers.
Claim 7
Dependent Claim
25 words
The process as defined in claim 3 wherein said complex-former solution comprises a solution of ethylene diamine tetraacetic acid or an alkali metal salt thereof.
Claim 8
Dependent Claim
47 words
The process as defined in claim 1 wherein a glass fiber reinforced plastic is employed and wherein before the roughened plastic surface is treated with the complex-former solution of step (b), the plastic is treated with a conditioner so as to attain wettability of the glass fibers.
Claim 9
Dependent Claim
32 words
The process as defined in claim 1 or 2 or 7 wherein said complex-former solution of step (b) comprises a solution of ethylene diamine tetraacetic acid or an alkali metal salt thereof.
Claim 10
Dependent Claim
51 words
The process as defined in claim 8 wherein the noble metal complex salt solution is a solution of palladium chloride and an alkali chloride in hydrochloric acid, this solution then being diluted with water and thereafter adjusted to a pH of about 5.5 by the addition of an alkali hydroxide solution.
Claim 11
Dependent Claim
24 words
A process according to claim 9, wherein the solution of the noble metal complex salt contains acetone which stabilizes the noble metal complex salt.
Claim 12
Dependent Claim
46 words
A process according to claim 10 wherein the adjusting of the pH results in the palladium chloride disproportionating to a palladium tetrachloro complex, and the acetone is added to the noble metal complex salt solution containing the palladium tetrachloro complex after the pH has been adjusted.
Claim 13
Dependent Claim
54 words
The process as defined in claim 9, wherein the noble metal complex salt solution when diluted with water, contains about 1 gram per liter of solution of palladium chloride, about 1 gram per liter of solution of sodium chloride as the alkali chloride, and about 10 ml per liter of solution of hydrochloric acid.
Claim 14
Dependent Claim
15 words
The process according to claim 9, wherein said alkali hydroxide solution is sodium hydroxide solution.
Claim 15
Dependent Claim
26 words
The process as defined in claim 8 wherein said noble metal complex is converted to said noble metal nuclei by means of chemical or photochemical reduction.
Claim 16
Dependent Claim
47 words
The process as defined in claim 8, wherein said complex former solution has a pH greater than 13 and comprises a solution in water of about 200 grams per liter of solution of NaOH and about 10 grams per liter of solution of ethylene diamine tetraacetic acid.
Claim 17
Dependent Claim
55 words
The process as defined in claim 1 or 2 or 7 wherein the noble metal complex salt solution is a solution of palladium chloride and an alkali chloride in hydrochloric acid, this solution then being diluted with water and thereafter adjusted to a pH of about 5.5 by the addition of an alkali hydroxide solution.
Claim 18
Dependent Claim
15 words
The process according to claim 16, wherein said alkali hydroxide solution is sodium hydroxide solution.
Claim 19
Dependent Claim
26 words
The process as defined in claim 16 wherein said noble metal complex is converted to said noble metal nuclei by means of chemical or photochemical reduction.
Claim 20
Dependent Claim
54 words
The process as defined in claim 16, wherein the noble metal complex salt solution when diluted with water, contains about 1 gram per liter of solution of palladium chloride, about 1 gram per liter of solution of sodium chloride as the alkali chloride, and about 10 ml per liter of solution of hydrochloric acid.
Claim 21
Dependent Claim
23 words
The process according to claim 19, wherein the solution of the noble metal complex salt contains acetone which stabilizes the noble metal complex.
Claim 22
Dependent Claim
24 words
A process according to claim 16, wherein the solution of the noble metal complex salt contains acetone which stabilizes the noble metal complex salt.
Claim 23
Dependent Claim
46 words
A process according to claim 21 wherein the adjusting of the pH results in the palladium chloride disproportionating to a palladium tetrachloro complex, and the acetone is added to the noble metal complex salt solution containing the palladium tetrachloro complex after the pH has been adjusted.
Claim 24
Dependent Claim
16 words
A process according to claim 21 wherein said solution contains up to 50% by volume acetone.
Claim 25
Dependent Claim
15 words
A process according to claim 21, wherein said solution contains about 1% by volume acetone.
Claim 26
Dependent Claim
16 words
A process according to claim 24, wherein said solution contains up to 50% by volume acetone.
Claim 27
Dependent Claim
15 words
A process according to claim 24, wherein said solution contains about 1% by volume acetone.
Claim 28
Dependent Claim
30 words
The process as defined in claim 1 or 2 or 7 wherein said noble metal complex is converted to said noble metal nuclei by means of chemical or photochemical reduction.
Claim 29
Dependent Claim
40 words
The process as defined in claim 1 wherein said noble metal complex is converted to metal nuclei by first converting said noble metal complex to a noble metal hydroxide and then converting said noble metal hydroxide to said noble metal.
Claim 30
Dependent Claim
18 words
The process as defined in claim 1 wherein treating steps (b) and (c) are each performed by dipping.
Claim 31
Dependent Claim
29 words
A process according to claim 1, 2, 7, 28, or 29, wherein the solution of the noble metal complex salt contains acetone which stabilizes the noble metal complex salt.
Claim 32
Dependent Claim
16 words
A process according to claim 30, wherein said solution contains up to 50% by volume acetone.
Claim 33
Dependent Claim
15 words
A process according to claim 30, wherein said solution contains about 1% by volume acetone.
Claim 34
Dependent Claim
12 words
Process according to claim 30, wherein said solution is an aqueous solution.
References Cited (Backward Citations)
US3484270A
Cited
US3607350A
Cited
US3627558A
Cited
US3620804A
Cited
JPS4828356A
Cited
US4148945A
Cited
US3915809A
Cited
US3993807A
Cited
US3962496A
Cited
US4153746A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-02 | 1985-05-04 | 1985-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-02 | 1989-05-04 | 1989-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-02 | 1993-05-04 | 1993-11-03 | $7700.00 | Window Closed / Lapsed |