Process for manufacturing a radiographic intensifying screen

Claim 2

A process for manufacturing a radiographic intensifying screen comprising steps of applying to a surface of a support a dispersion comprising (a) an ultraviolet radiation-curable resin composition which is composed of an unsaturated resin, a polymerizable monomer and a sensitizer, and (b) a radioluminescent phosphor dispersed in said composition (a) to form a coating on said support, removing from said coating, ingredients, if present, other than composition (a) or phosphor (b) so that the coating consists essentially of composition (a) and phosphor (b); and then curing the coating by exposing said coating to ultraviolet radiation to form a fluorescent layer on said support.

Claim 3

A process as defined in claim 1 wherein the weight ratio of said unsaturated resin to said polymerizable monomer is within the range of 1:0.1 to 1:2, and the amount of said sensitizer is within the range of 0.01 to 10 weight % of said ultraviolet radiation-curable resin composition.

Claim 4

A process as defined in claim 2 wherein said weight ratio is within the range of 1:0.5 to 1:1.5, and said amount is within the range of 0.5 to 5 weight %.

Claim 5

A process as defined in claim 1 wherein the weight ratio of said ultraviolet radiation-curable resin composition to said radioluminescent phosphor is within the range of 1:1 to 1:20.

Claim 6

A process as defined in claim 4 wherein said weight ratio is within the range of 3:10 to 1:10.

Claim 7

A process as defined in claim 1 wherein the exposed surface of said coating is exposed to said ultraviolet radiation.

Claim 8

A process as defined in claim 1 wherein said support is ultraviolet radiation-transmissive, and both surfaces of said coating are exposed to said ultraviolet radiation.

Claim 9

A process as defined in claim 1 wherein the source of said ultraviolet radiation is a mercury vapor lamp.

Claim 10

A process as defined in claim 8 wherein said mercury vapor lamp emits ultraviolet radiation of 365 nm.

Claim 11

A process as defined in claim 1 wherein at least a portion of the wavelength region of light absorption of the sensitizer overlaps at least a portion of the wavelength region of light emission of the radioluminescent phosphor when the latter is excited by ultraviolet radiation.

Claim 12

A process as defined in claim 10 wherein said light emission occurs as the phosphor is excited by said ultraviolet radiation during the coating curing step.

Claim 13

A process as defined in claims 1 or 10 wherein said overlapping wavelength regions extend from near ultraviolet to 500 nm.

Claim 14

A process as defined in claims 1 or 10 wherein said sensitizer absorbs light at least in the wavelength region of 200 to 500 nm while the radioluminescent phosphor at last exhibits light emission in the wavelength region less than about 500 nm when excited by ultraviolet radiation.

Claim 15

A process as in claim 1 wherein a solvent is added to said dispersion to facilitate the application of the dispersion to the support and wherein said solvent is remoed from the coating prior to the curing step.

Claim 16

A process for manufacturing a radiographic intensifying screen comprising steps of applying to a surface of a support a dispersion comprising (a) a first ultraviolet radiation-curable resin composition which is composed of a first unsaturated resin, a first polymerizable monomer and a first sensitizer, and (b) a radioluminescent phosphor dispersed in said first ultraviolet radiation-curable resin composition to form a first coating on said support, removing from said first coating, ingredient, if present, other than composition (a) or phosphor (b) so that the first coating consists essentially of composition (a) and phosphor (b); and then curing said first coating by exposing said first coating to first ultraviolet radiation to form a fluorescent layer on said support, applying to a surface of said fluorescent layer a second ultraviolet radiation-curable resin composition which is composed of a second unsaturated resin, a second polymerizable monomer and a second sensitizer to form a second coating on said fluorescent layer, and removing from said second coating, ingredients, if present, other than said second composition so that the second coating consists essentially of the second composition; and then curing said second coating by exposing said second coating to second ultraviolet radiation to form a transparent protective layer.

Claim 17

A process for manufacturing a radiographic intensifying screen comprising steps of applying to a surface of a support a dispersion comprising (a) a first ultraviolet radiation-curable resin composition which is composed of a first unsaturated resin, a first polymerizable monomer and a first sensitizer, and (b) a radioluminescent phosphor dispersed in said first ultraviolet radiation-curable resin composition to form a first coating on said support, removing from said first coating, ingredient, if present, other than composition (a) or phosphor (b) so that the first coating consists essentially of composition (a) and phosphor (b); and then curing said first coating by exposing said first coating to first ultraviolet radiation to form a fluorescent layer on said support, applying to a surface of said fluorescent layer a second ultraviolet radiation-curable resin composition which is composed of a second unsaturated resin, a second polymerizable monomer and a second sensitizer to form a second coating on said fluorescent layer, and removing from said second coating, ingredients, if present, other than said second composition so that the second coating consists essentially of the second composition; and then curing said second coating by exposing said second coating to second ultraviolet radiation to form a transparent protective layer.

Claim 18

A process as defined in claim 15 wherein the weight ratio of said first unsaturated resin to said first polymerizable monomer and the weight ratio of said second unsaturated resin to said second polymerizable monomer are both within the range of 1:0.1 to 1:2, and the amount of said first sensitizer and the amount of said second sensitizer are both within the range of 0.01 to 10 weight % of said first ultraviolet radiation-curable resin composition and of said second ultraviolet radiation-curable resin composition, respectively.

Claim 19

A process as defined in claim 16 wherein the range of said weight ratio is 1:0.5 to 1:1.5, and the range of said amount is 0.5 to 5 weight %.

Claim 20

A process as defined in claim 15 wherein the weight ratio of said first ultraviolet radiation-curable resin composition to said radioluminescent phosphor is within the range of 1:1 to 1:20.

Claim 21

A process as defined in claim 18 wherein said weight ratio is within the range of 3:10 to 1:10.

Claim 22

A process as defined in claim 15 wherein the exposed surface of said first coating is exposed to said first ultraviolet radiation.

Claim 23

A process as defined in claim 15 wherein said support is ultraviolet radiation-transmissive, and both surfaces of said coating are exposed to said first ultraviolet radiation.

Claim 24

A process as defined in claim 15 wherein the source of said first ultraviolet radiation and the source of said second ultraviolet radiation are both mercury vapor lamps.

Claim 25

A process as defined in claim 17 wherein said mercury vapor lamp emits ultraviolet radiation of 365 nm.

Claim 26

A process as defined in claim 15 wherein at least a portion of the wavelength regions of light absorption of the first and second sensitizers respectively overlaps at least a portion of the wavelength regions of light emission of the first and second radioluminescent phosphors when the latter are excited by ultraviolet radiation.

Claim 27

A process as defined in claim 24 wherein said light emissions occur as the phosphors are excited by said ultraviolet radiation during their respective coating curing steps.

Claim 28

A process as defined in claims 15 or 24 wherein the respective overlapping wavelength regions extend from near ultraviolet to 500 nm.

Claim 29

A process as defined in claims 15 or 24 wherein said first and second sensitizers absorb light at least in the wavelength region of 200 to 500 nm while the first and second radioluminescent phosphors at least exhibit light emission in the wavelength region less than about 500 nm when excited by ultraviolet radiation.

Claim 30

A process as in claim 15 wherein a first solvent is added to said dispersion to facilitate the application of the dispersion to the support and wherein said first solvent is removed from the first coating prior to the first curing step.

Claim 31

A process for manufacturing a radiographic intensifying screen comprising steps of applying to a surface of a flat plate a dispersion comprising (a) an ultraviolet radiation-curable resin composition which is composed of an unsaturated resin, a polymerizable monomer and a sensitizer, and (b) a radioluminescent phosphor dispersed in said composition (a) to form a coating on said flat plate, removing from said coating, ingredients, if present, other than composition (a) or phosphor (b) so that the coating consists essentially of composition (a) and phosphor (b); and then curing said coating by exposing said coating to ultraviolet radiation to form a fluorescent layer on said flat plate, peeling off said fluorescent layer from said flat plate, and bonding said fluorescent layer to a surface of a support.

Claim 32

A process for manufacturing a radiographic intensifying screen comprising steps of applying to a surface of a flat plate a dispersion comprising (a) an ultraviolet radiation-curable resin composition which is composed of an unsaturated resin, a polymerizable monomer and a sensitizer, and (b) a radioluminescent phosphor dispersed in said composition (a) to form a coating on said flat plate, removing from said coating, ingredients, if present, other than composition (a) or phosphor (b) so that the coating consists essentially of composition (a) and phosphor (b); and then curing said coating by exposing said coating to ultraviolet radiation to form a fluorescent layer on said flat plate, peeling off said fluorescent layer from said flat plate, and bonding said fluorescent layer to a surface of a support.

Claim 33

A process as defined in claim 29 wherein the weigh ratio of said unsaturated resin to said polymerizable monomer is within the range of 1:0.1 to 1:2, and the amount of said sensitizer is within the range of 0.01 to 10 weight % of said ultraviolet radiation-curable resin composition.

Claim 34

A process as defined in claim 30 wherein said weight ratio is within the range of 1:0.5 to 1:1.5, and said amount is within the range of 0.5 to 5 weight %.

Claim 35

A process as defined in claim 29 wherein the weight ratio of said ultraviolet radiation-curable resin composition to said radioluminescent phosphor is within the range of 1:1 to 1:20.

Claim 36

A process as defined in claim 32 wherein said weight ratio is within the range of 3:10 to 1:10.

Claim 37

A process as defined in claim 29 wherein the exposed surface of said coating is exposed to said ultraviolet radiation.

Claim 38

A process as defined in claim 29 wherein said flat plate is ultraviolet radiation-transmissive, and both surfaces of said coating are exposed to said ultraviolet radiation.

Claim 39

A process as defined in claim 29 wherein the source of said ultraviolet radiation is a mercury vapor lamp.

Claim 40

A process as defined in claim 36 wherein said mercury vapor lamp emits ultraviolet radiation of 365 nm.

Claim 41

A process as defined in claim 29 wherein at least a portion of the wavelength region of light absorption of the sensitizer overlaps at least a portion of the wavelength region of light emission of the radioluminescent phosphor when the latter is excited by ultraviolet radiation.

Claim 42

A process as defined in claim 38 wherein said light emission occurs as the phosphor is excited by said ultraviolet radiation during the coating curing step.

Claim 43

A process as defined in claims 29 or 38 wherein said overlapping wavelength regions extend from near ultraviolet to 500 nm.

Claim 44

A process as defined in claims 29 or 38 wherein said sensitizer absorbs light at least in the wavelength region of 200 to 500 nm while the radioluminescent phosphor at least exhibits light emission in the wavelength region less than about 500 nm when excited by ultraviolet radiation.

Claim 45

A process as in claim 29 wherein a solvent is added to said dispersion to facilitate the application of the dispersion to the plate and wherein said solvent is removed from the coating prior to the curing step.