Process for fibrillating polyester

Claim 2

A process for improving the hand and comfort of a textile fabric comprising a plurality of yarns each said yarn comprising a multiplicity of texturized polyester filaments comprising the steps of: treating said textile fabric with an alkaline aqueous solution having a pH of at least about 9.5, the temperature of said solution being between about 30 and 70; and breaking on an average basis at least about 5 of said filaments per square centimeter of fabric while said fabric is wet with said aqueous alkaline solution.

Claim 3

The process of claim 1 wherein said filaments are broken by repeatedly passing the wet fabric through an orifice.

Claim 4

The process of claim 2 wherein said fabric is forced through said orifice by the action of a jet of said alkaline aqueous solution.

Claim 5

The process of claim 1 wherein said filaments are broken by abrading said fabric while immersed in said aqueous alkaline solution, and wherein aqueous alkaline solution also contains a quaternary ammonium salt.

Claim 6

The process of claim 1 wherein said filaments are broken by passing a fluid jet through said fabric.

Claim 7

The process of claim 1 wherein the pH of said aqueous alkaline solution is between about 10 and 13.5, the temperature is between about 30° and 70° C. and wherein said fabric is exposed to said aqueous alkaline solution for between about five and 120 minutes.

Claim 8

The process of claim 6 wherein on an average at least about 15 filaments per square centimeter of fabric are broken.

Claim 9

The process of claim 6 wherein on an average at least about 50 filaments per square centimeter of fabric are broken.

Claim 10

The process of claim 8 wherein said filaments are broken by repeatedly passing the wet fabric through an orifice.

Claim 11

The process of claim 9 wherein said fabric is forced through said orifice by the action of a jet of said alkaline aqueous solution.

Claim 12

The process of claim 1 wherein said filaments are broken by repeatedly passing the wet fabric through an orifice.

Claim 13

The process of claim 11 wherein said fabric is forced through said orifice by the action of a jet of said alkaline aqueous solution.

Claim 14

The process of claim 1 wherein said texturized polyester filaments are multilobal, and wherein said aqueous alkaline solution contains a quaternary ammonium salt.

Claim 15

The process of claim 13 wherein on an average at least about 15 filaments per square centimeter of fabric are broken.

Claim 16

The process of claim 13 wherein on an average at least about 50 filaments per square centimeter of fabric are broken.

Claim 17

The process of claim 1 wherein on an average at least about 15 filaments per square centimeter of fabric are broken.

Claim 18

The process of claim 1 wherein on an average at least about 50 filaments per square centimeter of fabric are broken.

Claim 19

A process for improving the hand and comfort of a textile fabric comprising a plurality of yarns each said yarn comprising a multiplicity of multilobal texturized polyester filaments comprising the steps of: immersing said textile fabric in an aqueous alkaline solution having a pH between about 10 and 13.5 at temperatures between about 30° and 70° C.; and breaking and fibrillating at least about 50 of said filaments per square centimeter of fabric by forcing said fabric through an orifice by the action of a jet of said aqueous alkaline solution.

Claim 20

A process for improving the hand and comfort of a textile fabric comprising a plurality of yarns each said yarn comprising a multiplicity of multilobal texturized polyester filaments comprising the steps of: immersing said textile fabric in an aqueous alkaline solution having a pH between about 10 and 13.5 at temperatures between about 30° and 70° C.; and breaking and fibrillating at least about 50 of said filaments per square centimeter of fabric by forcing said fabric through an orifice by the action of a jet of said aqueous alkaline solution.