Abstract This invention is related to the production of glazes and enamels for decorating glass, glass-ceramic, and ceramic articles. The glass frits suitable therefor exhibit good glass stability, coefficients of thermal expansion (20°-300° C.) between about 65-75×10 -7 /°C., demonstrate excellent resistance to attack by acids and bases, and, being essentially free from toxic heavy metals such as lead, are eminently useful in food preparation and service applications. The frit compositions are encompassed within the system Li 2 O--BaO--TiO 2 --ZrO 2 --B 2 O 3 --SiO 2 , wherein at least one member of the group consisting of MgO, CaO, ZnO, and Bi 2 O 3 , is optionally present. Operable frits are encompassed within the ranges, expressed in weight percent, of: ______________________________________ SiO 2 35-47%
B 2 O 3 5.5-9
BaO 24-42
TiO 2 1.5-4
ZrO 2 6-10
Li 2 O 3 1-5
MgO 0-5
CaO 0-4
SrO 0-8
ZnO 0-10
Bi 2 O 3 0-8
SrO + MgO + CaO + ZnO + Bi 2 O 3 0-10
______________________________________
A frit essentially free from cadmium and lead demonstrating good glass stability, a coefficient of thermal expansion (20°-300° C.) between about 65-75×10 -7 /°C., a viscosity suitable for firing at about 700°-950° C., and excellent resistance to attack by acids and bases as evidenced by no change of gloss and a weight loss of no more than about 0.02% after immersion for 24 hours at 96° C. into an aqueous solution containing 10% by weight citric acid and by no change of gloss and a weight loss of no more than about 0.02% after immersion for 24 hours at 96° C. into an aqueous solution containing 0.3% by weight of an alkaline detergent, said frit consisting essentially, expressed in weight percent on the oxide basis as calculated from the batch, of ______________________________________
SiO.sub.2 35-47
B.sub.2 O.sub.3
5.5-9
BaO 24-42
TiO.sub.2 1.5-4
ZrO.sub.2 6-10
Li.sub.2 O 1-5
MgO 0-5
CaO 0-4
SrO 0-8
ZnO 0-10
Bi.sub.2 O.sub.3
0-8
MgO + CaO + SrO + ZnO + Bi.sub.2 O.sub.3
0-10
______________________________________
Claim 2
Dependent Claim
169 words
A frit essentially free from cadmium and lead demonstrating good glass stability, a coefficient of thermal expansion (20°-300° C.) between about 65-75×10 -7 /°C., a viscosity suitable for firing at about 700°-950° C., and excellent resistance to attack by acids and bases as evidenced by no change of gloss and a weight loss of no more than about 0.02% after immersion for 24 hours at 96° C. into an aqueous solution containing 10% by weight citric acid and by no change of gloss and a weight loss of no more than about 0.02% after immersion for 24 hours at 96° C. into an aqueous solution containing 0.3% by weight of an alkaline detergent, said frit consisting essentially, expressed in weight percent on the oxide basis as calculated from the batch, of ______________________________________
SiO.sub.2 35-47
B.sub.2 O.sub.3
5.5-9
BaO 24-42
TiO.sub.2 1.5-4
ZrO.sub.2 6-10
Li.sub.2 O 1-5
MgO 0-5
CaO 0-4
SrO 0-8
ZnO 0-10
Bi.sub.2 O.sub.3
0-8
MgO + CaO + SrO + ZnO + Bi.sub.2 O.sub.3
0-10
______________________________________
Claim 3
Dependent Claim
84 words
A frit according to claim 1 exhibiting a coefficient of thermal expansion ( 20°-300° C.) between about 65-70×10 -7 /°C. and a viscosity suitable for firing at about 700°-850° C. consisting essentially, expressed in weight percent on the oxide basis as calculated from the batch, of ______________________________________
SiO.sub.2 35-47 MgO 0-4
B.sub.2 O.sub.3
6-8 CaO 0-4
BaO 31-39 SrO 0-8
TiO.sub.2 2-3 ZnO 0-6
ZrO.sub.2 8-9.5 Bi.sub.2 O.sub.3
0-7
Li.sub.2 O 1-2.5
MgO + CaO + SrO + ZnO + Bi.sub.2 O.sub.3
2-8
______________________________________