Method for forming an insulating film layer of silicon oxynitride on a semiconductor substrate surface
Assignee: Fujitsu Ltd
•
Filing: 1979-10-15
•
Granted: 1981-08-04
•
Expires: 1999-10-15
Abstract
Abstract An insulating film layer consisting of silicon oxynitride is formed on a silicon semiconductor substrate surface by bringing a surface of a silicon substrate into contact with an ammonia gas atmosphere containing a gas comprising containing substance gas, for example, oxygen gas, carbon dioxide gas, carbon monoxide gas, nitrogen monoxide gas, nitrogen dioxide gas, or water vapor, in a volume concentration of from 10 2 to 10 4 ppm in terms of molecular oxygen, at an elevated temperature, for example, of from 900°to 1300° C.
Inventors
- 👤 Takao Nozaki
- 👤 Takashi Ito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:34
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6318; H10P14/6322; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6927; Y; Y10; Y10S; Y10S438/00; Y10S438/909
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
97 words
A method for forming an insulating film on a surface of a silicon semiconductor substrate with a relatively low density of surface defects between the substrate and insulating film, comprising directly converting a surface portion of the silicon substrate into an insulating film layer comprising silicon oxynitride by bringing a cleaned surface of said silicon substrate into contact with an atmosphere consisting essentially of an ammonia gas and an oxygen-containing substance gas at an elevated temperature, said oxygen-containing substance gas having a volume concentration, in terms of molecular oxygen, of from 10 2 to 10 4 ppm.
Claim 2
Independent Claim
97 words
A method for forming an insulating film on a surface of a silicon semiconductor substrate with a relatively low density of surface defects between the substrate and insulating film, comprising directly converting a surface portion of the silicon substrate into an insulating film layer comprising silicon oxynitride by bringing a cleaned surface of said silicon substrate into contact with an atmosphere consisting essentially of an ammonia gas and an oxygen-containing substance gas at an elevated temperature, said oxygen-containing substance gas having a volume concentration, in terms of molecular oxygen, of from 10 2 to 10 4 ppm.
Claim 3
Dependent Claim
42 words
A method as claimed in claim 1, wherein said oxygen-containing substance gas is selected from the group consisting of oxygen gas, carbon dioxide gas, carbon monoxide gas, nitrogen monoxide, nitrogen dioxide, water vapor and mixtures of two or more of said gases.
Claim 4
Dependent Claim
32 words
A method as claimed in claim 1, wherein said contact of said silicon substrate surface with the ammonia gas atmosphere is carried out at a temperature of from 900° to 1300° C.
Claim 5
Dependent Claim
58 words
The method of claim 1 comprising providing said molecular oxygen to have volume concentration in the range from 10 2 to 10 3 ppm, and performing said directly converting said silicon substrate to oxynitride to have a density of surface defects of less than 10 12 /cm 2 and a refractive index in the range from 1.5to 1.8.
Claim 6
Dependent Claim
27 words
A method as claimed in claim 1, 2, 3 or 4 wherein said reaction is carried out under a pressure of from 10 to 10 -5 atm.
Claim 7
Dependent Claim
27 words
A method as claimed in claim 1, 2 or 3 wherein said silicon oxynitride insulating film has a refractive index of from about 1.5 to about 1.8.
Claim 8
Dependent Claim
35 words
The method of claim 1, 2, 3 or 4, comprising contacting said semiconductor substrate surface with said gas for a period between 1 to 1000 minutes at a pressure from 10 to 10 -5 atm.
Claim 9
Dependent Claim
27 words
The method of claim 1, 2, 3 or 4, comprising forming said insulating film layer to have a thickness in the range from 35 to 100 angstroms.
Claim 10
Dependent Claim
36 words
The method of claim 1, 2, 3 or 4, comprising forming said insulating film layer on said semiconductor substrate surface to have a density of structural defects of as little as 10 11 /cm 2 .
Claim 11
Dependent Claim
37 words
The method of claim 1, 2, 3 or 4, comprising forming said insulating film layer to effectively mask against an oxidizing atmosphere for a period in the range from 10 minutes up to at least 70 minutes.
Claim 12
Dependent Claim
41 words
The method of claim 1, 2, 3 or 4, comprising forming said insulating film layer to have an etching rate in a mixture of 10 parts of NH 4 F to 1 part HF of 100 angstroms per minute or less.
Claim 13
Dependent Claim
40 words
The method of claim 4, said oxygen-containing substance gas being selected from the group consisting of oxygen gas, carbon dioxide gas, carbon monoxide gas, nitrogen monoxide, nitrogen dioxide, water vapor and mixtures of two or more of the said gases.
Claim 14
Dependent Claim
32 words
The method of claim 4 or 12, wherein said contact of said silicon substrate surface with the ammonia gas atmosphere is carried out at a temperature of from 900° to 1300° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-03 | 1985-02-02 | 1985-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-03 | 1989-02-02 | 1989-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-03 | 1993-02-02 | 1993-08-04 | $7700.00 | Window Closed / Lapsed |