US4278769A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Blowing agent concentrate
Assignee: Dynamit Nobel AG
•
Filing: 1979-02-21
•
Granted: 1981-07-14
•
Expires: 1999-02-21
Abstract
Abstract A blowing agent concentrate comprising a chemical blowing agent and a thermoplastic composition vehicle therefore, said thermoplastic composition being a saturated polyester and/or copolyester having a crystalline melting point between 100° C. and 220° C. and a reduced viscosity of 0.4 dl/g to 1.6 dl/g; the use of such blowing agent concentrate in the formation of foamed articles of high molecular weight polyalkyleneterephthalate which articles can be filled and/or reinforced and/or flame proofed and can contain other additives. Particularly contemplated is the use of such blowing agent concentrate in the formation of glass fiber reinforced structural foam moldings of polyalkyleneterephthalates especially polytetramethylene terephthalates.
Inventors
- 👤 Peter Gebauer
- 👤 Karl G. Sturm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 04:58
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08J3/00; C08J3/20; C08J3/22; C08J3/226; C08J9/0061; C08J2201/00; C08J2201/02; C08J2201/024; C08J2367/00; C08J2367/02; C08J2467/00
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
64 words
A blowing agent concentrate consisting of a chemical blowing agent and a thermoplastic vehicle therefor, said vehicle being a saturated polyester or copolyester having a crystalline melting point between 100° C. and 220° C. and a reduced viscosity between 0.4 dl/g and 1.6 dl/g, said chemical blowing agent being present in said blowing agent concentrate in an amount of at least 5 weight percent.
Claim 2
Dependent Claim
64 words
A blowing agent concentrate consisting of a chemical blowing agent and a thermoplastic vehicle therefor, said vehicle being a saturated polyester or copolyester having a crystalline melting point between 100° C. and 220° C. and a reduced viscosity between 0.4 dl/g and 1.6 dl/g, said chemical blowing agent being present in said blowing agent concentrate in an amount of at least 5 weight percent.
Claim 3
Dependent Claim
24 words
A blowing agent concentrate according to claim 1 wherein the polyester or copolyester has a crystalline melting point between 160° C. and 220° C.
Claim 4
Dependent Claim
90 words
A blowing agent concentrate according to claim 1 wherein at least 50 mole percent of the acid component of the polyester or copolyester is supplied by terephthalic acid or a polyester forming derivative thereof, the balance of the acid components being supplied by one or more other aromatic and/or saturated aliphatic dicarboxylic acid of 2 to 12 carbon atoms between the functional groups or their polyester-forming derivatives and the diol component of such polyester or copolyester is supplied by at least one aliphatic glycol having 2 to 12 carbon atoms.
Claim 5
Dependent Claim
40 words
A blowing agent according to claim 3 wherein the polyester or copolyester are derived, with respect to the diol or codiol component, from ethylene glycol, propanediol-1,2, propanediol-1,3, butanediol-1,3, butanediol-1,4, pentanediol-1,5, neopentyl glycol, hexanediol-1,6, octanediol-1,8 or cyclohexanedimethanol or a mixture thereof.
Claim 6
Dependent Claim
45 words
A blowing agent according to claim 3 wherein the thermoplastic composition is a copolyester in which the co-acid is supplied by isophthalic acid and/or sebacic acid and/or azelaic acid and/or succinic acid and/or glutaric acid and/or adipic acid and/or cyclohexanedicarboxylic acid or their polyester-forming derivatives.
Claim 7
Dependent Claim
45 words
A blowing agent concentrate according to claim 5 wherein 60 to 90 mole percent of the acid component of the copolyester is supplied by terephthalic acid or a polyester-forming derivative thereof, the balance being supplied by one or more co-acids or their respective polyester-forming derivatives.
Claim 8
Dependent Claim
24 words
A blowing agent concentrate according to claim 6 wherein at least a portion of the diol component of the copolyester is supplied by butanediol-1,4.
Claim 9
Dependent Claim
23 words
A blowing agent concentrate according to claim 7 wherein up to 100% of the diol component of the copolyester is supplied by butanediol-1,4.
Claim 10
Dependent Claim
31 words
A blowing agent concentrate according to claim 8 wherein up to 10 mole percent of the butanediol-1,4 is replaced by one or more other diols having 2 to 12 carbon atoms.
Claim 11
Dependent Claim
50 words
A blowing agent concentrate according to claim 6 wherein 65 to 75 mole percent of the acid component of the copolyester is supplied by terephthalic acid or its polyester-forming derivatives, the balance of the acid component being adipic acid and the diol component of the copolyester is supplied by butanediol-1,4.
Claim 12
Dependent Claim
57 words
A blowing agent concentrate according to claim 6 wherein 60 to 85 mole percent of the acid component of the copolyester is supplied by terephthalic or a polyester-forming derivative thereof and 15 to 40 mole percent of the acid component is supplied by isophthalic acid or a polyester-forming derivative thereof, the diol component being supplied by butanediol-1,4.
Claim 13
Dependent Claim
71 words
A blowing agent concentrate according to claim 6 wherein 60 to 85 mole percent of the acid component of the copolyester is supplied by terephthalic acid or a polyester-forming derivative thereof, the balance of the acid component being supplied at least in part by azelaic and/or adipic and/or sebacic acid or a polyester-forming derivative thereof, any balance to make up 100% being supplied by isophthalic acid or a polyester-forming derivative thereof.
Claim 14
Dependent Claim
82 words
A blowing agent concentrate according to claim 4 wherein 70 to 80 mole percent of the acid component of the copolyester is supplied by terephthalic acid or a polyester-forming derivative thereof, 20 to 30 mole percent of the acid component of the copolyester is supplied by one or more other aromatic and/or one or more alipthatic saturated co-acids having 2 to 12 carbon atoms between the two carboxyl groups and the diol component is supplied at least in part by ethylene glycol.
Claim 15
Dependent Claim
24 words
A blowing agent concentrate according to claim 13 wherein up to 100% of the diol component of the copolyester is supplied by ethylene glycol.
Claim 16
Dependent Claim
31 words
A blowing agent concentrate according to claim 14 wherein up to 10 mole percent of the ethylene glycol is replaced by one or more diols having 3 to 12 carbon atoms.
Claim 17
Dependent Claim
31 words
A blowing agent concentrate according to claim 3 wherein the polyesters are derived in respect to the diol component from hexanediol-1,6 and, with respect to the acid component from terephthalic acid.
Claim 18
Dependent Claim
32 words
A blowing agent concentrate according to claim 3 wherein the blowing agent is present in an amount of 5 to 50 weight percent based upon the weight of the blowing agent concentrate.
Claim 19
Dependent Claim
44 words
A blowing agent concentrate according to claim 3 wherein the copolyester is derived in respect of the acid components from 85% terephthalic acid and from 15% isophthalic acid and in respect of the diols from 50 Mol-% butanediol 1,4 and 50 Mol-% hexanediol 1,6.
Claim 20
Dependent Claim
28 words
A blowing agent concentrate according to claim 17 wherein the blowing agent is present in the blowing agent concentrate in an amount of 5 to 30 weight percent.
Claim 21
Dependent Claim
29 words
A blowing agent concentrate according to claim 19 wherein the blowing agent is present in the blowing agent concentrate in an amount of between 5 and 20 weight percent.
Claim 22
Dependent Claim
16 words
A blowing agent concentrate according to claim 17 wherein the blowing agent is 5-phenyl-tetrazol or 5-phthalimidotetrazol.
Claim 23
Dependent Claim
21 words
A blowing agent concentrate to claim 17 wherein the blowing agent has a decomposition temperature ranging from 120° to 260° C.
Claim 24
Dependent Claim
24 words
A blowing agent concentrate according to claim 22 wherein the blowing agent has a decomposition temperature in the range of 200° to 260° C.
Claim 25
Dependent Claim
118 words
In a process for forming a foamed article from polyalkyleneterephthalate polymer when said polymer is mixed with a blowing agent and thereafter introduced into a mold maintained under conditions to activate the blowing agent and form said polymer into a shape, the improvement which comprises introducing said blowing agent into said polymer in the form of a concentrate containing a thermoplastic composition as a vehicle for said blowing agent, said concentrate consisting essentially of a chemical blowing agent present in an amount of at least 5 weight percent, said thermoplastic vehicle being a saturated polyester or copolyester having a crystalline melting point between 100° C. and 220° C. and a reduced viscosity between 0.4 dl/g and 1.6 dl/g.
Claim 26
Dependent Claim
118 words
In a process for forming a foamed article from polyalkyleneterephthalate polymer when said polymer is mixed with a blowing agent and thereafter introduced into a mold maintained under conditions to activate the blowing agent and form said polymer into a shape, the improvement which comprises introducing said blowing agent into said polymer in the form of a concentrate containing a thermoplastic composition as a vehicle for said blowing agent, said concentrate consisting essentially of a chemical blowing agent present in an amount of at least 5 weight percent, said thermoplastic vehicle being a saturated polyester or copolyester having a crystalline melting point between 100° C. and 220° C. and a reduced viscosity between 0.4 dl/g and 1.6 dl/g.
Claim 27
Dependent Claim
24 words
A process according to claim 24 wherein the blowing agent is present in the concentrate in an amount of 5 to 50 weight percent.
Claim 28
Dependent Claim
24 words
A process according to claim 25 wherein the blowing agent is present in the concentrate in an amount of 20 to 30 weight percent.
Claim 29
Dependent Claim
44 words
A process according to claim 25 wherein an amount of blowing agent concentrate is added to the polyalkyleneterephthalate such that the amount of blowing agent present in the complete mixture of blowing agent concentrate and polyalkyleneterephthalate is from 0.05 to about 10.0 weight percent.
Claim 30
Dependent Claim
17 words
A process according to claim 27 wherein the polyalkyleneterephthalate has a reduced viscosity of 0.7 to 2.3.
Claim 31
Dependent Claim
13 words
A process according to claim 25 wherein the polyalkyleneterephthalate is a polytetramethylene terephthalate.
Claim 32
Dependent Claim
26 words
A process according to claim 25 wherein the polyalkyleneterephthalate to which the blowing agent concentrate is added contains a filler, reinforcing element and/or flame proofing agent.
Claim 33
Dependent Claim
20 words
A process according to claim 30 wherein the polyalkyleneterephthalate to which the blowing agent concentrate is added contains glass fibers.
Claim 34
Dependent Claim
32 words
A blowing agent concentrate according to claim 1 wherein the blowing agent is present in an amount of 10 to 50 weight percent based upon the weight of the blowing agent concentrate.
Claim 35
Dependent Claim
24 words
A blowing agent concentrate according to claim 1 wherein said saturated polyester or copolyester has a glass transition temperature between -20° and +50° C.
Claim 36
Dependent Claim
62 words
A process according to claim 24 wherein said blowing agent is present in said blowing agent concentrate in an amount of 10 to 50 weight percent and the blowing agent concentrate is added to the polyalkyleneterephthalate such that the amount of blowing agent present in the completed mixture of blowing agent concentrate and polyalkyleneterephthalate is from 0.05 to about 10 weight percent.
Claim 37
Dependent Claim
61 words
A process according to claim 24 wherein said blowing agent is present in said blowing agent concentrate in an amount of 10 to 50 weight percent and the blowing agent concentrate is added to the polyalkyleneterephthalate such that the amount of blowing agent present in the completed mixture of blowing agent concentrate and polyalkyleneterephthalate is from 0.1 to 5.0 weight percent.
Claim 38
Dependent Claim
22 words
A process according to claim 35 wherein the glass transition temperature of the saturated polyester and/or copolyester is -20° to +50° C.
Claim 39
Dependent Claim
28 words
A blowing agent concentrate according to claim 17, wherein the concentrate is a granulate, having the blowing agent homogeneously imbedded in each granule particle of the thermoplastic vehicle.
References Cited (Backward Citations)
US2945828A
Cited
US3198859A
Cited
US3511788A
Cited
US3634564A
Cited
US3725321A
Cited
US3962154A
Cited
US3936400A
Cited
US3876566A
Cited
US3965053A
Cited
US4097421A
Cited
US4002581A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-13 | 1985-01-12 | 1985-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-13 | 1989-01-12 | 1989-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-13 | 1993-01-12 | 1993-07-14 | $7700.00 | Window Closed / Lapsed |