Abstract
Abstract This invention relates to foamable, thermoplastic polyester molding compositions, to molded products suitable for structural applications and to a process for their manufacture. The resin compositions when foamed have a cellular interior and a skin having structural strength.
Inventors
- 👤 Tai Ming Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:28
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/34; C08J9/0014; C08J9/0023; C08J9/0085; C08K; C08K5/00; C08K5/04; C08K5/09; C08K7/00; C08K7/02; C08K7/04; C08K7/10; C08K7/12; C08K7/14; C08J2367/00; C08J2367/02; Y; Y10; Y10S; Y10S264/00; Y10S264/83
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
183 words
Foamable thermoplastic polyester moldable compositions having reduced melt viscosity compared with the original polyester resin comprising (a) thermoplastic polyester resin homopolyesters selected from the group consisting of poly(ethylene terephthalate) and poly(tetramethylene terephthalate), copolyesters and physical blends of homopolyesters and copolyesters of ethylene terephthalate and of tetramethylene terephthalate having crystalline melting points above about 300° F., (b) 0.05 to 15 parts by weight based on the weight of polyester resin of a melt viscosity reducing agent selected from the group consisting of esters of organic acids containing from 10 to 27 carbon atoms and alkali or alkaline earth metal salts of an organic acid having from 10 to 25 carbon atoms, (c) 0.05 to 15 parts by weight based on the weight of the polyester resin of a hydrocarbyltetrazole which can be decomposed to release a gas harmless to the polyester, and (d) 2 to 45 parts by weight of a reinforcing agent selected from the group consisting of glass fibers, potassium titanate fibers, aramid fibers, asbestos fibers and graphite fibers based on the combined weight of the polyester resin and the reinforcing agent.
Claim 2
Dependent Claim
183 words
Foamable thermoplastic polyester moldable compositions having reduced melt viscosity compared with the original polyester resin comprising (a) thermoplastic polyester resin homopolyesters selected from the group consisting of poly(ethylene terephthalate) and poly(tetramethylene terephthalate), copolyesters and physical blends of homopolyesters and copolyesters of ethylene terephthalate and of tetramethylene terephthalate having crystalline melting points above about 300° F., (b) 0.05 to 15 parts by weight based on the weight of polyester resin of a melt viscosity reducing agent selected from the group consisting of esters of organic acids containing from 10 to 27 carbon atoms and alkali or alkaline earth metal salts of an organic acid having from 10 to 25 carbon atoms, (c) 0.05 to 15 parts by weight based on the weight of the polyester resin of a hydrocarbyltetrazole which can be decomposed to release a gas harmless to the polyester, and (d) 2 to 45 parts by weight of a reinforcing agent selected from the group consisting of glass fibers, potassium titanate fibers, aramid fibers, asbestos fibers and graphite fibers based on the combined weight of the polyester resin and the reinforcing agent.
Claim 3
Dependent Claim
29 words
A composition as described in claim 1 wherein the metal salt is selected from the group consisting of lithium stearate, sodium stearate, potassium stearate, calcium stearate and zine stearate.
Claim 4
Dependent Claim
26 words
A composition as described in claim 1 wherein the foaming agent is a 5-hydrocarbyltetrazole selected from the group consisting of p-phenylene-bis(5-tetrazole), 5-methyltetrazole, 5-phenyltetrazole, 5-(benzyl)-tetrazole and 5-(p-toluyl)-tetrazole.
Claim 5
Independent Claim
228 words
A method of preparing foamable polyester compositions containing a tetrazole foaming agent said polyester being selected from the group consisting of polyethylene terephthalate and polytetramethylene terephthalate, copolyester resins and physical blends of homopolyester and copolyester resins of ethylene terephthalate and of tetramethylene terephthalate having crystalline melting points above about 300° F. comprising lowering the processing temperature of said polyester resin by (a) combining the thermoplastic polyester resin with (1) 0.05 to 15 parts by weight based on the weight of the polyester of a lubricating agent selected from the group consisting of esters of organic acids having from 10 to 27 carbon atoms and alkali or alkaline earth metal salts of an organic acid having from 10 to 25 carbon atoms and then mixing the combination with (2) 0.05 to 15 parts by weight based on the weight of the polyester of a foaming agent comprising 5-hydrocarbyltetrazoles selected from the group consisting of p-phenylene-bis(5-tetrazole), 5-methyltetrazole, 5-phenyltetrazole, 5-(benzyl)-tetrazole and 5-(p-toluyl)-tetrazole, and (3) 2 to 45 parts by weight of a reinforcing agent selected from the group consisting of glass fibers, potassium titanate fibers, aramid fibers, asbestos fibers and graphite fibers based on the combined weight of the polyester resin and reinforcing agent, (b) said combination taking place at a temperature about equal to or lower than the temperature at which appreciable decomposition of the 5-hydrocarbyltetrazole foaming agent takes place.
Claim 6
Independent Claim
228 words
A method of preparing foamable polyester compositions containing a tetrazole foaming agent said polyester being selected from the group consisting of polyethylene terephthalate and polytetramethylene terephthalate, copolyester resins and physical blends of homopolyester and copolyester resins of ethylene terephthalate and of tetramethylene terephthalate having crystalline melting points above about 300° F. comprising lowering the processing temperature of said polyester resin by (a) combining the thermoplastic polyester resin with (1) 0.05 to 15 parts by weight based on the weight of the polyester of a lubricating agent selected from the group consisting of esters of organic acids having from 10 to 27 carbon atoms and alkali or alkaline earth metal salts of an organic acid having from 10 to 25 carbon atoms and then mixing the combination with (2) 0.05 to 15 parts by weight based on the weight of the polyester of a foaming agent comprising 5-hydrocarbyltetrazoles selected from the group consisting of p-phenylene-bis(5-tetrazole), 5-methyltetrazole, 5-phenyltetrazole, 5-(benzyl)-tetrazole and 5-(p-toluyl)-tetrazole, and (3) 2 to 45 parts by weight of a reinforcing agent selected from the group consisting of glass fibers, potassium titanate fibers, aramid fibers, asbestos fibers and graphite fibers based on the combined weight of the polyester resin and reinforcing agent, (b) said combination taking place at a temperature about equal to or lower than the temperature at which appreciable decomposition of the 5-hydrocarbyltetrazole foaming agent takes place.
Claim 7
Dependent Claim
15 words
A method as described in claim 4 wherein the thermoplastic polyester resin is poly(tetramethylene terephthalate).
Claim 8
Dependent Claim
13 words
A method as described in claim 5 wherein the foaming agent is 5-phenyltetrazole.
Claim 9
Dependent Claim
33 words
A method as described in claim 6 wherein the metallic salt is a metallic stearate salt selected from the group consisting of lithium stearate, sodium stearate, potassium stearate, zinc stearate and calcium stearate.
Claim 10
Dependent Claim
14 words
A method as described in claim 7 wherein the reinforcing material is glass fibers.
Claim 11
Dependent Claim
29 words
A method as described in claim 8 wherein the glass fiber is in a concentration of 30 percent by weight of the thermoplastic polyester resin and glass fiber combined.
Claim 12
Independent Claim
199 words
A method of preparing foamed polyester compositions said polyester being selected from the group consisting of thermoplastic homopolyester resins polyethylene terephthalate and polytetramethylene terephthalate, copolyester resins and physical blends of homopolyester and copolyester resins of ethylene terephthalate and of tetramethylene terephthalate having crystalline melting points above about 300° F. comprising lowering the processing temperature of said polyester resin by (a) combining the thermoplastic polyester resin with (1) 0.05 to 15 parts by weight based on the weight of the polyester of a lubricating agent selected from the group consisting of esters of organic acids having from 10 to 27 carbon atoms and alkali or alkaline earth metal salts of an organic acid having from 10 to 25 carbon atoms and then mixing the combination with (2) 0.05 to 15 parts by weight based on the weight of the polyester of a foaming agent comprising 5-hydrocarbyltetrazoles selected from the group consisting of p-phenylene-bis(5-tetrazole), 5-methyltetrazole, 5-phenyltetrazole, 5-(benzyl)-tetrazole and 5-(p-toluyl)-tetrazole and (3) 2 to 45 parts by weight of a reinforcing agent selected from the group consisting of glass fibers, potassium titanate fibers, aramid fibers, asbestos fibers and graphite fibers based on the combined weight of the polyester resin and reinforcing agent,
Claim 13
Independent Claim
199 words
A method of preparing foamed polyester compositions said polyester being selected from the group consisting of thermoplastic homopolyester resins polyethylene terephthalate and polytetramethylene terephthalate, copolyester resins and physical blends of homopolyester and copolyester resins of ethylene terephthalate and of tetramethylene terephthalate having crystalline melting points above about 300° F. comprising lowering the processing temperature of said polyester resin by (a) combining the thermoplastic polyester resin with (1) 0.05 to 15 parts by weight based on the weight of the polyester of a lubricating agent selected from the group consisting of esters of organic acids having from 10 to 27 carbon atoms and alkali or alkaline earth metal salts of an organic acid having from 10 to 25 carbon atoms and then mixing the combination with (2) 0.05 to 15 parts by weight based on the weight of the polyester of a foaming agent comprising 5-hydrocarbyltetrazoles selected from the group consisting of p-phenylene-bis(5-tetrazole), 5-methyltetrazole, 5-phenyltetrazole, 5-(benzyl)-tetrazole and 5-(p-toluyl)-tetrazole and (3) 2 to 45 parts by weight of a reinforcing agent selected from the group consisting of glass fibers, potassium titanate fibers, aramid fibers, asbestos fibers and graphite fibers based on the combined weight of the polyester resin and reinforcing agent,
Claim 14
Dependent Claim
31 words
A method as described in claim 10 wherein the foamed thermoplastic polyester resin has a density of from about 0.7 grams per cubic centimeter to about 1.52 grams per cubic centimeter.
Claim 15
Dependent Claim
34 words
A composition as described in claim 10 wherein the foamed polyester composition has a tensile strength as measured by ASTM-D 638 of from 5000 pounds per square inch to 18,000 pounds per square inch.
Claim 16
Dependent Claim
40 words
A composition as described in claim 10 wherein the foamed polyester composition has a flexural modulus as determined by ASTM D-790 of from 5.8 × 10 5 pounds per square inch to 12.0 × 10 5 pounds per square inch.
Claim 17
Dependent Claim
34 words
A composition as described in claim 10 wherein the foamed polyester composition has a flexural strength as determined by ASTM D-790 of from 12,000 pounds per square inch to 27,000 pounds per square inch.
Claim 18
Dependent Claim
36 words
A composition as described in claim 10 wherein the foamed polyester composition has a heat deflection temperature as measured by ASTM D-648 at 264 pounds per square inch of from about 355° to about 405° F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |