Sequentially annealed oxidation of silicon to fill trenches with silicon dioxide
Assignee: AT&T Inc
•
Filing: 1979-11-08
•
Granted: 1981-07-14
•
Expires: 1999-11-08
Abstract
Abstract A process for making dielectrically isolated silicon integrated circuits which use silicon oxide filled trenches to provide isolation is described. To minimize damage to the silicon, the trenches are filled by sequentially annealed oxidation process which involves alternately growing some oxide and then annealing to relieve stresses before growing more oxide.
Inventors
- 👤 Jorge Agraz-Guerena
- 👤 Lewis E. Katz
- 👤 Bernard L. Morris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:36
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90; H10P95/906; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0121; H10W10/0124; H10W10/10; H10W10/13
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
121 words
In the fabrication of silicon integrated circuits made in silicon chips which utilize trenches filled with silicon oxide to provide dielectric isolation between different surface portions of the chip, the process of filling the trenches in the silicon chip with silicon oxide which comprises heating the silicon chip, which has been masked to leave exposed the trenches while covering the surface between the trenches, in a relatively strong oxidizing ambient to fill partially the trenches with silicon oxide, annealing the chip in an ambient in which any oxide growth is insignificant for a time to relieve stresses in the chip, and repeating the heating and annealing steps until the trenches are substantially filled and planarity is essentially restored to the chip.
Claim 2
Dependent Claim
121 words
In the fabrication of silicon integrated circuits made in silicon chips which utilize trenches filled with silicon oxide to provide dielectric isolation between different surface portions of the chip, the process of filling the trenches in the silicon chip with silicon oxide which comprises heating the silicon chip, which has been masked to leave exposed the trenches while covering the surface between the trenches, in a relatively strong oxidizing ambient to fill partially the trenches with silicon oxide, annealing the chip in an ambient in which any oxide growth is insignificant for a time to relieve stresses in the chip, and repeating the heating and annealing steps until the trenches are substantially filled and planarity is essentially restored to the chip.
Claim 3
Dependent Claim
28 words
The process of claim 1 in which the first filling step is done at relatively high temperature and the subsequent filling steps are done at a lower temperature.
Claim 4
Dependent Claim
30 words
The process of claim 1 in which the first filling step is done in steam at atmospheric pressure and the subsequent filling steps are done in steam at higher pressures.
Claim 5
Dependent Claim
32 words
The process of claim 1 in which the first filling layer grown is thicker than the second layer grown but each successive layer grown thereafter is thicker than the immediately preceding layer.
Claim 6
Dependent Claim
30 words
The process of claim 2 in which the first filling step is done in steam at atmospheric pressure and the subsequent filling steps are done in steam at higher pressures.
References Cited (Backward Citations)
US3969162A
Cited
US3913211A
Cited
US3958040A
Cited
US4001465A
Cited
US4042726A
Cited
US4079506A
Cited
US4139658A
Cited
US4167915A
Cited
US4140548A
Cited
US4199384A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-13 | 1985-01-12 | 1985-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-13 | 1989-01-12 | 1989-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-13 | 1993-01-12 | 1993-07-14 | $7700.00 | Window Closed / Lapsed |