Process for forming phosphor screens with treated phosphors
Assignee: Mitsubishi Chemical Corp
•
Filing: 1979-10-19
•
Granted: 1981-06-30
•
Expires: 1999-10-19
Abstract
Abstract A process for forming a phosphor screen of a color picture tube comprising forming a thin layer using a photosensitive composition which contains an aromatic diazonium salt as a photosensitive component and produces tackiness by exposure to actinic light on the surface of the substrate and contacting the tackified thin layer after exposure to light with phosphor particles to form each phosphor layer for emitting color is improved by using as the phosphor particles those coated with at least one surface coating material selected from the group consisting of Zn(OH) 2 , Zn 3 (PO 4 ) 2 and AlPO 4 in shortening the contact time between the thin layer and the phosphor particles.
Inventors
- 👤 Toshikatsu Manabe
- 👤 Saburo Nonogaki
- 👤 Hajime Morishita
- 👤 Shoichi Uchino
- 👤 Yoshifumi Tomita
- 👤 Masahiro Nishizawa
- 👤 Hiroshi Yokomizo
- 👤 Susumu Ohmatoi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:56
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/20; H01J9/22; H01J9/227; H01J9/2271; C; C09; C09K; C09K11/00; C09K11/02; C09K11/025
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
176 words
In a process for forming a phosphor screen of a color picture tube by a dry phosphor deposition method comprising coating a photosensitive composition, which contains an aromatic diazonium salt or a mixture of an aromatic diazonium salt as a photosensitive component and produces tackiness by exposure to actinic light, on the inner surface of the face plate of a color picture tube to form a thin layer, exposing the thin layer imagewisely to actinic light for producing tackiness on the portions exposed, contacting the exposed thin layer with phosphor particles, and making the thin layer receive the phosphor particles depending on receptive ability of the thin layer to form each phosphor layer for emitting color, the improvement which comprises using as the phosphor particles those coated with at least one surface coating material selected from the group consisting of Zn(OH) 2 , Zn 3 (PO 4 ) 2 and AlPO 4 , whereby the amount of time necessary for the phosphor to contact the thin layer to provide said each phosphor layer thereon is shortened.
Claim 2
Dependent Claim
176 words
In a process for forming a phosphor screen of a color picture tube by a dry phosphor deposition method comprising coating a photosensitive composition, which contains an aromatic diazonium salt or a mixture of an aromatic diazonium salt as a photosensitive component and produces tackiness by exposure to actinic light, on the inner surface of the face plate of a color picture tube to form a thin layer, exposing the thin layer imagewisely to actinic light for producing tackiness on the portions exposed, contacting the exposed thin layer with phosphor particles, and making the thin layer receive the phosphor particles depending on receptive ability of the thin layer to form each phosphor layer for emitting color, the improvement which comprises using as the phosphor particles those coated with at least one surface coating material selected from the group consisting of Zn(OH) 2 , Zn 3 (PO 4 ) 2 and AlPO 4 , whereby the amount of time necessary for the phosphor to contact the thin layer to provide said each phosphor layer thereon is shortened.
Claim 3
Dependent Claim
29 words
A process according to claim 1, wherein the surface coating material is Zn(OH) 2 and phosphor particles are undercoated with SiO 2 followed by coating with Zn(OH) 2 .
Claim 4
Dependent Claim
37 words
A process according to claim 1, wherein the surface coating material is Zn 3 (PO 4 ) 2 and phosphor particles are undercoated with SiO 2 followed by coating with Zn 3 (PO 4 ) 2 .
Claim 5
Dependent Claim
35 words
A process according to claim 1, 2 or 3, wherein the surface coating material is coated on the phosphor in an amount of 0.01 to 2% by weight based on the weight of the phosphor.
Claim 6
Dependent Claim
36 words
A process according to claim 1 or 2, wherein the surface coating material is Zn(OH) 2 , which is used in an amount of 0.01 to 0.7% by weight based on the weight of the phosphor.
Claim 7
Dependent Claim
40 words
A process according to claim 1 or 3, wherein the surface coating material is Zn 3 (PO 4 ) 2 , which is used in an amount of 0.05 to 1.5% by weight based on the weight of the phosphor.
Claim 8
Dependent Claim
34 words
A process according to claim 1, wherein the surface coating material is AlPO 4 , which is used in an amount of 0.05 to 1% by weight based on the weight of the phosphor.
Claim 9
Dependent Claim
29 words
A process according to claim 2 or 3, wherein the amount of SiO 2 for undercoating is 0.05 to 1% by weight based on the weight of the phosphor.
Claim 10
Dependent Claim
22 words
A process according to claim 1, wherein the phosphor is a blue-emitting phosphor and the surface coating material is Zn(OH) 2 .
Claim 11
Dependent Claim
26 words
A process according to claim 9, wherein the amount of Zn(OH) 2 is 0.01 to 0.7% by weight based on the weight of the blue-emitting phosphor.
Claim 12
Dependent Claim
26 words
A process according to claim 1, wherein the phosphor is a red-emitting phosphor undercoated with SiO 2 and the surface coating material is Zn(OH) 2 .
Claim 13
Dependent Claim
43 words
A process according to claim 11, wherein the amount of SiO 2 is 0.05 to 1% by weight based on the red-emitting phosphor and the amount of Zn(OH) 2 is 0.01 to 0.7% by weight based on the weight of the red-emitting phosphor.
Claim 14
Dependent Claim
29 words
A process according to claim 1, wherein the phosphor is a green-emitting phosphor and the surface coating material is Zn(OH) 2 or Zn 3 (PO 4 ) 2 .
Claim 15
Dependent Claim
26 words
A process according to claim 13, wherein the amount of Zn(OH) 2 is 0.01 to 0.7% by weight based on the weight of the green-emitting phosphor.
Claim 16
Dependent Claim
30 words
A process according to claim 13, wherein the amount of Zn 3 (PO 4 ) 2 is 0.05 to 1.5% by weight based on the weight of the green-emitting phosphor.
Claim 17
Dependent Claim
239 words
A process according to claim 1, wherein the process comprises the steps of coating a photosensitive composition, which contains an aromatic diazonium salt or mixture of an aromatic diazonium salt as a photosensitive component and produces tackiness by exposure to actinic light, on the inner surface of the face plate to form a thin layer, (1) exposing the thin layer imagewisely to actinic light to produce tackiness over the portions exposed, contacting the resulting thin layer with blue-emitting phosphor particles coated with Zn(OH) 2 , making the exposed portions receive the surface treated blue-emitting phosphor particles, and removing superfluous blue-emitting phosphor particles from the thin layer, (2) exposing secondly the non-exposed portions of the thin layer imagewisely to actinic light to produce tackiness over the portions exposed, contacting the resulting thin layer with green-emitting phosphor particles coated with Zn(OH) 2 or Zn 3 (PO 4 ) 2 or a mixture of the two, making the secondly exposed portions receive the surface treated green-emitting phosphor particles, and removing superfluous green-emitting phosphor particles from the thin layer, and (3) exposing thirdly the non-exposed portions of the thin layer imagewisely to actinic light to produce tackiness over the portions exposed, contacting the resulting thin layer with red-emitting phosphor particles undercoated with SiO 2 followed by coating with Zn(OH) 2 , making the thirdly exposed portions receive the surface treated red-emitting phosphor particles, and removing superfluous red-emitting phosphor particles from the thin layer.
Claim 18
Dependent Claim
42 words
A process according to claim 1, wherein the coated phosphor particles are dried prior to the exposed thin layer being contacted with the coated phosphor particles, whereby the exposed thin layer is contacted with phosphor particles which are in a dried state.
Claim 19
Dependent Claim
28 words
A process according to claim 16, wherein the photosensitive composition includes at least one material selected from the group consisting of organic polymeric materials and surface active agents.
Claim 20
Dependent Claim
49 words
A process according to claim 18, wherein the organic polymeric material is selected from the group consisting of gum arabic, polyvinyl alcohol, polyacrylamide, poly(N-vinylpyrrolidone) hydroxypropylmethylcellulose, alginic acid, propylene glycol ester of alginic acid, a copolymer of acrylamide and diacetone-acrylamide, and a copolymer of methyl vinyl ether and maleic anhydride.
Claim 21
Dependent Claim
31 words
A process according to claim 18, wherein the organic polymeric material is used in an amount of 0.05 to 500% by weight based on the weight of the aromatic diazonium salt.
Claim 22
Dependent Claim
25 words
A process according to claim 1, wherein the phosphor particles which are coated with said at least one surface coated material are pigment-coated phosphor particles.
Claim 23
Dependent Claim
22 words
A process according to claim 1, wherein said phosphor particles comprise a mixture of phosphor particles coated with different surface coating materials.
References Cited (Backward Citations)
US2929708A
Cited
GB1103864A
Cited
US3707396A
Cited
US3607371A
Cited
US3676177A
Cited
US4128674A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-29 | 1984-12-29 | 1985-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-29 | 1988-12-29 | 1989-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-29 | 1992-12-29 | 1993-06-30 | $7700.00 | Window Closed / Lapsed |