Metalized polyester resin laminate

Claim 2

A process for the manufacture of laminated thin sheets having improved weathering properties which comprises bonding a metalized transparent polyester resin film to a polyvinyl chloride film sheet by an in-situ formed thermosetting polyurethane adhesive layer, wherein the metalized surface of said polyester film is primed with an applied coating comprising an acid modified vinyl chloride vinyl acetate copolymer.

Claim 3

The process as defined in claim 1 wherein said primer coating is applied as a solution in organic solvent.

Claim 4

The process as defined in claim 1 wherein said applied primer coating comprises as a cross-linking agent a liquid epoxy polymer having an epoxide equivalent of 185-192.

Claim 5

The process as defined in claim 3 wherein said primer coating further comprises at least one catalyst from the group consisting of tertiary amines and tin catalysts.

Claim 6

The process as defined in claim 3 wherein said primer coating further comprises catalytic amounts of tertiary amine and stannous octoate.

Claim 7

The process as defined in claim 1 wherein said polyurethane adhesive layer is formed by reaction in-situ of a polyester polyol with triisocyanate.

Claim 8

The process as defined in claim 6 wherein said in-situ reaction is carried out in the presence of a tertiary amine catalyst.

Claim 9

The process as defined in claim 1 wherein said polyurethane adhesive layer is formed in-situ by reaction of at least one polyester polyol with a mixture of a slow acting and a fast acting polyisocyanate.

Claim 10

The process as defined in claim 1 wherein said polyurethane adhesive layer is formed by reaction of a polyester polyol with a mixture of an aromatic triisocyanate and an aliphatic triisocyanate.

Claim 11

The process as defined in claim 9 wherein said in-situ reaction is effected in the presence of a tertiary amine catalyst and said mixture of triisocyanates comprises 5 to 30 parts of aliphatic triisocyanates to respectively 95 to 70 parts of aromatic triisocyanate.

Claim 12

The process as defined in claim 10 wherein said aromatic triisocyanate is one formed from reaction of tolylene diisocyanate with trimethylol propane.

Claim 13

The process as defined in claim 10 wherein said aliphatic triisocyanate is one formed by reaction of hexamethylene diisocyanate with water.

Claim 14

The process as defined in claim 1 wherein said polyurethane adhesive layer is formed by reaction of a polyester polyol with a mixture of polyisocyanates, comprising (1) an aromatic polyisocyanate formed from reaction of tolylene driisocyanate with trimethylolpropane and (2) aliphatic triisocyanate formed by reaction of hexamethylene diisocyanate with water.

Claim 15

The process as defined in claim 1 wherein said polyurethane adhesive layer is formed by reaction with organic isocyanate in organic solution, a polyester polyol compound formed by reaction of at least one polyhydric alcohol with a dicarboxy acid from the group consisting of isophthalic and terephthalic acids, said urethane-forming reaction being carried out in the presence of a catalytic amount of dimethylethanolamine.

Claim 16

The process as defined in claim 14 wherein said polyhydric alcohol is a glycol selected from the group consisting of butanediol, neopentyl glycol and mixtures of these.

Claim 17

The process as defined in claim 14 wherein the weight ratio of polyester polyol compound to isocyanates is in the range of 20:1 to about 2:1.

Claim 18

The process as defined in claim 1 wherein said polyurethane adhesive layer is one formed by reaction of polyisocyanate with a solution of a polyester polyol having an acid/OH ratio of not greater than 1.0 and a hydroxy number above 3.

Claim 19

The process as defined in claim 17 wherein said polyester polyol is one having an acid number below 2.0.

Claim 20

The process as defined in claim 17 wherein said polyester polyol is one having an acid/OH ratio of not greater than 0.2.

Claim 21

The process of forming laminated thin sheets having improved weathering properties which comprises (1) applying to a vinyl copolymer primed metal surface of an aluminized polyester film, an adhesive layer of a thermosetting adhesive formed in-situ by reaction of polyisocyanates in organic solution with a polyester polyol, said polyester polyol being one formed by reaction of at least one glycol from the group consisting of butane diol and neopentyl glycol, with at least one dicarboxylic acid from the group consisting of isophthalic and terephthalic acids; and (2) bonding the adhesive containing film to a polyvinyl chloride backing film at said adhesive layer.

Claim 22

The process of forming laminated thin sheets having improved weathering properties which comprises (1) applying to a vinyl copolymer primed metal surface of an aluminized polyester film, an adhesive layer of a thermosetting adhesive formed in-situ by reaction of polyisocyanates in organic solution with a polyester polyol, said polyester polyol being one formed by reaction of at least one glycol from the group consisting of butane diol and neopentyl glycol, with at least one dicarboxylic acid from the group consisting of isophthalic and terephthalic acids; and (2) bonding the adhesive containing film to a polyvinyl chloride backing film at said adhesive layer.

Claim 23

The process as defined in claim 20 wherein said polyester polyol solution has a viscosity of about 17± seconds in a #3 Zahn cup.

Claim 24

The process as defined in claim 20 wherein said polyester polyol is one having an acid/OH ratio not greater than 1.0, and a hydroxy number above 3.

Claim 25

The process as defined in claim 20 wherein there is further applied to the opposite face of said polyester film a transparent protective lacquer coating comprising an organic solvent solution of a polyester resin containing an ultraviolet inhibitor.

Claim 26

The process as defined in claim 23 wherein said ultraviolet inhibitor is one corresponding to the general formula ##STR2## wherein x is OH or OCH 3 , y is H or OH, and z is H, OH, or OCH 3 .

Claim 27

The process as defined in claim 23 wherein said ultraviolet inhibitor is 2,2', 4,4'-tetrahydroxy benzophenone.

Claim 28

The process as defined in claim 20 wherein the reverse face of said polyvinyl chloride backing film is further treated by application thereto of a dry heat seal adhesive having a dried thickness of 1 to 3 microns.

Claim 31

Polyethylene terephthalate film having at one face thereof a vacuum-applied coating of aluminum metal and the opposite face coated with a polyester resin lacquer composition containing as an ultraviolet inhibitor 2,2', 4,4' tetrahydroxy benzophenone.

Claim 32

Polyethylene terephthalate film having at one face thereof a vacuum-applied coating of aluminum metal and the opposite face coated with a polyester resin lacquer composition containing as an ultraviolet inhibitor 2,2', 4,4' tetrahydroxy benzophenone.

Claim 35

A thin flexible laminated structure comprising a film of aluminized transparent polyethylene terephthalate bonded at the metalized surface thereof to a vinyl film sheet by an intervening layer of a cured thermoset polyester-polyisocyanate adhesive composition, the opposite exposed surface of said aluminized film being coated with a weather resistant protective lacquer comprising a polyester resin, containing ultraviolet inhibitor; said polyester-polyisocyanate adhesive composition comprising the reaction product of at least one triisocyanate reacted with a condensation copolymer formed from at least one glycol compound from the group consisting of butanediol and neopentyl glycol and at least one dicarboxylic acid from the group consisting of isophthalic and terephthalic acids.

Claim 36

A thin flexible laminated structure comprising a film of aluminized transparent polyethylene terephthalate bonded at the metalized surface thereof to a vinyl film sheet by an intervening layer of a cured thermoset polyester-polyisocyanate adhesive composition, the opposite exposed surface of said aluminized film being coated with a weather resistant protective lacquer comprising a polyester resin, containing ultraviolet inhibitor; said polyester-polyisocyanate adhesive composition comprising the reaction product of at least one triisocyanate reacted with a condensation copolymer formed from at least one glycol compound from the group consisting of butanediol and neopentyl glycol and at least one dicarboxylic acid from the group consisting of isophthalic and terephthalic acids.

Claim 37

The structure defined in claim 30 wherein said adhesive composition is the reaction product of said condensation copolymer with at least one slow reacting triisocyanate and at least one more rapidly reacting triisocyanate.

Claim 38

The structure defined in claim 30 wherein the metalized surface of said polyester film is treated with a thin layer of a priming composition comprising an acid-modified vinyl chloride-vinyl acetate copolymer.

Claim 39

The structure as defined in claim 32 wherein said copolymer of said priming composition is cross linked by epoxy resin.

Claim 40

An auto trim molding comprising an extruded vinyl strip having bonded on at least part of its surface an ornamental metal-simulating laminate as defined in claim 33.

Claim 41

An auto trim molding comprising an extruded vinyl strip having bonded on at least part of its surface an ornamental metal-simulating laminate as defined in claim 30.

Claim 42

A thin flexible laminated structure comprising a film of aluminized transparent polyethylene terephthalate bonded at the metalized surface thereof to a vinyl film sheet by an intervening layer of a cured thermoset polyester-polyisocyanate adhesive composition, the opposite surface of said aluminized film having bonded thereto a protective film of polyvinyl fluoride; said polyester-polyisocyanate adhesive composition comprising the reaction product of at least one triisocyanate reacted with a condensation copolymer formed from at least one glycol compound from the group consisting of butanediol and neopentyl glycol and at least one dicarboxylic acid from the group consisting of isophthalic and terephthalic acids.

Claim 43

A thin flexible laminated structure comprising a film of aluminized transparent polyethylene terephthalate bonded at the metalized surface thereof to a vinyl film sheet by an intervening layer of a cured thermoset polyester-polyisocyanate adhesive composition, the opposite surface of said aluminized film having bonded thereto a protective film of polyvinyl fluoride; said polyester-polyisocyanate adhesive composition comprising the reaction product of at least one triisocyanate reacted with a condensation copolymer formed from at least one glycol compound from the group consisting of butanediol and neopentyl glycol and at least one dicarboxylic acid from the group consisting of isophthalic and terephthalic acids.