Dopant diffusion method of making semiconductor products
Assignee: Northrop Grumman Space and Mission Systems Corp
•
Filing: 1978-12-14
•
Granted: 1981-06-23
•
Expires: 1998-12-14
Abstract
Abstract Arsenic or other dopant selected from Group III or Group V of the Periodic Table of Elements is diffused into a silicon substrate to form a semiconductor product having a buried region, such as a buried layer or channel, by providing the substrate with a layer of polycrystalline silicon doped with the selected dopant and heating the substrate and layer in an oxygen environment at a temperature and for a period of time sufficient to oxidize all or substantially all the polycrystalline silicon and simultaneously diffuse the dopant into the substrate. The substrate comprises single crystal silicon or other silicon form whose oxidation rate is comparable to or less than the polycrystalline silicon to permit complete oxidation of the polycrystalline silicon without excessive oxidation of the substrate.
Inventors
- 👤 Alan S. Templin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:44
CPC Classifications
H; H10; H10W; H10W15/00; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P32/00; H10P32/10; H10P32/14; H10P32/1408; H10P32/1414; H10P32/17; H10P32/171; H10W15/01; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/92; Y10S438/981
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
134 words
The method of making a silicon semiconductor product having a patterned doped region, comprising the steps of: forming on an unmasked surface of a silicon substrate a patterned layer of polycrystalline silicon doped with a dopant selected from Group III or Group V of the Periodic Table of Elements and surrounded by and rising above a bare surface portion of said substrate; and heating said substrate and layer in an oxygen environment at a temperature and for a period of time sufficient to concurrently oxidize substantially all the polycrystalline silicon in said layer, diffuse said dopant into said substrate, and consume by oxidation said bare surrounding substrate surface portion, thereby forming a patterned upstanding mesa structure on said substrate and a correspondingly patterned buried doped region below and locationally marked by said mesa structure.
Claim 2
Independent Claim
134 words
The method of making a silicon semiconductor product having a patterned doped region, comprising the steps of: forming on an unmasked surface of a silicon substrate a patterned layer of polycrystalline silicon doped with a dopant selected from Group III or Group V of the Periodic Table of Elements and surrounded by and rising above a bare surface portion of said substrate; and heating said substrate and layer in an oxygen environment at a temperature and for a period of time sufficient to concurrently oxidize substantially all the polycrystalline silicon in said layer, diffuse said dopant into said substrate, and consume by oxidation said bare surrounding substrate surface portion, thereby forming a patterned upstanding mesa structure on said substrate and a correspondingly patterned buried doped region below and locationally marked by said mesa structure.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein said patterned polycrystalline silicon layer is formed by: depositing a layer of polycrystalline silicon on said unmasked substrate surface and then removing portions of said latter layer.
Claim 4
Dependent Claim
55 words
The method of claim 2 wherein: said substrate comprises a form of silicon having an oxidation rate approximating or substantially slower than the oxidation rate of said polycrystalline silicon when said substrate and layer are heated in said oxygen environment whereby said polycrystalline silicon can be substantially totally oxidized without excessive oxidation of said substrate.
Claim 5
Dependent Claim
57 words
The method of claim 2 wherein: said substrate is a single crystal silicon substrate whose oxidation rate is comparable to or substantially slower than the oxidation rate of said polycrystalline silicon when said substrate and layer are heated in said oxygen environment, whereby said polycrystalline silicon can be substantially totally oxidized without excessive oxidation of said substrate.
References Cited (Backward Citations)
US3156591A
Cited
US3502517A
Cited
US3767485A
Cited
US3798081A
Cited
US3928095A
Cited
US4063967A
Cited
US4063973A
Cited
US4151021A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-22 | 1984-12-22 | 1985-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-22 | 1988-12-22 | 1989-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-22 | 1992-12-22 | 1993-06-23 | $7700.00 | Window Closed / Lapsed |