Electrically conductive, infrared reflective, transparent coatings of stannic oxide
Assignee: Individual
•
Filing: 1979-04-09
•
Granted: 1981-05-05
•
Expires: 1999-04-09
Abstract
Abstract Electrically-conductive films of tin oxide are prepared by a novel process utilizing gaseous chemical compounds which react to form a tin-fluorine bond at a temperature which is (1) high enough so that the newly-created tin-fluorine bond-bearing molecule remains in the vapor phase; and (2) low enough so that oxidation of the molecule occurs only after the indicated re-arrangement. Films prepared by the process of the invention are characterized by surface resistances as low as 1 ohm per square when the film thickness is as thin as about a micron. These films are also characterized by extremely good reflectance of infrared radiation.
Inventors
- 👤 Roy G. Gordon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:21
CPC Classifications
H; H05; H05B; H05B3/00; H05B3/84; C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C03C17/2453; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/407; G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1343; G02F1/13439; H10; H10F; H10F71/00; H10F71/138; H05B2203/00; H05B2203/017; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
49 words
An article of manufacture comprising a generally transparent inorganic substrate such as glass and a fluorine-doped stannic oxide film thereon said object having an infrared reflectivity of at least about 85% as measured with 10 micron wavelength of incident radiation, said film having a maximum resistivity of 10 ohms.
Claim 2
Dependent Claim
49 words
An article of manufacture comprising a generally transparent inorganic substrate such as glass and a fluorine-doped stannic oxide film thereon said object having an infrared reflectivity of at least about 85% as measured with 10 micron wavelength of incident radiation, said film having a maximum resistivity of 10 ohms.
Claim 3
Dependent Claim
21 words
An article of manufacture as defined in claim 1 wherein said film comprises a fluorine to oxygen ratio of about 0.01.
Claim 4
Dependent Claim
18 words
An article of manufacture as defined in claim 1 wherein said film reflects 90% of said incident radiation.
Claim 5
Dependent Claim
25 words
An article of manufacture as defined in claim 3 wherein said film comprises a fluorine to oxygen ratio of from about 0.01 to about 0.02.
Claim 6
Dependent Claim
25 words
An article as defined in claims 1, 2, 3, or 4 wherein said film is from about 0.2 micron to about 1 micron in thickness.
Claim 7
Dependent Claim
30 words
An article as defined in claims 1, 2, 3, or 4 wherein said free electron concentration is from about 10 20 cm -3 to about 10 21 cm -3 .
Claim 8
Dependent Claim
26 words
An article as defined in claims 1, 2, 3, or 4 wherein said film comprise an electron drift mobility value of about 40 cm 2 /Volt-second.
Claim 9
Dependent Claim
33 words
An article of manufacture comprisng a generally transparent substrate such as glass and a fluorine-doped stannic oxide film thereon, said film characterized by a maximum surface resistance of about 5 ohms per square.
Claim 10
Dependent Claim
33 words
An article of manufacture comprisng a generally transparent substrate such as glass and a fluorine-doped stannic oxide film thereon, said film characterized by a maximum surface resistance of about 5 ohms per square.
Claim 11
Dependent Claim
28 words
An article of manufacture as defined in claim 8 having an infrared reflectivity of about 90%, said film having a fluorine-to-oxygen ratio of between about 0.007 and 0.03.
Claim 12
Dependent Claim
30 words
An article of manufacture comprising an inorganic substrate and an electroconductive fluorine-doped stannic oxide film thereon, said doped film having an electron drift mobility of above 40 cm 2 /volt-second.
Claim 13
Dependent Claim
30 words
An article of manufacture comprising an inorganic substrate and an electroconductive fluorine-doped stannic oxide film thereon, said doped film having an electron drift mobility of above 40 cm 2 /volt-second.
Claim 14
Dependent Claim
20 words
An article of manufacture as defined in claim 10 wherein said electron drift mobility is above 50 cm 2 .
Claim 15
Dependent Claim
23 words
An article of manufacture as defined in claim 10 wherein said film comprises a fluorine-to-oxygen ratio of from about 0.01 to about 0.025.
Claim 16
Dependent Claim
24 words
An article of manufacture as defined in claims 10, 11, or 12 wherein the resistivity of said film is below 10 ohms per square.
Claim 17
Dependent Claim
43 words
A semiconductor article of the type used in electronic circuitry comprising a coating of fluorine-doped stannic oxide which is characterized by a resistance of less than about 5 ohms per square and a bulk resistivity in said coating of about 10 -4 ohm-cm.
Claim 18
Dependent Claim
43 words
A semiconductor article of the type used in electronic circuitry comprising a coating of fluorine-doped stannic oxide which is characterized by a resistance of less than about 5 ohms per square and a bulk resistivity in said coating of about 10 -4 ohm-cm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-04 | 1984-11-03 | 1985-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-04 | 1988-11-03 | 1989-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-04 | 1992-11-03 | 1993-05-05 | $7700.00 | Window Closed / Lapsed |