Etching of optical fibers
Assignee: RCA Corp
•
Filing: 1979-05-04
•
Granted: 1981-05-05
•
Expires: 1999-05-04
Abstract
Abstract A method for reducing the diameter of the end of an optical fiber while leaving the fiber end flat or slightly concave so that a lens can be formed thereon. The fiber end is etched in a solution of aqueous hydrofluoric acid to which is added ammonium fluoride, ammonium bifluoride or a combination thereof.
Inventors
- 👤 Ivan Ladany
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:56
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/66; C03C25/68; G; G02; G02B; G02B6/00; G02B6/24; G02B6/42; G02B6/4201; G02B6/4202; G02B6/4203
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
88 words
A method of etching a single mode optical fiber comprising a fused silica core with a borosilicate glass cladding and having a flat end face whereby a portion of the cladding is removed while leaving the end face flat or slightly concave which consists essentially of etching an end portion of the fiber in a concentrated aqueous hydrofluoric acid solution containing an amount of ammonium fluoride, ammonium bifluoride or mixtures thereof effective for reducing the diameter of the fiber while leaving the end face flat or slightly concave.
Claim 2
Independent Claim
88 words
A method of etching a single mode optical fiber comprising a fused silica core with a borosilicate glass cladding and having a flat end face whereby a portion of the cladding is removed while leaving the end face flat or slightly concave which consists essentially of etching an end portion of the fiber in a concentrated aqueous hydrofluoric acid solution containing an amount of ammonium fluoride, ammonium bifluoride or mixtures thereof effective for reducing the diameter of the fiber while leaving the end face flat or slightly concave.
Claim 3
Dependent Claim
134 words
In a method for forming a lens on the end of a single mode optical fiber comprising a fused silica core and a borosilicate glass cladding having a flat end face which comprises removing a portion of the cladding by chemical etching of an end portion of said fiber, cutting said end portion to form a flat end face thereon and forming a lens on the flat end face of said fiber, the improvement which consists essentially of etching said end portion in a concentrated aqueous hydrofluoric acid solution containing an effective amount of ammonium fluoride, ammonium bifluoride or mixtures thereof whereby a portion of said cladding is removed while leaving said end face flat or slightly concave thereby eliminating the step of cutting said end portion to form a flat end face thereon.
Claim 4
Dependent Claim
134 words
In a method for forming a lens on the end of a single mode optical fiber comprising a fused silica core and a borosilicate glass cladding having a flat end face which comprises removing a portion of the cladding by chemical etching of an end portion of said fiber, cutting said end portion to form a flat end face thereon and forming a lens on the flat end face of said fiber, the improvement which consists essentially of etching said end portion in a concentrated aqueous hydrofluoric acid solution containing an effective amount of ammonium fluoride, ammonium bifluoride or mixtures thereof whereby a portion of said cladding is removed while leaving said end face flat or slightly concave thereby eliminating the step of cutting said end portion to form a flat end face thereon.
Claim 5
Dependent Claim
32 words
A method according to claim 1 or 2 wherein said etching solution consists of about 0.40 to about 0.46 gram of ammonium bifluoride per cubic centimeter of concentrated aqueous hydrofluoric acid solution.
Claim 6
Dependent Claim
33 words
A method according to claim 1 or 2 wherein said etching solution consists of about 0.17 to about 0.25 gram of ammonium fluoride per cubic centimeter of a concentrated aqueous hydrofluoric acid solution.
Claim 7
Dependent Claim
25 words
A method according to claim 1 or 2 wherein said concentrated aqueous hydrofluoric acid solution consists of about 48 to 51% by weight hydrofluoric acid.
References Cited (Backward Citations)
US2479286A
Cited
US3551228A
Cited
US3883353A
Cited
US4040897A
Cited
US4118270A
Cited
US4040893A
Cited
US4193663A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-04 | 1984-11-03 | 1985-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-04 | 1988-11-03 | 1989-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-04 | 1992-11-03 | 1993-05-05 | $7700.00 | Window Closed / Lapsed |