Method of preparing a luminescent aluminate
Assignee: US Philips Corp
•
Filing: 1979-09-14
•
Granted: 1981-04-21
•
Expires: 1999-09-14
Abstract
Abstract In a method of preparing a luminescent aluminate comprising aluminium and one or more of the metals yttrium and elements of the lanthanum series the component metals of the aluminate are co-precipitated from aqueous solutions of salts of these metals by combining these salts with a precipitation agent comprising carbon dioxide and ammonia in a quantity from 1 to 3 mole per mole of carbon dioxide. Such a quantity of the precipitation agent is used that the molar ratio of the carbon in the precipitation agent to the sum of the metals in the salts has a value from 1 to 10, a higher value in that range being chosen for this ratio according as the desired average grain size of the precipitate is larger. Finally, the precipitate obtained is heated at an elevated temperature.
Inventors
- 👤 Franciscus J. M. Swinkels
- 👤 Rudolfus J. C. Bannenberg
- 👤 Johannes H. A. Schmitz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:56
CPC Classifications
C; C01; C01F; C01F17/00; C01F17/30; C01F17/32; C01F17/34; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7774; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/60
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
162 words
A method of preparing a luminescent aluminate comprising as a cation at least one metal selected from the group consisting of yttrium and an element selected from those having atomic numbers 57 to 71 inclusive comprising: (a) forming an aqueous solution of the chloride salts of the component metals of the aluminate. (b) adding a precipitation agent containing ammonium carbonate or carbon dioxide and ammonia in a quantity ranging from 1 to 3 moles of ammonia per mole of carbon dioxide to said aqueous solution in an amount such that the molar ratio of carbon in the ammonium carbonate or carbon dioxide of the precipitation agent to the sum of the metals of the salts has a value of from 3 to 10 to thereby cause said component metals of said aluminate to co-precipitate from said aqueous solution, and (c) separating and heating said resultant co-precipitate at a temperature and for a time sufficient to effect the formation of said luminescent aluminate.
Claim 2
Independent Claim
162 words
A method of preparing a luminescent aluminate comprising as a cation at least one metal selected from the group consisting of yttrium and an element selected from those having atomic numbers 57 to 71 inclusive comprising: (a) forming an aqueous solution of the chloride salts of the component metals of the aluminate. (b) adding a precipitation agent containing ammonium carbonate or carbon dioxide and ammonia in a quantity ranging from 1 to 3 moles of ammonia per mole of carbon dioxide to said aqueous solution in an amount such that the molar ratio of carbon in the ammonium carbonate or carbon dioxide of the precipitation agent to the sum of the metals of the salts has a value of from 3 to 10 to thereby cause said component metals of said aluminate to co-precipitate from said aqueous solution, and (c) separating and heating said resultant co-precipitate at a temperature and for a time sufficient to effect the formation of said luminescent aluminate.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein the molar ratio of the carbon to the sum of the metals is 3 to 8.
Claim 4
Dependent Claim
62 words
The method of claim 2 wherein the solution of the metal chlorides contains from 0.5 to 3 mols of chloride per liter and an aqueous solution of ammonium carbonate containing at least 1.5 moles of ammonium carbonate per liter is used as the precipitation agent and wherein the temperature of the solutions has a value above 50° to 95° C. during precipitation.
Claim 5
Dependent Claim
35 words
The method of claim 3 wherein the solution of the ammonium carbonate contains at least 3 mols of carbonate per liter and the temperature of the solutions during precipitation is from 70° to 95° C.
Claim 6
Dependent Claim
27 words
The method of claim 4 wherein the solution of metal chlorides and the solution of the ammonium carbonate are supplied simultaneously with stirring to a reaction vessel.
Claim 7
Dependent Claim
62 words
The method of claim 5 wherein aluminum chloride, cerium chloride, terbium chloride and magnesium chloride in an aqueous solution are co-precipitated by the addition thereto of an aqueous solution of ammonium carbonate and the resulting co-precipitate is heated at a temperature and for a time sufficient to effect the formation of a luminescent terbium-activated cerium magnesium aluminate having a hexagonal crystal structure.
Claim 8
Dependent Claim
21 words
A method as claimed in claim 1, characterized in that an aqueous ammonium carbonate solution is used as the precipitation agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-20 | 1984-10-20 | 1985-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-20 | 1988-10-20 | 1989-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-20 | 1992-10-20 | 1993-04-21 | $7700.00 | Window Closed / Lapsed |