Abstract An otherwise conventional two-stage (mass suspension polymerization system for making impact polystyrene is modified in several respects: (a) the rubber (about 7% to about 10% of the polymerization charge) to be dissolved in styrene has a cis content greater than 97%, (b) a portion, i.e. 5-15%, of the free-radical catalyst to be used is added at the beginning of the mass polymerization stage, i.e. at about 235 DEG -250 DEG F. after dissolving the rubber in the styrene, and (c) the addition of the major portion (about at least 85%) of the mercaptan chain regulator added is made at the time of the initiation of the mass polymerization stage when the temperature first reaches the temperature employed for mass polymerization (such temperature selected from the range of 235 DEG -250 DEG F.). The rubber used should have a viscosity as a 5% solution in toluene of 70-95 cps at 25 DEG C. Mineral oil, preferably high boiling, containing at least 20% saturated naphthenic hydrocarbons, is added in an amount of about 1.3% to about 2.3% of the reaction charge. The resulting product is exceptionally high in impact resistance.
Inventors
👤 Harry D. Anspon
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-08 12:13
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
254 words
Method of making polystyrene useful in sheet forming applications comprising: (a) preparing a polymerization charge comprising about 7% to about 10% polybutadiene rubber having a cis content of at least 97%, and having a viscosity as a 5% solution in toluene of 70-95 cps at 25° C., about 1.3% to about 2.3% of a high boiling mineral oil containing at least 20% saturated naphthenic hydrocarbons, about 0 to about 0.62×10 -4 mole mercaptan chain regulator per mole of styrene and the balance styrene, (b) elevating the temperature of the charge to at least about 235° F. and below 250° F. and adding thereto about 0.27×10 -4 mole to about 0.80×10 -4 mole free radical peroxy catalyst per mole of styrene, said catalyst having a half-life of from about 1/2 hour to about 10 hours at 235°-250° F., (c) adding to the charge about 3.5×10 -4 mole to about 4.73×10 -4 mole of mercaptan chain regulator per mole of styrene within fifteen minutes after the initiation of mass polymerization on reaching a temperature selected from within the range of 235°-250° F., (d) maintaining the temperature of the polymerization charge between about 235° C. and 250° C. until phase inversion is complete and a suitable viscosity for suspension is reached, (e) suspending the polymerization reaction mixture in water, (f) adding about 4.55×10 -4 mole to about 5.89 mole of a free radical peroxy catalyst per mole of styrene, and (g) continuing the polymerization at temperatures of up to about 270° F. until at least 99.7% complete.
Claim 2
Dependent Claim
254 words
Method of making polystyrene useful in sheet forming applications comprising: (a) preparing a polymerization charge comprising about 7% to about 10% polybutadiene rubber having a cis content of at least 97%, and having a viscosity as a 5% solution in toluene of 70-95 cps at 25° C., about 1.3% to about 2.3% of a high boiling mineral oil containing at least 20% saturated naphthenic hydrocarbons, about 0 to about 0.62×10 -4 mole mercaptan chain regulator per mole of styrene and the balance styrene, (b) elevating the temperature of the charge to at least about 235° F. and below 250° F. and adding thereto about 0.27×10 -4 mole to about 0.80×10 -4 mole free radical peroxy catalyst per mole of styrene, said catalyst having a half-life of from about 1/2 hour to about 10 hours at 235°-250° F., (c) adding to the charge about 3.5×10 -4 mole to about 4.73×10 -4 mole of mercaptan chain regulator per mole of styrene within fifteen minutes after the initiation of mass polymerization on reaching a temperature selected from within the range of 235°-250° F., (d) maintaining the temperature of the polymerization charge between about 235° C. and 250° C. until phase inversion is complete and a suitable viscosity for suspension is reached, (e) suspending the polymerization reaction mixture in water, (f) adding about 4.55×10 -4 mole to about 5.89 mole of a free radical peroxy catalyst per mole of styrene, and (g) continuing the polymerization at temperatures of up to about 270° F. until at least 99.7% complete.
Claim 3
Dependent Claim
13 words
Method of claim 1 in which the mercaptan chain regulator is t-dodecyl mercaptan.
Claim 4
Dependent Claim
11 words
Method of claim 1 in which the catalyst is t-butyl perbenzoate.