Graft polybutadiene-styrene interpolymers and process for making same

Claim 2

A moldable composition, having improved impact value, comprising a graft interpolymer of styrene and from about 1 to 20 percent of a rubbery, 1,4-polybutadiene, based on the total composition weight, said amount of polybutadiene being effective in substantially improving the impact value in said composition, said 1,4-polybutadiene characterized by having a cis butadiene content of at least 25 percent and a 1,2-addition content of not more than about 10 percent based on the weight of said 1,4-polybutadiene, said composition prepared by polymerizing under free radical polymerization conditions, with agitation, a homogeneous mixture comprising said styrene and said polybutadiene to provide a dispersed and substantially uniform composition, said composition containing a continuous phase which is polymerized styrene and a discontinuous phase which is a graft copolymer of 1,4-polybutadiene and styrene, said discontinuous phase being substantially insoluble in toluene at room temperature.

Claim 3

The composition of claim 1 which is prepared by solution polymerization.

Claim 4

The composition of claim 1 wherein the 1,4-polybutadiene employed has a minor percentage greater than 25 percent of cis butadiene content and a 1,2-addition butadiene content of less than about 10 percent.

Claim 5

The composition of claim 3 wherein the 1,4-polybutadiene has a cis butadiene content of about 35 percent.

Claim 6

The composition of claim 1 wherein the 1,4-polybutadiene employed has a content of cis butadiene units up to about 95% and a low amount of 1,2-addition butadiene content which is less than about 10 percent.

Claim 7

The composition of claim 5 wherein the 1,4 polybutadiene employed has a cis butadiene content of about 95 percent.

Claim 8

The composition of claim 1 wherein said polybutadiene is present in an amount of from 1 to about 10 percent by weight.

Claim 9

The composition of claim 7 wherein said polybutadiene is percent in an amount of at least about 5 percent by weight.

Claim 10

The composition of claim 3 wherein said polybutadiene is present in an amount of from 1 to about 10 percent by weight.

Claim 11

The composition of claim 9 wherein said polybutadiene is present in an amount of at least about 5 percent by weight.

Claim 12

The composition of claim 5 wherein said polybutadiene is present in an amount of from 1 to about 10 percent by weight.

Claim 13

The composition of claim 11 wherein said polybutadiene is present in an amount of an least about 5 percent by weight.

Claim 14

A moldable vinyl aromatic polymer composition of improved impact value comprising a graft copolymer of polymerized vinyl aromatic monomer and a rubbery, 1,4-polybutadiene polymer, said rubbery 1,4-polybutadiene being present in an amount of from about 1 to 20 percent by weight of the composition, said amount of polybutadiene being effective in substantially improving the impact value of said composition, said polybutadiene further characterized by having a cis butadiene content of at least 25 percent and a 1,2-addition content of not more than about 10 percent based on the weight of said 1,4-polybutadiene, said composition being prepared by polymerizing under free radical polymerization conditions, with agitation, a homogeneous mixture comprising said vinyl aromatic monomer and said 1,4-polybutadiene, to provide a dispersed and substantially uniform composition, said composition comprising a continuous phase of polymerized vinyl aromatic monomer and a discontinuous phase which is a graft copolymer of 1,4-polybutadiene and vinyl aromatic monomer, said discontinuous phase being substantially insoluble in toluene at room temperature.

Claim 15

A moldable vinyl aromatic polymer composition of improved impact value comprising a graft copolymer of polymerized vinyl aromatic monomer and a rubbery, 1,4-polybutadiene polymer, said rubbery 1,4-polybutadiene being present in an amount of from about 1 to 20 percent by weight of the composition, said amount of polybutadiene being effective in substantially improving the impact value of said composition, said polybutadiene further characterized by having a cis butadiene content of at least 25 percent and a 1,2-addition content of not more than about 10 percent based on the weight of said 1,4-polybutadiene, said composition being prepared by polymerizing under free radical polymerization conditions, with agitation, a homogeneous mixture comprising said vinyl aromatic monomer and said 1,4-polybutadiene, to provide a dispersed and substantially uniform composition, said composition comprising a continuous phase of polymerized vinyl aromatic monomer and a discontinuous phase which is a graft copolymer of 1,4-polybutadiene and vinyl aromatic monomer, said discontinuous phase being substantially insoluble in toluene at room temperature.

Claim 16

The composition of claim 13 wherein the vinyl aromatic monomer is styrene.

Claim 17

A moldable styrene polymer composition having improved impact value, formed by the polymerization of styrene monomer having rubbery, 1,4-polybutadiene homogeneously dispersed therein, said polymerization being carried out under free radical polymerization conditions until the polymerization of said styrene monomer is substantially completed and being carried out under agitation conditions to provide a dispersed and substantially uniform composition, said 1,4-polybutadiene being present in an amount of from 1 percent to about 20 percent based on the total final polymer composition weight, said amount of polybutadiene being effective in substantially improving the impact value of said composition, said polybutadiene being characterized by having a cis butadiene content of at least about 25 percent and a 1,2-addition butadiene content of not more than about 10 percent, based on the weight of said polybutadiene.

Claim 18

A moldable styrene polymer composition having improved impact value, formed by the polymerization of styrene monomer having rubbery, 1,4-polybutadiene homogeneously dispersed therein, said polymerization being carried out under free radical polymerization conditions until the polymerization of said styrene monomer is substantially completed and being carried out under agitation conditions to provide a dispersed and substantially uniform composition, said 1,4-polybutadiene being present in an amount of from 1 percent to about 20 percent based on the total final polymer composition weight, said amount of polybutadiene being effective in substantially improving the impact value of said composition, said polybutadiene being characterized by having a cis butadiene content of at least about 25 percent and a 1,2-addition butadiene content of not more than about 10 percent, based on the weight of said polybutadiene.

Claim 19

The moldable styrene polymer composition of claim 15 which is prepared by solution polymerization techniques.

Claim 20

The composition of claim 15 wherein the 1,4-polybutadiene employed has a minor percentage greater than 25 percent of cis butadiene content and a 1,2-addition butadiene content of less than about 10 percent.

Claim 21

The composition of claim 17 wherein the 1,4-polybutadiene has a cis butadiene content of about 35 percent.

Claim 22

The composition of claim 15 wherein the 1,4-polybutadiene employed has a content of cis butadiene units up to about 95 percent and a low amount of 1,2-addition butadiene content which is less than about 10 percent.

Claim 23

The composition of claim 19 wherein the 1,4-polybutadiene employed has a cis butadiene content of about 95 percent.

Claim 24

The composition of claim 15 wherein said polybutadiene is present in an amount of from 1 to about 10 percent by weight.

Claim 25

The composition of claim 21 wherein said polybutadiene is present in an amount of at least about 5 percent by weight.

Claim 26

The composition of claim 17 wherein said polybutadiene is present in an amount of from 1 to about 10 percent by weight.

Claim 27

The composition of claim 23 wherein said polybutadiene is present in an amount of at least about 5 percent by weight.

Claim 28

The composition of claim 19 wherein said polybutadiene is present in an amount of from 1 to about 10 percent by weight.

Claim 29

The composition of claim 25 wherein said polybutadiene is present in an amount of from at least about 5 percent by weight.

Claim 30

The composition of claim 15 comprising a continuous phase which is polymerized styrene and a discontinuous phase which is a graft copolymer 1,4-polybutadiene and styrene.