Hot-melt size compositions and process for textiles
Assignee: Burlington Industries Inc
•
Filing: 1979-03-20
•
Granted: 1981-03-03
•
Expires: 1999-03-20
Abstract
Abstract A hot-melt warp yarn size composition and a method for applying, desizing, and disposing of it which essentially eliminates atmospheric and water pollution at all stages of the process. The size is a melt blend of ethylene/vinyl acetate copolymer with microcrystalline, paraffin, or hydrogenated tallow wax. It is applied as a melt to warp yarn, desized with hot petroleum solvent, and the extracted size and unrecovered solvent burned to non-polluting carbon dioxide and water.
Inventors
- 👤 Walter F. Illman
- 👤 Delano M. Conklin
- 👤 Clifton H. Karnes, Jr.
- 👤 Robert C. Malpass
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:50
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/227; D06L; D06L1/00; D06L1/02; D06L1/06; D06M13/00; D06M13/02; D06M13/10; D06M13/224
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
106 words
A process for treating textiles comprising the steps of: establishing a continuous feed of warp yarn; continuously applying a warp size to the continuously fed warp yarn to form sized yarn; forming the sized yarn into fabric; desizing the fabric utilizing a solvent; and removing the solvent from the fabric; wherein the improvement comprises: applying as the warp size a melt warp size consisting essentially of synthetic organic polymer or copolymer and wax, the wax selected from the group consisting essentially of microcrystalline, paraffin, and hydrogenated tallow waxes; and wherein the desizing is accomplished utilizing a heated hydrocarbon solvent, and wherein the removed solvent is recovered.
Claim 2
Dependent Claim
106 words
A process for treating textiles comprising the steps of: establishing a continuous feed of warp yarn; continuously applying a warp size to the continuously fed warp yarn to form sized yarn; forming the sized yarn into fabric; desizing the fabric utilizing a solvent; and removing the solvent from the fabric; wherein the improvement comprises: applying as the warp size a melt warp size consisting essentially of synthetic organic polymer or copolymer and wax, the wax selected from the group consisting essentially of microcrystalline, paraffin, and hydrogenated tallow waxes; and wherein the desizing is accomplished utilizing a heated hydrocarbon solvent, and wherein the removed solvent is recovered.
Claim 3
Dependent Claim
51 words
A process as recited in claim 1 wherein the size is burnable to carbon dioxide and water, and the solvent is a hot petroleum solvent, and comprising the further step of burning a mixture of the size removed from the fabric and unrecovered solvent while recovering the heat value during burning.
Claim 4
Dependent Claim
47 words
A process as recited in claims 1 or 2 wherein said size applying step is practiced by applying 2-22%, based upon yarn weight, of melted size having 10-45% synthetic organic polymer or copolymer with an inherent viscosity of 0.5 to 1.02, and 90 to 55 percent wax.
Claim 5
Dependent Claim
50 words
A process as recited in claim 1 wherein the desizing step is accomplished by soaking the fabric in a hot petroleum solvent, scouring the fabric in solvent vapors with hot liquid solvent, and then partially distilling the scouring extract to recover solvent in a mixture of unrecovered solvent and size.
Claim 6
Dependent Claim
24 words
A process as recited in claim 4 wherein the mixture of unrecovered solvent and size is burned while recovering the heat value during burning.
Claim 7
Dependent Claim
37 words
A process as recited in claim 1 wherein the solvent removal step is accomplished by drying the fabric to form vapors, collecting the vapors, condensing the collected vapors, and distilling the condensed vapors to form recovered solvent.
Claim 8
Dependent Claim
53 words
A process as recited in claims 1, 2, 4, or 6 wherein said size applying step is accomplished by applying 2-22%, based upon yarn weight, of melted size which comprises 10-45% of 85-70% ethylene to 15-30% vinyl acetate copolymer having an inherent viscosity of 0.5 to 1.02, and 90 to 55 percent wax.
Claim 9
Dependent Claim
48 words
A textile yarn melt-sized with 2-22%, based upon yarn weight, of a size which comprises 10-45% of 85-70% ethylene to 15-30% vinyl acetate copolymer having an inherent viscosity of 0.5-1.02; and 90-55% wax, the wax selected from the group consisting essentially of microcrystalline, paraffin, and hydrogenated tallow waxes.
Claim 10
Dependent Claim
48 words
A textile yarn melt-sized with 2-22%, based upon yarn weight, of a size which comprises 10-45% of 85-70% ethylene to 15-30% vinyl acetate copolymer having an inherent viscosity of 0.5-1.02; and 90-55% wax, the wax selected from the group consisting essentially of microcrystalline, paraffin, and hydrogenated tallow waxes.
References Cited (Backward Citations)
US3048553A
Cited
US2877196A
Cited
US3025167A
Cited
US3476504A
Cited
US3466717A
Cited
US3645948A
Cited
US3625735A
Cited
US3739567A
Cited
US3841833A
Cited
USRE29287E
Cited
US3984594A
Cited
US3960485A
Cited
US4076629A
Cited
US4106900A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |