Plasma sprayed MCrAlY coating
Assignee: RTX Corp
•
Filing: 1979-09-11
•
Granted: 1981-01-20
•
Expires: 1999-09-11
Abstract
Abstract An article with an improved MCrAlY coating is disclosed wherein a plasma sprayed MCrAlY coating is provided with a metallic envelope and then hot isostatically pressed to densify the coating and interdiffuse the envelope. Thus, the substrate is provided with a coating which in its bulk is the densified plasma coating with an outer surface zone which is enriched in a metal which enhances the oxidation-corrosion protective properties of the coating. Preferred coatings have a standard CoCrAlY bulk with a metal-enriched surface zone of about 0.02 mm depth. When aluminum is added the surface zone is comprised by weight percent of about 60 Co, 20 Cr and 22 Al. With chromium the surface zone is about 50 Co, 43 Cr and 8.5 Al.
Inventors
- 👤 Norman S. Bornstein
- 👤 Francis J. Wallace
- 👤 Michael A. De Crescente
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 01:07
CPC Classifications
F; F01; F01D; F01D5/00; F01D5/12; F01D5/28; F01D5/288; C; C23; C23C; C23C4/00; C23C4/18; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12736; Y10T428/1275; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12847; Y10T428/12854; Y10T428/12861; Y10T428/12931
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
191 words
An article with improved oxidation-corrosion resistance, usable in a gas turbine engine, comprising a superalloy component having an oxidation-corrosion protective MCrAlY type coating adhered thereto, where M is selected from the group consisting of nickel, cobalt and iron and where the coating is produced by the process which includes: (a) plasma spraying the MCrAlY coating onto the superalloy substrate, the coating being characterized as having pores, voids and similar defects, some of which extend to the free surface of the coating, said defects reducing the protectiveness of the coating; (b) sealing the free surface of the MCrAlY coating by providing a metallic envelope thereover, said envelope spanning and sealing the defects which extend to the free surface of the coating; and (c) hot isostatically pressing the coated substrate at a sufficient pressure and temperature and for a sufficient time to close the defects internal of the MCrAlY coating and those intersecting said free surface and to diffuse at least a portion of the metallic envelope into the MCrAlY coating, closure of said defects and diffusion of said metal envelope into the coating significantly enhancing the oxidation-corrosion protective properties of the coating.
Claim 2
Dependent Claim
191 words
An article with improved oxidation-corrosion resistance, usable in a gas turbine engine, comprising a superalloy component having an oxidation-corrosion protective MCrAlY type coating adhered thereto, where M is selected from the group consisting of nickel, cobalt and iron and where the coating is produced by the process which includes: (a) plasma spraying the MCrAlY coating onto the superalloy substrate, the coating being characterized as having pores, voids and similar defects, some of which extend to the free surface of the coating, said defects reducing the protectiveness of the coating; (b) sealing the free surface of the MCrAlY coating by providing a metallic envelope thereover, said envelope spanning and sealing the defects which extend to the free surface of the coating; and (c) hot isostatically pressing the coated substrate at a sufficient pressure and temperature and for a sufficient time to close the defects internal of the MCrAlY coating and those intersecting said free surface and to diffuse at least a portion of the metallic envelope into the MCrAlY coating, closure of said defects and diffusion of said metal envelope into the coating significantly enhancing the oxidation-corrosion protective properties of the coating.
Claim 3
Dependent Claim
13 words
The article of claim 1 wherein the outer zone is enriched in aluminum.
Claim 4
Dependent Claim
13 words
The article of claim 1 wherein the outer zone is enriched in chromium.
Claim 5
Dependent Claim
14 words
The article of claim 1 wherein the envelope of metal is a chromium electrodeposit.
Claim 6
Dependent Claim
40 words
The article of claim 1 wherein the weight percent composition of the bulk of the coating is comprised of about 65 Co, 24 Cr, 12 Al and that of the outer zone is about 60 Co, 20 Cr, 22 Al.
Claim 7
Dependent Claim
40 words
The article of claim 1 wherein the weight percent composition of the bulk of the coating is comprised of about 65 Co, 24 Cr, 12 Al, and that of the outer zone is about 50 Co, 43 Cr, 8.5 Al.
References Cited (Backward Citations)
US3361562A
Cited
US3542530A
Cited
US3594219A
Cited
US3754903A
Cited
US3676085A
Cited
US3873347A
Cited
US3961098A
Cited
US3866301A
Cited
US3978251A
Cited
US4070507A
Cited
US4145481A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |