Fibrated admix or polymer and process therefore
Assignee: Gates Corp
•
Filing: 1978-08-10
•
Granted: 1981-01-13
•
Expires: 1998-08-10
Abstract
Abstract A process for preparing: (1) a generally dry fibrated admix; (2) a powdered elastomer/fiber composite master batch or fully compounded stock; or (3) an elastomer/fiber composite master batch or fully compounded stock; by mixing a partitioning agent and, optionally, plasticizers or adhesives with a generally dry defiberized material to define the fibrated admix; and blending the fibrated admix with a powdered polymer to define a powdered master batch or compounded stock; or dispersing the fiber in a viscoelastic mass to define a master batch or fully compounded stock or formed article, and then curing the mass to define an improved fiber composite structure.
Inventors
- 👤 Richard W. Posiviata
- 👤 Jonathan A. Johnston
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:02
CPC Classifications
C; C08; C08L; C08L21/00; C08L77/00; C08L77/10; C08L9/00; C08L9/06; C08K; C08K3/00; C08K3/02; C08K3/04; C08K7/00; C08K7/02; C08L1/00; C08L1/02; C08L67/00
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
76 words
A fibrated admix comprising: synthetic discontinuous fibers selected from the group consisting of aramid, nylon and polyester, the fibers coated with a non-elastomeric stiffening agent and mechanically impacted and sized to pass through a discharge screen having openings with a breadth of about 0.5 mm to about 2 mm; carbon black particles dusted on the fibers and generally partitioning the fibers from each other; oil dispersed with and affixed to the fibers and carbon black particles.
Claim 2
Dependent Claim
76 words
A fibrated admix comprising: synthetic discontinuous fibers selected from the group consisting of aramid, nylon and polyester, the fibers coated with a non-elastomeric stiffening agent and mechanically impacted and sized to pass through a discharge screen having openings with a breadth of about 0.5 mm to about 2 mm; carbon black particles dusted on the fibers and generally partitioning the fibers from each other; oil dispersed with and affixed to the fibers and carbon black particles.
Claim 3
Dependent Claim
75 words
A composition comprising: a vulcanizable visco elastomeric matrix; discontinuous fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat and substantially uniformly dispersed in the matrix, said fibers characterized by being mechanically impacted and sized to pass through a discharge screen having a breadth of about 0.5 mm to about 2 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of the composition.
Claim 4
Dependent Claim
75 words
A composition comprising: a vulcanizable visco elastomeric matrix; discontinuous fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat and substantially uniformly dispersed in the matrix, said fibers characterized by being mechanically impacted and sized to pass through a discharge screen having a breadth of about 0.5 mm to about 2 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of the composition.
Claim 5
Dependent Claim
20 words
The composition of claim 2 wherein the fibers are selected from the group consisting of cellulose, aramid, nylon and polyester.
Claim 6
Dependent Claim
20 words
The composition of claim 3 wherein the fibers have a median length of about 0.03 mm to about 2.9 mm.
Claim 7
Dependent Claim
62 words
In a vulcanizable visco-elastomer-fiber composite, the improvement comprising: discontinuous fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat, substantially uniformly dispersed in the matrix, and sized to a median fiber length of about 0.1 mm to about 2.3 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of composite.
Claim 8
Dependent Claim
62 words
In a vulcanizable visco-elastomer-fiber composite, the improvement comprising: discontinuous fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat, substantially uniformly dispersed in the matrix, and sized to a median fiber length of about 0.1 mm to about 2.3 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of composite.
Claim 9
Dependent Claim
20 words
The composite of claim 5 wherein the fibers are selected from the group consisting of cellulose, aramid, nylon and polyester.
Claim 10
Dependent Claim
64 words
In a vulcanizable visco-elastomer-fiber composite, the improvement comprising: discontinuous cellulose fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat and including fibrated fibers defining fibrated particles, the fibers having a median length from about 0.1 mm to about 2.4 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of the composite.
Claim 11
Dependent Claim
64 words
In a vulcanizable visco-elastomer-fiber composite, the improvement comprising: discontinuous cellulose fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat and including fibrated fibers defining fibrated particles, the fibers having a median length from about 0.1 mm to about 2.4 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of the composite.
Claim 12
Dependent Claim
13 words
The composite of claim 7 wherein the fibers are of the newsprint type.
Claim 13
Dependent Claim
48 words
In a vulcanized elastomer-fiber composite, the improvement comprising: discontinuous cellulose fibers, including fibrated fibers defining fibrated particles, the fibers having a median length from about 0.1 mm to about 2.3 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of the composite.
Claim 14
Dependent Claim
48 words
In a vulcanized elastomer-fiber composite, the improvement comprising: discontinuous cellulose fibers, including fibrated fibers defining fibrated particles, the fibers having a median length from about 0.1 mm to about 2.3 mm and wherein the fibers constitute from about 5 to about 60 percent by volume of the composite.
Claim 15
Dependent Claim
13 words
The composite of claim 9 wherein the fibers are of the newsprint type.
Claim 16
Dependent Claim
141 words
In an oil-extended, rubber-like composite with carbon black filler, the improvement comprising: discontinuous cellulose fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat and have a median length of about 0.1 mm to about 2.3 mm and which constitute from about 15 to about 80 percent by volume of the composite and wherein the carbon black plus fiber constitute from about 20 to about 200 parts by weight per 100 parts by weight of rubber and where the fiber constitutes from about 25 to 60 percent of a combined volume occupied by the carbon black and fiber; and oil parts constituting at least about 80 percent by weight of the combined carbon black and fiber parts weight and wherein the oil occupies a volume comprising about 50 to 120 percent of the fiber volume.
Claim 17
Dependent Claim
141 words
In an oil-extended, rubber-like composite with carbon black filler, the improvement comprising: discontinuous cellulose fibers pretreated with oil and a particulate partitioning agent, the fibers free of an elastomeric precoat and have a median length of about 0.1 mm to about 2.3 mm and which constitute from about 15 to about 80 percent by volume of the composite and wherein the carbon black plus fiber constitute from about 20 to about 200 parts by weight per 100 parts by weight of rubber and where the fiber constitutes from about 25 to 60 percent of a combined volume occupied by the carbon black and fiber; and oil parts constituting at least about 80 percent by weight of the combined carbon black and fiber parts weight and wherein the oil occupies a volume comprising about 50 to 120 percent of the fiber volume.
Claim 18
Dependent Claim
23 words
The rubber-fiber composite of claim 11 wherein the composite has a with grain 10 percent secant modulus of at least about 50 psi.
Claim 19
Dependent Claim
15 words
The rubber-fiber composite of claim 11 wherein the cellulose includes a plurality of fibrous particles.
Claim 20
Dependent Claim
21 words
The rubber-fiber-composite of claim 11 wherein the fibers constitute from about 25 to about 60 percent by volume of the composite.
References Cited (Backward Citations)
US3697364A
Cited
US3709845A
Cited
US3969568A
Cited
US3985702A
Cited
US4060510A
Cited
US4125493A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |