Dry blending process

Claim 2

An improvement in the process for dry blending a polymeric composition in a mixing vessel, said composition having various components including: a. 100 parts by weight of a thermoplastic elastomer, said thermoplastic elastomer being a block copolymer having at least two monoalkenyl arene polymer end blocks A and at least one elastomeric conjugated diene mid block B, each block A having an average molecular weight between about 5,000 and about 125,000 and each block B having an average molecular weight between about 15,000 and about 250,000, said blocks A comprising 8-55% by weight of the copolymer, said block copolymer having an average particle size of between about 0.1 mm and about 2.0 mm, b. between about 25 and about 150 parts by weight of a thermoplastic polymer having an average particle size of between about 0.1 mm and 2.0 mm, and c. between about 5 and about 175 parts by weight of a plasticizer, which improvement comprises dry blending the various components at a temperature of between about 175° F and about 250° F.

Claim 3

A process according to claim 1 wherein said temperature is the discharge temperature of the polymeric composition.

Claim 4

A process according to claim 1 wherein said thermoplastic polymer is selected from the group consisting of poly(styrene), poly(ethylene), poly(propylene), copolymers of ethylene and vinyl acetate, and mixtures thereof.

Claim 5

A process according to claim 3 wherein said plasticizer is a hydrocarbon rubber extending oil.

Claim 6

A process according to claim 1 wherein the various components include from about 0 to about 150 parts by weight of a filler and from about 0 to about 90 parts by weight of an end block compatible resin.

Claim 7

A process according to claim 5 wherein said filler is selected from clay, talc, calcium carbonate and mixtures thereof.

Claim 8

A process for dry blending a polymeric composition which comprises: a. adding 100 parts by weight of a thermoplastic elastomer, from about 0 to about 150 parts by weight of a filler, and from about 25 to about 150 parts by weight of a thermoplastic polymer to a mixing vessel at ambient temperature wherein said thermoplastic elastomer is a block copolymer having at least two monoalkenyl arene polymer end blocks A and at least one elastomeric conjugated diene mid block B, each block A having an average molecular weight between about 5,000 and about 125,000 and each block B having an average molecular weight between about 15,000 and about 250,000, said blocks A comprising 8-55% by weight of the copolymer, and wherein said thermoplastic elastomers and said thermoplastic polymer have average particle sizes of between about 0.1 mm and about 2.0 mm; b. mixing the thermoplastic polymer, filler and thermoplastic elastomer for 0 to 60 seconds wherein the temperature of the resulting mixture increases to between about 100° F and 150° F; c. adding from about 5 to about 175 parts by weight of a plasticizer to the mixing vessel; and d. mixing the resulting polymeric composition for between about 3 and about 7 minutes until the temperature of the polymeric composition has increased to between about 175° F and about 250° F.

Claim 9

A process for dry blending a polymeric composition which comprises: a. adding 100 parts by weight of a thermoplastic elastomer, from about 0 to about 150 parts by weight of a filler, and from about 25 to about 150 parts by weight of a thermoplastic polymer to a mixing vessel at ambient temperature wherein said thermoplastic elastomer is a block copolymer having at least two monoalkenyl arene polymer end blocks A and at least one elastomeric conjugated diene mid block B, each block A having an average molecular weight between about 5,000 and about 125,000 and each block B having an average molecular weight between about 15,000 and about 250,000, said blocks A comprising 8-55% by weight of the copolymer, and wherein said thermoplastic elastomers and said thermoplastic polymer have average particle sizes of between about 0.1 mm and about 2.0 mm; b. mixing the thermoplastic polymer, filler and thermoplastic elastomer for 0 to 60 seconds wherein the temperature of the resulting mixture increases to between about 100° F and 150° F; c. adding from about 5 to about 175 parts by weight of a plasticizer to the mixing vessel; and d. mixing the resulting polymeric composition for between about 3 and about 7 minutes until the temperature of the polymeric composition has increased to between about 175° F and about 250° F.

Claim 10

A process according to claim 7 wherein: i. said thermoplastic polymer is selected from the group consisting of poly(styrene), poly(ethylene), poly(propylene), copolymers of ethylene and vinyl acetate, and mixtures thereof; ii. said plasticizer is a hydrocarbon rubber extending oil; and iii. said filler is selected from the group consisting of clay, talc, calcium carbonate and mixtures thereof.