US4243705A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for coating high solids coating compositions
Assignee: Sherwin Williams Co
•
Filing: 1977-12-08
•
Granted: 1981-01-06
•
Expires: 1997-12-08
Abstract
Abstract This invention is directed to a high solids coating composition and more specifically to a coating comprising low molecular weight hydroxy-containing polyesters, an epoxy resin and at least one crosslinking agent consisting of an isocyanate, an alkoxy alkyl melamine, or an amino condensation product.
Inventors
- 👤 William J. Yapp
- 👤 Robert E. McDonald
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:52
CPC Classifications
C; C09; C09D; C09D167/00; C09D167/02; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/4009; C08G18/4063; C08G18/62; C08G18/6212; C08G18/6216; C08G18/622; C08G18/6225; C08G18/6229; C08G63/00; C08G63/02; C08G63/12; C08G63/16; C08G63/18; C08G63/181; C09D175/00; C09D175/04; C09D175/06
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
192 words
A method for preparing a hard flexible film on a substrate which comprises coating the substrate at temperatures ranging up to about 250° F. with an effective amount of a high-solids coating composition and subsequently curing the coated substrate at temperatures ranging up to about 400° F.; said high-solids coating composition comprising from about 50 to 80 parts by weight of a polyester having an average molecular weight ranging up to about 1200 and a hydroxy content ranging from 2.0 to 12% by weight, about 10 to 40 parts by weight of at least one crosslinking agent selected from the class consisting of lower alkoxy methyl melamines, and condensation products of an aldehyde with an aminotriazine, aldehyde with urea, aldehyde with guanamine and said condensation products alkylolated with alcohol having 1 to 4 carbon atoms, about 2.0 to 10 parts by weight of a polyepoxide, about 2.0 to 8.0 parts by weight of a copolymer obtained by copolymerizing styrene or an alkyl-substituted styrene with at least one hydroxy compound selected from the class consisting of hydroxyalkyl acrylates and allyl alcohol, and up to about 5.0 parts by weight of an acid catalyst.
Claim 2
Independent Claim
192 words
A method for preparing a hard flexible film on a substrate which comprises coating the substrate at temperatures ranging up to about 250° F. with an effective amount of a high-solids coating composition and subsequently curing the coated substrate at temperatures ranging up to about 400° F.; said high-solids coating composition comprising from about 50 to 80 parts by weight of a polyester having an average molecular weight ranging up to about 1200 and a hydroxy content ranging from 2.0 to 12% by weight, about 10 to 40 parts by weight of at least one crosslinking agent selected from the class consisting of lower alkoxy methyl melamines, and condensation products of an aldehyde with an aminotriazine, aldehyde with urea, aldehyde with guanamine and said condensation products alkylolated with alcohol having 1 to 4 carbon atoms, about 2.0 to 10 parts by weight of a polyepoxide, about 2.0 to 8.0 parts by weight of a copolymer obtained by copolymerizing styrene or an alkyl-substituted styrene with at least one hydroxy compound selected from the class consisting of hydroxyalkyl acrylates and allyl alcohol, and up to about 5.0 parts by weight of an acid catalyst.
Claim 3
Dependent Claim
28 words
The method of claim 1 further characterized in that an organic solvent is present in an amount ranging from about 1.0 to 20% by weight of the composition.
Claim 4
Dependent Claim
27 words
The method of claim 2 further characterized in that the organic solvent is present in an amount ranging up to about 10% by weight of the composition.
Claim 5
Dependent Claim
21 words
The method of claim 1 further characterized in that the high solids composition is coated onto the substrate above ambient temperatures.
Claim 6
Dependent Claim
27 words
The method of claim 1 further characterized in that an inorganic pigment is present in an amount ranging up to about 60% by weight of the composition.
References Cited (Backward Citations)
US3410926A
Cited
US3516955A
Cited
US3719725A
Cited
US3852275A
Cited
US3978015A
Cited
US3959201A
Cited
US3922447A
Cited
US3989767A
Cited
US3978153A
Cited
DE2514338A1
Cited
US4027066A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-06 | 1984-07-07 | 1985-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-06 | 1988-07-07 | 1989-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-06 | 1992-07-07 | 1993-01-06 | $7700.00 | Window Closed / Lapsed |