Colored photochromic glasses and method

Claim 2

A colored silver halide-containing photochromic glass article exhibiting a surface coloration produced by the heat treatment of the photochromic glass article under flowing gaseous reducing conditions at a heat treatment temperature not exceeding about 450° C., said colored photochromic glass article exhibiting, in at least one cross-sectional dimension in the undarkened state, a spectral transmittance curve comprising at least one treatment-induced absorption peak having a peak location to the right of the line CB of FIG. 1 of the drawing.

Claim 3

A colored glass article in accordance with claim 1 which has a composition consisting essentially, in weight percent, of about 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, 0-6% Cs 2 O, 8-20% total of Li 2 O+Na 2 O+K 2 O+Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.004-0.02% CuO, 0.15-0.3% Ag, 0.1-0.2% Br, and 0.1-0.25% Cl, and includes, as optional constituents, up to about 10% total of other oxides or elements selected in amounts not exceeding the indicated proportions from the group consisting of up to 6% ZrO 2 , up to 3% TiO 2 , up to 0.5% PbO, up to 7% BaO, up to 4% CaO, up to 3% MgO, up to 6% Nb 2 O 5 , up to 4% La.sub. 2 O 3 , up to 2% F, up to 1% of transition metal oxide colorants, and up to 5% of rare earth metal oxide colorants, wherein the molar ratio of alkali metal oxides:B 2 O 3 ranges between about 0.55-0.85 and the weight ratio Ag:(Cl+Br) ranges between about 0.65-0.95.

Claim 4

A colored glass article in accordance with claim 2 which contains about 56.46 parts SiO 2 , 6.19 parts Al 2 O 3 , 18.15 parts B 2 O 3 , 1.81 parts Li 2 O, 4.08 parts Na 2 O, 5.72 parts K 2 O, 4.99 parts ZrO 2 , 2.07 parts TiO 2 , 0.006 parts CuO, 0.207 parts Ag, 0.116 parts Cl and 0.137 parts Br by weight.

Claim 5

A colored glass article in accordance with claim 3 which contains about 0.09 parts NiO and 0.01 parts CoO by weight.

Claim 6

A colored glass article in accordance with claim 3 which contains about 0.017 parts NiO and 0.020 parts CoO by weight.

Claim 7

A colored glass article in accordance with claim 1 which has a composition consisting essentially, in weight percent, of about 57.1-65.3% SiO 2 , 9.6-13.9% Al 2 O 3 , 12.0-22.0% B 2 O 3 , 1.0-3.5% Li 2 O, 3.7-12.0% Na 2 O, 0-5.8% K 2 O, 6-15% total of Li 2 O+Na 2 O+K 2 O, a weight ratio of Li 2 O content to Na 2 O+K 2 O content not exceeding about 2:3, 0.7-3.0% PbO, 0.1-1.0% Ag, 0.15-1.0% Cl, 0-3.0% Br, 0-2.5% F, 0.008-0.12% CuO, 0-1% total of transition metal oxide colorants, and 0-5% total of rare earth metal oxide colorants.

Claim 8

A colored glass article in accordance with claim 6 which contains about 58.6 parts SiO 2 , 17.5 parts B 2 O 3 , 11.5 Al 2 O 3 , 7.7 parts Na 2 O, 2.0 parts Li 2 O, 1.5 parts K 2 O, 2.2 parts PbO, 0.3 parts Ag, 0.37 parts Cl, 0.13 parts Br, 0.022 parts F and 0.025 parts CuO by weight.

Claim 11

A method in accordance with claim 8 wherein the silver halide-containing photochromic glass article is a finished ophthalmic lens which has been strengthened by a thermal or chemical tempering technique.

Claim 12

A method in accordance with claim 8 which comprises the further step, following the heat treatment of the article under reducing conditions, of strengthening the article by a thermal or chemical tempering technique.

Claim 13

A method in accordance with claim 8 wherein the silver halide-containing glass article has a composition consisting essentially, in weight percent, about 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, 0-6% Cs 2 O, 8-20% total of Li 2 O+Na 2 O+K 2 O+Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.004-0.02% CuO, 0.15-0.3% Ag, 0.1-0.2% Br, and 0.1-0.25% Cl, and includes, as optional constituents, up to about 10% total of other oxides or elements selected in amounts not exceeding the indicated proportions from the group consisting of up to 6% ZrO 2 , up to 3% TiO 2 , up to 0.5% PbO, up to 7% BaO, up to 4% CaO, up to 3% MgO, up to 6% Nb 2 O 5 , up to 4% La 2 O 3 , up to 2% F, up to 1% of transition metal oxide colorants, and up to 5% of rare earth metal oxide colorants, wherein the molar ratio of alkali metal oxides:B 2 O 3 ranges between about 0.55-0.85 and the weight ratio Ag:(Cl+Br) ranges between about 0.65-0.95.

Claim 14

A method in accordance with claim 8 wherein the silver halide-containing glass article has a composition consisting essentially, in weight percent, of about 57.1-65.3% SiO 2 , 9.6-13.9% Al 2 O 3 , 12.0-22.0% B 2 O 3 , 1.0-3.5% Li 2 O, 3.7-12.0% Na 2 O, 0-5.8% K 2 O, 6-15% total of Li 2 O+Na 2 O+K 2 O, a weight ratio of Li 2 O content to Na 2 O+K 2 O content not exceeding about 1:3, 0.7-3.0% PbO, 0.1-1.0% Ag, 0.15-1.0% Cl, 0-3.0% Br, 0-2.5% F, 0.008-0.12% CuO, 0-1% total of transition metal oxide colorants, and 0-5% total of rare earth metal oxide colorants.