Photochromic glass
Assignee: Corning Glass Works
•
Filing: 1979-02-28
•
Granted: 1980-02-26
•
Expires: 1999-02-28
Abstract
Abstract The instant invention is concerned with transparent photochromic glass compositions which not only exhibit desirably rapid darkening and fading characteristics, but which also demonstrate the other physical and optical properties required for use in ophthalmic applications. Such glasses utilize the presence of silver chloride and/or silver bromide crystals to impart photochromic behavior in a narrowly-defined composition range within the alkali metal aluminoborosilicate base system. Copper ions are also included in the composition to perform as a sensitizing agent. The glasses have the capability of being either thermally tempered or chemically strengthened to comply with the United States Food and Drug Administration regulations for lenses used in ophthalmic applications. Improved independence of temperature effects upon the photochromic properties can be achieved where the copper level, expressed as CuO, is maintained between about 0.004-0.02% by weight, the chloride value, expressed as Cl, is held between about 0.1-0.25% by weight, the silver content, expressed as Ag, is included between about 0.15-0.3% by weight, and the quantity of bromide, expressed as Br, is varied between about 0.1-0.2% by weight. The fading rate of the glasses is enhanced by maintaining the molar ratio of alkali metal oxides to B 2 O 3 between about 0.55-0.85, the molar ratio of alkali metal oxides minus Al 2 O 3 to B 2 O 3 is about 0.25-0.4, and the weight ratio Ag:(Cl+Br) is about 0.65-0.95.
Inventors
- 👤 George B. Hares
- 👤 David L. Morse
- 👤 Thomas P. Seward, III
- 👤 Dennis W. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:25
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/04; C03C4/06; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/903
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
266 words
A transparent photochromic glass which, in bodies of 2 mm cross section, will exhibit the following properties: (a) at about 20° C. will darken to a luminous transmittance below 40% in the presence of actinic radiation; will fade at least 30 percentage units of transmittance after five minutes' removal from the actinic radiation; and will fade to a luminous transmittance in excess of 80% in no more than two hours after being removed from the actinic radiation; (b) at about 40° C. will darken to a luminous transmittance below 55% in the presence of actinic radiation; will fade at least 25 percentage units of transmittance after five minutes' removal from the actinic radiation; and will fade to a luminous transmittance in excess of 80% in no more than two hours after being removed from the actinic radiation; and (c) at about -18° C. will not darken to a luminous transmittance below 15% in the presence of actinic radiation; said glass having a base composition consisting essentially, in weight percent on the oxide basis, of 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, 0-6% Cs 2 O, 8-20% Li 2 O+Na 2 O+K 2 O+Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.004-0.02% CuO, 0.15-0.3% Ag, 0.1-0.25% Cl, and 0.1-0.2% Br, the molar ratio of alkali metal oxide:B 2 O 3 ranging between about 0.55-0.85, where the composition is essentially free from divalent metal oxides other than CuO, and the weight ratio Ag:(Cl+Br) ranges about 0.65-0.95.
Claim 2
Dependent Claim
266 words
A transparent photochromic glass which, in bodies of 2 mm cross section, will exhibit the following properties: (a) at about 20° C. will darken to a luminous transmittance below 40% in the presence of actinic radiation; will fade at least 30 percentage units of transmittance after five minutes' removal from the actinic radiation; and will fade to a luminous transmittance in excess of 80% in no more than two hours after being removed from the actinic radiation; (b) at about 40° C. will darken to a luminous transmittance below 55% in the presence of actinic radiation; will fade at least 25 percentage units of transmittance after five minutes' removal from the actinic radiation; and will fade to a luminous transmittance in excess of 80% in no more than two hours after being removed from the actinic radiation; and (c) at about -18° C. will not darken to a luminous transmittance below 15% in the presence of actinic radiation; said glass having a base composition consisting essentially, in weight percent on the oxide basis, of 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, 0-6% Cs 2 O, 8-20% Li 2 O+Na 2 O+K 2 O+Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.004-0.02% CuO, 0.15-0.3% Ag, 0.1-0.25% Cl, and 0.1-0.2% Br, the molar ratio of alkali metal oxide:B 2 O 3 ranging between about 0.55-0.85, where the composition is essentially free from divalent metal oxides other than CuO, and the weight ratio Ag:(Cl+Br) ranges about 0.65-0.95.
Claim 3
Dependent Claim
43 words
A photochromic glass according to claim 1 wherein said P 2 O 5 content is no more than 5% and said SiO 2 content is 45-65%, the molar ratio (alkali metal oxide-Al 2 O 3 ):B 2 O 3 ranges between about 0.25-0.4.
Claim 4
Dependent Claim
100 words
A photochromic glass according to claim 1 wherein to said base composition are added up to 10% by weight total of the following extraneous ingredients in the indicated proportions of up to 6% ZrO 2 , up to 3% TiO 2 , up to 0.5% PbO, up to 7% BaO, up to 4% CaO, up to 3% MgO, up to 6% Nb 2 O 5 , up to 4% La 2 O 3 , and up to 2% F; and up to 1% total of transition metal oxides and/or up to 5% total of rare earth metal oxides as colorants.
Claim 5
Dependent Claim
41 words
A photochromic glass according to claim 1 wherein CuO is present in an amount of 0.005-0.011%, Ag is present in an amount between 0.175-0.225%, Cl is present in an amount of 0.12-0.225%, and Br is present in an amount between 0.1-0.15%.
Claim 6
Dependent Claim
49 words
A photochromic glass according to claim 2 and also containing up to 6% ZrO 2 and/or up to 6% Nb 2 O 5 wherein the molar ratio of (alkali metal oxide-Al 2 O 3 -ZrO 2 and/or Nb 2 O 5 ):B 2 O 3 ranges between about 0.25-0.4.
Claim 7
Dependent Claim
38 words
A photochromic glass according to claim 1 having a refractive index suitable for ophthalmic applications and having the capability of being chemically strengthened which contains at least 4 cation percent of Li 2 O and/or Na 2 O.
Claim 8
Dependent Claim
80 words
A photochromic glass according to claim 1 having a refractive index of 1.523 and the capability of being chemically strengthened having a base glass composition of the following approximate values, expressed in parts by weight of: ______________________________________
SiO.sub.2 56.46
Al.sub.2 O.sub.3
6.19
B.sub.2 O.sub.3
18.15
Li.sub.2 O 1.81
Na.sub.2 O 4.08
K.sub.2 O 5.72
ZrO.sub.2 4.99
TiO.sub.2 2.07
______________________________________ and containing photochromic elements, as analyzed in weight percent of about: ______________________________________
CuO 0.006
Ag 0.207
Cl 0.166
Br 0.137
______________________________________
Claim 9
Dependent Claim
19 words
A photochromic glass according to claim 1 wherein said glass contains no Li 2 O and/or Na 2 O.
References Cited (Backward Citations)
US3795523A
Cited
US4001019A
Cited
US3998647A
Cited
US3957499A
Cited
US4018965A
Cited
FR2320913B1
Cited
US4102693A
Cited
US4130437A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-25 | 1983-08-27 | 1984-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-25 | 1987-08-27 | 1988-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-25 | 1991-08-27 | 1992-02-26 | $7700.00 | Window Closed / Lapsed |