Method of making heat curable adhesive coated insulation for transformers
Assignee: Westinghouse Electric Corp
•
Filing: 1978-12-01
•
Granted: 1980-12-16
•
Expires: 1998-12-01
Abstract
Abstract A flexible resin adhesive coated substrate is made by: (A) coating a sheet material with a wet, heat reactive adhesive resin, containing a monomer and an amount of an ultraviolet radiation sensitive photoinitiator effective to cause polymerization of monomer in response to ultraviolet radiation, and (B) applying ultraviolet radiation to the adhesive resin coating on the sheet material to polymerize monomer without the application of heat, forming a dry, uncured coating of adhesive bonded to the sheet material.
Inventors
- 👤 George D. Dixon
- 👤 Edward J. Croop
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:57
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/10; B05D7/00; B05D7/24; C; C08; C08F; C08F283/00; C08F283/10; C09; C09J; C09J7/00; C09J7/20; C09J7/21; C09J7/30; C09J7/35; H; H01; H01F; H01F41/00; H01F41/02; H01F41/04; H01F41/12; H01F41/122; H01F41/125; H01F41/127
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
171 words
A method of making a flexible, resin adhesive coated substrate comprising the steps of: (A) applying a surface coating, on at least one side of a porous, flexible sheet material containing at least 4 wt.% moisture without appreciably impregnating the sheet, said coating consisting of a wet, heat reactive adhesive resin, having added thereto from about 10 parts to about 80 parts per 100 parts heat reactive resin of a monomer selected from the group consisting of acrylic monomer, vinyl monomer and mixtures thereof, and an amount of an ultraviolet radiation sensitive photoinitiator effective to cause polymerization of monomer in response to ultraviolet radiation; (B) applying ultraviolet radiation to the adhesive resin coating on the sheet material, in a manner and for a time effective to polymerize monomer without the application of heat so that the sheet material retains at least 3.5 wt.% moisture, to form a flexible substrate with a dry, uncured surface coating of adhesive bonded to the sheet material, said adhesive being curable by the application of heat.
Claim 2
Independent Claim
171 words
A method of making a flexible, resin adhesive coated substrate comprising the steps of: (A) applying a surface coating, on at least one side of a porous, flexible sheet material containing at least 4 wt.% moisture without appreciably impregnating the sheet, said coating consisting of a wet, heat reactive adhesive resin, having added thereto from about 10 parts to about 80 parts per 100 parts heat reactive resin of a monomer selected from the group consisting of acrylic monomer, vinyl monomer and mixtures thereof, and an amount of an ultraviolet radiation sensitive photoinitiator effective to cause polymerization of monomer in response to ultraviolet radiation; (B) applying ultraviolet radiation to the adhesive resin coating on the sheet material, in a manner and for a time effective to polymerize monomer without the application of heat so that the sheet material retains at least 3.5 wt.% moisture, to form a flexible substrate with a dry, uncured surface coating of adhesive bonded to the sheet material, said adhesive being curable by the application of heat.
Claim 3
Independent Claim
241 words
A method of making a flexible, patterned, porous, resin adhesive coated substrate comprising the steps of: (A) applying a surface coating, on at least one side of a moving, flexible, paper sheet material, containing at least 4 wt.% moisture, in a predetermined, discontinuous pattern, without appreciably impregnating the sheet, said coating consisting of a wet, heat reactive adhesive resin, having added thereto from about 10 parts to about 80 parts per 100 parts heat reactive resin of a monomer selected from the group consisting of acrylic monomer, vinyl monomer and mixtures thereof, and an amount of an ultraviolet radiation sensitive photoinitiator effective to cause polymerization of monomer in response to ultraviolet radiation, said adhesive resin pattern coating covering from about 10 percent to 90 percent of the sheet material area; (B) applying ultraviolet radiation to the adhesive resin coating on the sheet material, in a manner and for a time effective to polymerize monomer without the application of heat so that the sheet material retains at least 3.5 wt.% moisture to form a flexible substrate with a discontinuous, patterned, dry, uncured surface coating of adhesive bonded to the sheet material, where the sheet is moved by the ultraviolet radiation source at a rate of speed of between about 5 ft./min. to about 120 ft./min.; said adhesive being curable by the application of heat and said adhesive pattern coating covering from about 10 percent to 90 percent of the sheet material area.
Claim 4
Independent Claim
241 words
A method of making a flexible, patterned, porous, resin adhesive coated substrate comprising the steps of: (A) applying a surface coating, on at least one side of a moving, flexible, paper sheet material, containing at least 4 wt.% moisture, in a predetermined, discontinuous pattern, without appreciably impregnating the sheet, said coating consisting of a wet, heat reactive adhesive resin, having added thereto from about 10 parts to about 80 parts per 100 parts heat reactive resin of a monomer selected from the group consisting of acrylic monomer, vinyl monomer and mixtures thereof, and an amount of an ultraviolet radiation sensitive photoinitiator effective to cause polymerization of monomer in response to ultraviolet radiation, said adhesive resin pattern coating covering from about 10 percent to 90 percent of the sheet material area; (B) applying ultraviolet radiation to the adhesive resin coating on the sheet material, in a manner and for a time effective to polymerize monomer without the application of heat so that the sheet material retains at least 3.5 wt.% moisture to form a flexible substrate with a discontinuous, patterned, dry, uncured surface coating of adhesive bonded to the sheet material, where the sheet is moved by the ultraviolet radiation source at a rate of speed of between about 5 ft./min. to about 120 ft./min.; said adhesive being curable by the application of heat and said adhesive pattern coating covering from about 10 percent to 90 percent of the sheet material area.
Claim 5
Dependent Claim
56 words
The method of claim 2, wherein the sheet material is paper having a thickness of between about 1 mil to about 30 mil and a moisture content of between about 4 wt.% and about 15 wt.%, and the viscosity of the coating, containing adhesive resin, monomer and photoinitiator is between about 50 cps. and 5,500 cps.
Claim 6
Dependent Claim
37 words
The method of claim 2, wherein the photoinitiator is selected from the group consisting of benzophenone; diethoxy-acetophenone; benzoin methyl ether; benzoin ethyl ether; benzoin isopropyl ether; benzoin isobutyl ether; diethoxy-xanthanone; chlorothio-xanthanone; azo-bis-isobutyronitrile; N-methyl diethanolamine-benzophenone, and mixtures thereof.
Claim 7
Dependent Claim
55 words
The method of claim 2, wherein the monomer is present in the amount of from about 20 parts to about 35 parts by weight per 100 parts of heat reactive adhesive resin; and the photoinitiator is present in the amount of from about 0.25 wt.% to about 7.5 wt.% based on the weight of monomer.
Claim 8
Dependent Claim
41 words
The method of claim 2, including the additional steps of wrapping the flexible, dry adhesive coated sheet material around an article and then heating the dry coating for a time and at a temperature effective to heat cure the dry adhesive.
Claim 9
Dependent Claim
64 words
The method of claim 2, wherein the monomer is selected from the group consisting of 2-ethyl hexyl acrylate; 2-hydroxy ethyl acrylate; 2-methoxy ethyl acrylate; 2-ethoxy ethyl acrylate; 2-phenoxy ethyl acrylate; hexanediol diacrylate; neopentyl glycol diacrylate; tetraethylene glycol diacrylate; trimethylol propane triacrylate; pentaerythritol triacrylate; pentaerythritol tetracrylate; styrene; vinyl toluene; vinyl pyrrolidone; vinyl acetate; divinyl benzene, and mixtures thereof, and the adhesive resin is epoxy resin.
Claim 10
Dependent Claim
72 words
The method of claim 1, wherein the viscosity of the coating, containing adhesive resin monomer and photoinitiator, is between about 50 cps. and 5,500 cps., the sheet material is paper having a thickness of between 1 mil to about 30 mil., and the adhesive resin is coated onto and the ultraviolet radiation is applied to a sheet moving at a rate of speed of between about 5 ft./min. to about 120 ft./min.
References Cited (Backward Citations)
US3246271A
Cited
US3551270A
Cited
US3723223A
Cited
US4025407A
Cited
US3935330A
Cited
US4004061A
Cited
US4017453A
Cited
US4126505A
Cited
US3974302A
Cited
US4092443A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-16 | 1984-06-16 | 1984-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-16 | 1988-06-16 | 1988-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-16 | 1992-06-16 | 1992-12-16 | $7700.00 | Window Closed / Lapsed |