Method for preparing high solids films employing a plurality of curing mechanisms
Assignee: PPG Industries Inc
•
Filing: 1974-11-04
•
Granted: 1977-05-24
•
Expires: 1994-11-04
Abstract
Abstract Conventional thermosetting resins are thinned with radiation sensitive or actinic light sensitive materials and then subjected to a dual cure wherein the material is first subjected to ionizing irradiation or actinic light and then to the conventional curing mechanism of the thermosetting resin. The resultant film contains the properties of both the radiation sensitive material and the conventional thermosetting resin and is easily applied as a coating.
Inventors
- 👤 Wen-Hsuan Chang
- 👤 Marco Wismer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:53
CPC Classifications
C; C09; C09D; C09D167/00; C09D167/06; C08; C08G; C08G59/00; C08G59/14; C09D175/00; C09D175/04; C09D4/00; C09D4/06; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31688; Y10T428/31692
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
160 words
A method for preparing high solids films comprising subjecting a film of a mixture comprising a. a radiation sensitive liquid material; and b. a radiation insensitive thermosetting resin wherein said radiation sensitive liquid material is present in said mixture in an amount in the range of from about 20 to about 90 percent by weight and wherein said radiation insensitive thermosetting resin is present in said mixture in an amount in the range of from about 10 to about 80 percent by weight, to a member of either of the following two classes of crosslinking conditions: c. a first class consisting of ionizing irradiation and actinic light, or d. a second class consisting of oxidation, moisture and heating to partially cure said mixture and subsequently completely curing the remainder of said mixture by subjecting said partially cured mixture to a member of the other of said classes of curing conditions to form a film which is flexible and abrasion resistant.
Claim 2
Independent Claim
160 words
A method for preparing high solids films comprising subjecting a film of a mixture comprising a. a radiation sensitive liquid material; and b. a radiation insensitive thermosetting resin wherein said radiation sensitive liquid material is present in said mixture in an amount in the range of from about 20 to about 90 percent by weight and wherein said radiation insensitive thermosetting resin is present in said mixture in an amount in the range of from about 10 to about 80 percent by weight, to a member of either of the following two classes of crosslinking conditions: c. a first class consisting of ionizing irradiation and actinic light, or d. a second class consisting of oxidation, moisture and heating to partially cure said mixture and subsequently completely curing the remainder of said mixture by subjecting said partially cured mixture to a member of the other of said classes of curing conditions to form a film which is flexible and abrasion resistant.
Claim 3
Dependent Claim
128 words
The method of claim 1 wherein a. said radiation sensitive liquid material is selected from the group consisting of ethylenically unsaturated polyester resins solubilized in vinyl monomers, esters of acrylic acid, esters of methacrylic acid, amides of acrylic acid, amides of methacrylic acid, diacrylates, dimethacrylates, triacrylates and trimethacrylates; b. said radiation insensitive thermosetting resin is selected from the group consisting of radiation insensitive thermosetting alkyd resins, radiation insensitive thermosetting polyurethane resins, radiation insensitive thermosetting acrylic resins, radiation insensitive thermosetting polyepoxide resins, radiation insensitive thermosetting aminoplast resins and radiation insensitive thermosetting phenolic resins; and c. said first class consists of electron radiation having an energy of at least about 100,000 electron volts and ultraviolet light having a wavelength in the range of from about 180 to about 400 nanometers.
Claim 4
Dependent Claim
118 words
The method of claim 1 wherein a. said radiation sensitive liquid material is selected from the group consisting of ethylenically unsaturated polyester resins solubilized in vinyl monomers, esters of acrylic acid, esters of methacrylic acid, amides of acrylic acid, amides of methacrylic acid, diacrylates, dimethacrylates, triacrylates and trimethacrylates; b. said radiation insensitive thermosetting resin is selected from the group consisting of radiation insensitive thermosetting alkyd resins, radiation insensitive thermosetting polyurethane resins, radiation insensitive thermosetting acrylic resins and radiation insensitive thermosetting polyepoxide resins; and c. said first class consists of electron radiation having an energy of at least about 100,000 electron volts and ultraviolet light having a wavelength in the range of from about 180 to about 400 nanometers.
Claim 5
Dependent Claim
47 words
The method of claim 1 wherein said mixture is subjected to said first class of crosslinking conditions to partially cure said mixture and then said partially cured mixture is subjected to said second class of crosslinking conditions to form a film which is flexible and abrasion resistant.
Claim 6
Dependent Claim
47 words
The method of claim 1 wherein said mixture is subjected to said second class of crosslinking conditions to partially cure said mixture and then said partially cured mixture is subjected to said first class of crosslinking conditions to form a film which is flexible and abrasion resistant.
Claim 7
Dependent Claim
18 words
The method of claim 1 wherein said radiation insensitive thermosetting resin is a radiation insensitive thermosetting polyurethane resin.
Claim 8
Dependent Claim
14 words
The method of claim 6 wherein said second class of curing conditions is moisture.
Claim 9
Dependent Claim
18 words
The method of claim 1 wherein said radiation insensitive thermosetting resin is a radiation insensitive thermosetting alkyd resin.
Claim 10
Dependent Claim
14 words
The method of claim 8 wherein said second class of curing conditions is oxidation.
Claim 11
Dependent Claim
86 words
The method of claim 1 wherein said radiation insensitive thermosetting resin is a radiation insensitive thermosetting acrylic resin comprising an interpolymer of an unsaturated carboxylic acid amide and at least one other monomer having a CH 2 = C<group, said interpolymer being characterized by having amido hydrogen atoms replaced by the structure --RCHOR 1 , wherein R is selected from the group consisting of hydrogen and saturated lower aliphatic hydrocarbon radicals and R 1 is selected from the group consisting of hydrogen and lower alkyl radicals.
Claim 12
Dependent Claim
14 words
The method of claim 10 wherein said second class of crosslinking conditions is heating.
Claim 13
Dependent Claim
18 words
The method of claim 1 wherein said radiation insensitive thermosetting resin is a radiation insensitive thermosetting polyepoxide resin.
Claim 14
Dependent Claim
14 words
The method of claim 12 wherein said second class of crosslinking conditions is oxidation.
Claim 15
Dependent Claim
24 words
The method of claim 1 wherein said mixture is subjected to a total dose of ionizing irradiation of from 0.2 to about 20 megarads.
Claim 16
Independent Claim
166 words
A method for preparing high solids films comprising subjecting a film of a mixture comprising a. radiation sensitive liquid esters of acrylic acid; and b. radiation insensitive thermosetting polyurethane resin wherein said radiation sensitive liquid esters of acrylic acid are present in said mixture in an amount in the range of from about 20 to about 90 percent by weight and wherein said radiation insensitive thermosetting polyurethane resin is present in said mixture in an amount in the range of from about 10 to about 80 percent by weight, to a member of either of the following two classes of crosslinking conditions. c. a first class consisting of ionizing irradiation and actinic light, or d. a second class consisting of oxidation, moisture and heating to partially cure said mixture and subsequently completely curing the remainder of said mixture by subjecting said partially cured mixture to a member of the other of said classes of curing conditions to form a film which is flexible and abrasion resistant.
Claim 17
Independent Claim
166 words
A method for preparing high solids films comprising subjecting a film of a mixture comprising a. radiation sensitive liquid esters of acrylic acid; and b. radiation insensitive thermosetting polyurethane resin wherein said radiation sensitive liquid esters of acrylic acid are present in said mixture in an amount in the range of from about 20 to about 90 percent by weight and wherein said radiation insensitive thermosetting polyurethane resin is present in said mixture in an amount in the range of from about 10 to about 80 percent by weight, to a member of either of the following two classes of crosslinking conditions. c. a first class consisting of ionizing irradiation and actinic light, or d. a second class consisting of oxidation, moisture and heating to partially cure said mixture and subsequently completely curing the remainder of said mixture by subjecting said partially cured mixture to a member of the other of said classes of curing conditions to form a film which is flexible and abrasion resistant.
References Cited (Backward Citations)
US2673151A
Cited
US2921006A
Cited
US3380950A
Cited
US3700752A
Cited
US3660217A
Cited
US3670049A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |