US4235651A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fabrication of GaAs-GaAlAs solar cells
Assignee: Raytheon Co
•
Filing: 1979-03-19
•
Granted: 1980-11-25
•
Expires: 1999-03-19
Abstract
Abstract The specification describes an improved III-V compound solar cell structure and fabrication process therefor wherein a P-type layer of gallium aluminum arsenide is epitaxially grown on an N-type gallium arsenide substrate to form a P-type region and a PN junction in the substrate. Controlled amounts of beryllium are introduced into both the epitaxial layer and the substrate, either during epitaxial growth or by using beryllium ion implantation techniques subsequent to the P-type epitaxial growth step. The homojunction-heterostructure device thus formed exhibits improved power conversion efficiencies in excess of 17%.
Inventors
- 👤 G. Sanjiv Kamath
- 👤 Carl L. Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:19
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/14; H10F10/144; H10F10/16; H10F10/163; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/544; Y10; Y10S; Y10S148/00; Y10S148/04; Y10S438/00; Y10S438/98
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
140 words
A process for fabricating a III-V compound solar cell having an improved power conversion efficiency, comprising: (a) providing a saturated epitaxial growth solution of gallium aluminum arsenide in gallium and aluminum at a predetermined solution growth temperature, (b) introducing beryllium atoms into said solution in a preselected amount sufficient to establish a desired P-type doping level in said solution, and (c) exposing an N-type gallium arsenide substrate to said solution for a predetermined time and under conditions of controlled liquid epitaxial growth temperature to form a P-type epitaxial layer of gallium aluminum arsenide on said gallium arsenide substrate and to convert a region of said substrate to P-type gallium arsenide, thereby defining a PN junction of said solar cell bounded by relatively low resistivity material which resistivity is substantially invariant with changes in the aluminum concentration in said solar cell.
Claim 2
Dependent Claim
140 words
A process for fabricating a III-V compound solar cell having an improved power conversion efficiency, comprising: (a) providing a saturated epitaxial growth solution of gallium aluminum arsenide in gallium and aluminum at a predetermined solution growth temperature, (b) introducing beryllium atoms into said solution in a preselected amount sufficient to establish a desired P-type doping level in said solution, and (c) exposing an N-type gallium arsenide substrate to said solution for a predetermined time and under conditions of controlled liquid epitaxial growth temperature to form a P-type epitaxial layer of gallium aluminum arsenide on said gallium arsenide substrate and to convert a region of said substrate to P-type gallium arsenide, thereby defining a PN junction of said solar cell bounded by relatively low resistivity material which resistivity is substantially invariant with changes in the aluminum concentration in said solar cell.
Claim 3
Dependent Claim
32 words
The process defined in claim 1 wherein beryllium is introduced into said epitaxial growth solution in quantities from between 5 to 10 milligrams for every 1,000 grams of gallium in said solution.
Claim 4
Dependent Claim
60 words
The process defined in claim 1 wherein said epitaxial growth solution is initially maintained at a crystal growth temperature of about 750° C. or greater and is thereafter reduced at approximately 0.2° C. per minute for approximately five minutes in order to grow a P-type epitaxial layer of gallium aluminum arsenide on the order of about one micrometer in thickness.
Claim 5
Dependent Claim
32 words
The process defined in claim 3 wherein beryllium is introduced into said epitaxial growth solution in quantities from between 5 to 10 milligrams for every 1,000 grams of gallium in said solution.
Claim 6
Dependent Claim
103 words
A process for lowering the resistivity in a III-V compound semiconductor structure substantially independently of the aluminum concentration therein which comprises: (a) providing a substrate of N-type gallium arsenide, (b) forming an epitaxial layer of gallium aluminum arsenide on said substrate and of P-type conductivity to thereby convert a region of said substrate to P-type conductivity and form a PN junction therein, and either simultaneously or subsequently (c) introducing predetermined quantities of beryllium into said P-type epitaxial layer and said P-type region thereunder to reduce the resistivity on both sides of said PN junction and thus reduce resistive power losses in said structure.
Claim 7
Dependent Claim
103 words
A process for lowering the resistivity in a III-V compound semiconductor structure substantially independently of the aluminum concentration therein which comprises: (a) providing a substrate of N-type gallium arsenide, (b) forming an epitaxial layer of gallium aluminum arsenide on said substrate and of P-type conductivity to thereby convert a region of said substrate to P-type conductivity and form a PN junction therein, and either simultaneously or subsequently (c) introducing predetermined quantities of beryllium into said P-type epitaxial layer and said P-type region thereunder to reduce the resistivity on both sides of said PN junction and thus reduce resistive power losses in said structure.
Claim 8
Dependent Claim
32 words
The process defined in claim 5 wherein beryllium is introduced into said epitaxial growth solution in quantities from between 5 and 10 milligrams for every 1,000 grams of gallium in said solution.
Claim 9
Dependent Claim
60 words
The process defined in claim 6 wherein said epitaxial growth solution is initially maintained at a crystal growth temperature of about 750° C. or greater and is thereafter reduced at approximately 0.2° C. per minute for approximately five minutes in order to grow a P-type epitaxial layer of gallium aluminum arsenide on the order of about one micrometer in thickness.
References Cited (Backward Citations)
US3675026A
Cited
US3931631A
Cited
US4051061A
Cited
US3994755A
Cited
US4126930A
Cited
US4026735A
Cited
US4163987A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-25 | 1984-05-26 | 1984-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-25 | 1988-05-26 | 1988-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-25 | 1992-05-26 | 1992-11-25 | $7700.00 | Window Closed / Lapsed |