Sodium-sulfur cell component protected by a high chromium alloy and method for forming
Assignee: Electric Power Research Institute
•
Filing: 1978-03-22
•
Granted: 1980-11-04
•
Expires: 1998-03-22
Abstract
Abstract A corrosion resistant contiguous duplex chromium-carbon-iron alloy layer bonded to a steel and other similar ferrocarbon substrate for use as a cell casing for a sodium-sulfur cell. The outer layer includes in excess of 60 weight % chromium. The duplex layer is formed by pack chromizing in a pack of chromium and ammonium halide at elevated temperatures in hydrogen or inert gas atmosphere.
Inventors
- 👤 Dong-Sil Park
- 👤 Debajyoti Chatterji
- 👤 Manfred W. Breiter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:53
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/3909; H01M50/00; H01M50/10; H01M50/116; H01M50/117; H01M50/119; H01M50/124; H01M50/126; H01M50/128; H01M50/131; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12847; Y10T428/12854
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
68 words
An electrically conductive, corrosion resistant component for a sodium-sulfur cell comprising a ferrocarbon substrate and a non-porous chromium-iron-carbon duplex alloy surface layer chemically diffusion-bonded to the substrate, said duplex alloy surface layer comprising contiguous outer and inner layers, said outer layer containing in excess of about 60 weight % chromium, and said inner layer containing less than about 50 weight % chromium in direct contact with the substrate.
Claim 2
Dependent Claim
68 words
An electrically conductive, corrosion resistant component for a sodium-sulfur cell comprising a ferrocarbon substrate and a non-porous chromium-iron-carbon duplex alloy surface layer chemically diffusion-bonded to the substrate, said duplex alloy surface layer comprising contiguous outer and inner layers, said outer layer containing in excess of about 60 weight % chromium, and said inner layer containing less than about 50 weight % chromium in direct contact with the substrate.
Claim 3
Dependent Claim
11 words
The component of claim 1 in which said ferrocarbon is steel.
Claim 4
Dependent Claim
14 words
The component of claim 2 in which said steel is a low carbon steel.
Claim 5
Dependent Claim
26 words
The component of claim 1 in the form of a cell casing in which said alloy layer is on the inner surface of the cell casing.
Claim 6
Dependent Claim
22 words
The component of claim 1 in which at least a portion of the chromium content of said alloy is in elemental form.
Claim 7
Dependent Claim
22 words
The component of claim 1 in which at least a portion of the chromium content of said alloy is in carbide form.
Claim 8
Dependent Claim
23 words
The method of claim 1 in which the temperature of diffusion is in a range from about 950° C. to about 1150° C.
Claim 9
Independent Claim
147 words
A method for forming a corrosion resistant layer on a ferrocarbon substrate comprising pack chromizing said substrate by totally submerging it in a solid pack of a chromium source and a halide activator at an elevated temperature to generate chromium halide at sufficient vapor pressure to diffuse the chromium into said substrate to form a duplex chromium-carbon-iron alloy layer chemically diffusion bonded to said substrate, said duplex alloy layer comprising contiguous outer and inner layers, said outer layer containing in excess of about 60 weight % chromium, and said inner layer containing less than about 50 weight % chromium in direct contact with the substrate, the vapor pressure of chromium halide in said solid pack being maintained at a predetermined level to form said duplex layer by providing a solid barrier over said pack and ferrocarbon substrate to inhibit loss of chromium halide vapor from said pack.
Claim 10
Independent Claim
147 words
A method for forming a corrosion resistant layer on a ferrocarbon substrate comprising pack chromizing said substrate by totally submerging it in a solid pack of a chromium source and a halide activator at an elevated temperature to generate chromium halide at sufficient vapor pressure to diffuse the chromium into said substrate to form a duplex chromium-carbon-iron alloy layer chemically diffusion bonded to said substrate, said duplex alloy layer comprising contiguous outer and inner layers, said outer layer containing in excess of about 60 weight % chromium, and said inner layer containing less than about 50 weight % chromium in direct contact with the substrate, the vapor pressure of chromium halide in said solid pack being maintained at a predetermined level to form said duplex layer by providing a solid barrier over said pack and ferrocarbon substrate to inhibit loss of chromium halide vapor from said pack.
Claim 11
Dependent Claim
41 words
The method of claim 8 in which the area of said ferrocarbon substrate to be chromized contains an open cavity at one end and said barrier is formed by disposing said substrate in said pack with said open end facing downwardly.
Claim 12
Dependent Claim
17 words
The method of claim 9 in which said substrate comprises a cell casing for a sodium-sulfur cell.
Claim 13
Dependent Claim
20 words
The method of claim 8 in which said barrier is formed by maintaining a lid on said pack during chromizing.
Claim 14
Dependent Claim
19 words
The method of claim 8 in which said process is carried out in hydrogen or an inert gas atmosphere.
Claim 15
Dependent Claim
15 words
The method of claim 8 in which said halide activator is selected from ammonium halides.
Claim 16
Dependent Claim
15 words
The method of claim 8 in which said ferrocarbon metal is a low carbon steel.
Claim 17
Dependent Claim
9 words
The product formed by the method of claim 8.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-04 | 1984-05-05 | 1984-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-04 | 1988-05-05 | 1988-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-04 | 1992-05-05 | 1992-11-04 | $7700.00 | Window Closed / Lapsed |