Method and structure for passivating a semiconductor device
Assignee: RCA Corp
•
Filing: 1979-04-16
•
Granted: 1980-09-23
•
Expires: 1999-04-16
Abstract
Abstract A method of passivating a silicon semiconductor device having at least one active component disposed in a crystalline region thereof comprises the steps of bombarding a surface of the crystalline region with ions to convert a part of the region adjacent the surface into an amorphous layer of graded crystallinity, and then exposing the amorphous layer to atomic hydrogen, whereby an integral layer of hydrogenated amorphous silicon is formed adjacent the crystalline region.
Inventors
- 👤 Jacques I. Pankove
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:05
CPC Classifications
H; H10; H10W; H10W74/00; H10W74/01; H10P; H10P36/00; H10P36/03; H10P95/00; H10P95/40; H10P95/402; H10W74/40; H10W74/481; Y; Y10; Y10S; Y10S148/00; Y10S148/093; Y10S438/00; Y10S438/958
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
66 words
A method of passivating a semiconductor device having at least one active component disposed in a crystalline region thereof comprising the steps of: converting a part of said region adjacent a surface of said crystalline region into an amorphous layer of graded crystallinity, and exposing said amorphous layer to atomic hydrogen, whereby an integral layer of hydrogenated amorphous semiconductor material is formed adjacent said crystalline region.
Claim 2
Independent Claim
66 words
A method of passivating a semiconductor device having at least one active component disposed in a crystalline region thereof comprising the steps of: converting a part of said region adjacent a surface of said crystalline region into an amorphous layer of graded crystallinity, and exposing said amorphous layer to atomic hydrogen, whereby an integral layer of hydrogenated amorphous semiconductor material is formed adjacent said crystalline region.
Claim 3
Dependent Claim
36 words
A method as recited in claim 1 wherein said converting step is performed by bombarding said surface with particles having sufficient energy to convert said part of said region into the amorphous layer of graded crystallinity.
Claim 4
Dependent Claim
33 words
A method as recited in claim 2 wherein said bombarding step is performed by subjecting said surface to a beam of ions having an energy in the range of 10 to 300 Kev.
Claim 5
Dependent Claim
44 words
A method as recited in claim 1 wherein said exposing step is performed by subjecting molecular hydrogen gas (H 2 ) to a glow discharge within a chamber at a pressure below about 5 torr and at a temperature lower than about 450° C.
Claim 6
Dependent Claim
20 words
A method as recited in claim 4 wherein said exposing step is performed for approximately one hour at 300° C.
Claim 7
Dependent Claim
35 words
A method as recited in claim 1 wherein said semiconductor device comprises a silicon wafer and wherein the integral layer of hydrogenated amorphous silicon contains between about 5 and about 50 atomic percent of hydrogen.
Claim 8
Dependent Claim
26 words
A method as recited in claim 6 wherein said integral layer of hydrogenated amorphous silicon has a thickness between about 0.01 μm and about 0.2 μm.
Claim 9
Dependent Claim
43 words
In a semiconductor device having at least one active component disposed in a crystalline region thereof, the improvement comprising an integral layer of hydrogenated amorphous semiconductor material adjacent said crystalline region, said layer having a gradually decreasing crystallinity away from said crystalline region.
Claim 10
Dependent Claim
43 words
In a semiconductor device having at least one active component disposed in a crystalline region thereof, the improvement comprising an integral layer of hydrogenated amorphous semiconductor material adjacent said crystalline region, said layer having a gradually decreasing crystallinity away from said crystalline region.
Claim 11
Dependent Claim
35 words
A semiconductor device as defined in claim 8 wherein said device comprises a silicon wafer and wherein the integral layer of hydrogenated amorphous silicon contains between about 5 and about 50 atomic percent of hydrogen.
Claim 12
Dependent Claim
27 words
A semiconductor device as defined in claim 9 wherein said integral layer of hydrogenated amorphous silicon has a thickness between about 0.01 μm and about 0.2 μm.
Claim 13
Dependent Claim
39 words
A semiconductor device as defined in claim 10 wherein said integral layer of hydrogenated amorphous silicon comprises one or more of the silicon hydride phases selected from the group consisting of Si:H, Si:H 2 , and Si:H 3 .
Claim 14
Dependent Claim
13 words
A semiconductor device made in accordance with the method recited in claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-23 | 1984-03-24 | 1984-09-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-23 | 1988-03-24 | 1988-09-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-23 | 1992-03-24 | 1992-09-23 | $7700.00 | Window Closed / Lapsed |