Process for the production of bead polymers
Assignee: Bayer AG
•
Filing: 1978-04-25
•
Granted: 1980-09-16
•
Expires: 1998-04-25
Abstract
Abstract A two-phase bead polymer having an average bead diameter of from 10μ to 150μ comprising (A) 88% to 99.5% by weight of a polymer of polymerized units of at least one methacrylic acid ester containing from 1 to 10 carbon atoms in the aliphatic, saturated alcohol component; and (B) 0.5% to 12% by weight of a polyurethane which has been obtained from (1) at least one dihydroxy compound, (2) a diisocyanate from the group comprising (a) aliphatic diisocyanates having a branched carbon skeleton of 7 to 26 carbon atoms, (b) cycloaliphatic diisocyanates and (c) aliphatic or cycloaliphatic diisocyanates modified by radical graft copolymerization with vinyl monomers, (3) an aliphatic or cycloaliphatic diamine and (4) a monofunctional chain terminator.
Inventors
- 👤 Carlhans Suling
- 👤 Gerhard Balle
- 👤 Michael Walkowiak
- 👤 Hans-Hermann Schulz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:45
CPC Classifications
C; C08; C08F; C08F299/00; C08F299/02; C08F299/06; C08F283/00; C08F283/006; C08F290/00; C08F290/02; C08F290/06; C08F290/067; Y; Y10; Y10S; Y10S525/00; Y10S525/92
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
119 words
A two-phase bead polymer having an average bead diameter of from 10μ to 150μ comprising (A) 88% to 99.5% by weight of a polymer of polymerised units of at least one methacrylic acid ester containing from 1 to 10 carbon atoms in the aliphatic, saturated alcohol component; and (B) 0.5% to 12% by weight of a monomer-soluble polyurethane which has been obtained from (1) at least one dihydroxy compound, (2) a diisocyanate from the group comprising (a) aliphatic diisocyanates having a branched carbon skeleton of 7 to 26 carbon atoms, (b) isophorone diisocyanate and (c) aliphatic or cycloaliphatic diisocyanates modified by radical graft copolymerisation with vinyl monomers, (3) an aliphatic or cycloaliphatic diamine and (4) a monofunctional chain terminator.
Claim 2
Dependent Claim
119 words
A two-phase bead polymer having an average bead diameter of from 10μ to 150μ comprising (A) 88% to 99.5% by weight of a polymer of polymerised units of at least one methacrylic acid ester containing from 1 to 10 carbon atoms in the aliphatic, saturated alcohol component; and (B) 0.5% to 12% by weight of a monomer-soluble polyurethane which has been obtained from (1) at least one dihydroxy compound, (2) a diisocyanate from the group comprising (a) aliphatic diisocyanates having a branched carbon skeleton of 7 to 26 carbon atoms, (b) isophorone diisocyanate and (c) aliphatic or cycloaliphatic diisocyanates modified by radical graft copolymerisation with vinyl monomers, (3) an aliphatic or cycloaliphatic diamine and (4) a monofunctional chain terminator.
Claim 3
Dependent Claim
76 words
A two-phase bead polymer as claimed in claim 1 wherein the component (A) comprises up to 30% by weight of copolymerised units of at least one monomer comprising one or more of acrylic acid esters containing from 1 to 10 carbon atoms in the aliphatic, saturated alcohol component, hydroxyalkyl esters of acrylic and methacrylic acids containing from 2 to 4 carbon in the alkyl group, styrene, vinylacetate, acrylamide, methacrylamide acrylic acid, methacrylic acid and itaconic acid.
Claim 4
Dependent Claim
19 words
A two-phase bead polymer as claimed in claim 1 wherein the monofunctional claim terminator, component (B4) contains unsaturated groups.
Claim 5
Dependent Claim
51 words
A two-phase bead polymer as claimed in claim 1, wherein component (B1) is a substantially linear bifunctional hydroxyl compound having a molecular weight Mn (number average) of from 400 to 6000 and a glass transition temperature of ≦-20° C. from the group comprising polyesters, polyethers, polyacetals, polycarbonates, polyester amides and polyamides.
Claim 6
Dependent Claim
18 words
A two-phase bead polymer as claimed in claim 1, wherein component (B1) is a polyester or polyether diol.
Claim 7
Dependent Claim
62 words
A two-phase bead polymer as claimed in claim 4, wherein component (B1) also contains a linear or branched aliphatic diol containing from 2 to 8 carbon atoms in the molecule or a lower oligomer thereof having a molecular weight Mn of from 62 to 400 in a quantity of from 0.5 to 25 mole % in the mixture of the components B1.
Claim 8
Dependent Claim
31 words
A two-phase bead polymer as claimed in claim 1, wherein component B4 is a compound which is free from olefinically unsaturated polymerisable groups and which contains at least one hydroxyl group.
Claim 9
Dependent Claim
36 words
A two-phase bead polymer as claimed in claim 1, wherein component B4 is a lower, aliphatic saturated alcohol containing from 1 to 4 carbon atoms or an aliphatic monoamine containing from 1 to 6 carbon atoms.
Claim 10
Dependent Claim
46 words
A two-phase bead polymer as claimed in claim 1, wherein component B4 is allyl alcohol or at least one hydroxy alkyl ester containing from 2 to 4 carbon atoms in the alkyl group of an α,β-monoolefinically unsaturated carboxylic acid containing from 3 to 5 carbon atoms.
Claim 11
Dependent Claim
15 words
A two-phase bead polymer as claimed in claim 1, wherein component B4 is 2-hydroxyethyl methacrylate.
Claim 12
Dependent Claim
202 words
A process for producing a two-phase bead polymer as claimed in claim 1, wherein (A 1 ) 88 to 110 parts by weight of at least one methacrylic acid ester containing from 1 to 10 carbon atoms in the aliphatic, saturated alcohol component, and (B 1 ) 0.5 to 12 parts by weight of a monomer soluble polyurethane which has been obtained from (1) at least one dihydroxy compound, (2) a diisocyanate from the group comprising (a) aliphatic diisocyanates having a branched carbon skeleton of 7 to 36 carbon atoms, (b) isophorone diisocyanate and (c) aliphatic or cycloaliphatic diisocyanates modified by radical graft copolymerisation with vinyl monomers, (3) aliphatic or cycloaliphatic diamines and (4) a monofunctional chain terminator optionally containing unsaturated groups, is polymerised in aqueous medium, 0.7 to 3.5 parts by wt. of aqueous medium being present per part by weight of the solutions of (A 1 ) and (B 1 ), under the conditions of bead polymerisation in the presence of from 0.5 to 2.5% by weight, based on polymerisable compounds, of at least one monomer-soluble radical former, from 0.5 to 100% by weight, based on polymerisable compounds, of a dispersant at a temperature of from 20° to 120° C.
Claim 13
Dependent Claim
69 words
A process, as claimed in claim 11, wherein the component (A 1 ) comprises up to 40 parts by wt. of at least one monomer comprising acrylic acid esters containing from 1 to 10 carbon atoms in the aliphatic, saturated alcohol component, hydroxy alkyl esters of acrylic or methacrylic acid containing from 2 to 4 carbon atoms in the alkyl group, styrene, vinylacetate, (meth)-acrylamide, (meth)-acrylic acid and itaconic acid.
Claim 14
Dependent Claim
16 words
A process as claimed in claim 11 wherein the polymerisation is carried out at normal pressure.
Claim 15
Dependent Claim
21 words
A process as claimed in claim 11, wherein the polymerisation is carried out at a pressure of up to 20 bars.
Claim 16
Dependent Claim
31 words
A process as claimed in claim 11, wherein the polymerisation is carried out in the presence of from 0.01 to 2% by weight based on polymerisable compounds of an anionic emulsifier.
Claim 17
Dependent Claim
23 words
A process as claimed in claim 11, wherein at least one water-insoluble salt of an alkaline earth metal is used as the dispersant.
Claim 18
Dependent Claim
15 words
A process as claimed in claim 11, wherein MgCO 3 is used as the dispersant.
Claim 19
Dependent Claim
15 words
A process as claimed in claim 11, wherein polymethacrylic acid is used as the dispersant.
Claim 20
Dependent Claim
15 words
A process as claimed in claim 11, wherein polyvinyl alcohol is used as the dispersant.
Claim 21
Dependent Claim
15 words
A process as claimed in claim 11, wherein polyvinyl pyrrolidone is used as the dispersant.
References Cited (Backward Citations)
US3509234A
Cited
US3677920A
Cited
US3700752A
Cited
US3641199A
Cited
US3962370A
Cited
US3907751A
Cited
GB1373182A
Cited
US3868431A
Cited
US4089763A
Cited
US3876726A
Cited
US3968089A
Cited
US4073828A
Cited
US4129641A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-16 | 1984-03-17 | 1984-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-16 | 1988-03-17 | 1988-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-16 | 1992-03-17 | 1992-09-16 | $7700.00 | Window Closed / Lapsed |