Substrate with multi-layer nonstick coating
Assignee: EIDP Inc
•
Filing: 1978-12-29
•
Granted: 1980-09-16
•
Expires: 1998-12-29
Abstract
Abstract A three-coat system for use on bakeware which has a silvery appearance and can be cured at low temperatures. First, an epoxide-formaldehyde-nitrogen resin primer, which may contain aluminum flake, is applied to the substrate, then a reactive silicone-epoxy coat containing talc and coarse aluminum flake is applied. Finally, a less reactive silicone resin containing coarse aluminum flake, but no other pigment is applied. The two final coats are applied directly on the preceding coat after only ambient temperature air drying. After the final coat is applied, the coated article is baked at temperatures that need not exceed 275° C.
Inventors
- 👤 Jacques M. L. Berghmans
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:03
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/08; A; A47; A47J; A47J36/00; A47J36/02; B05D7/00; B05D7/50; B05D7/56; B05D7/57; B05D7/574; B05D7/58; B05D7/584; C; C09; C09D; C09D183/00; C09D183/04; B05D2601/00; B05D2601/02; B05D2601/08; B05D2601/20; B05D2601/28; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/251; Y10T428/256; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522; Y10T428/31652; Y10T428/31663; Y10T428/31678; Y10T428/31688; Y10T428/31942
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
98 words
An article suitable for use as bakeware comprising a heat-resistant substrate coated with a multi-layered coating comprising: a primer coat comprising an epoxide-formaldehyde-nitrogen resin and optionally aluminum flake, an intermediate coat comprising a polymethylphenylsiloxane resin derived from a cross-linkable precondensate having a silicon-bonded hydroxyl content of at least about 3%, based on the weight of the precondensate, an epoxy resin, talc, and aluminum flake, and a topcoat consisting essentially of a polymethylphenylsiloxane resin derived from a cross-linkable precondensate having a silicon-bonded hydroxyl content of about 2 to 4%, based on the weight of the precondensate, and aluminum flake.
Claim 2
Dependent Claim
98 words
An article suitable for use as bakeware comprising a heat-resistant substrate coated with a multi-layered coating comprising: a primer coat comprising an epoxide-formaldehyde-nitrogen resin and optionally aluminum flake, an intermediate coat comprising a polymethylphenylsiloxane resin derived from a cross-linkable precondensate having a silicon-bonded hydroxyl content of at least about 3%, based on the weight of the precondensate, an epoxy resin, talc, and aluminum flake, and a topcoat consisting essentially of a polymethylphenylsiloxane resin derived from a cross-linkable precondensate having a silicon-bonded hydroxyl content of about 2 to 4%, based on the weight of the precondensate, and aluminum flake.
Claim 3
Dependent Claim
58 words
The article of claim 1 wherein the epoxide-formaldehyde-nitrogen resin of the primer is the reaction product of an epoxy resin and a urea-formaldehyde resin wherein the epoxy resin is a condensation of epichlorohydrin and bisphenol "A" having an epoxy equivalent weight of 1700-2500 and the urea formaldehyde resin has a combined molar ratio of urea:formaldehyde:butanol of about 1:2:1.
Claim 4
Dependent Claim
20 words
The article of claim 1 wherein the polymethylphenylsiloxane resin of the intermediate coat has a hydroxyl content of about 5%.
Claim 5
Dependent Claim
17 words
The article of claim 1 wherein the topcoat does not contain any pigment other than aluminum flake.
Claim 6
Dependent Claim
85 words
The article of claim 1 wherein the epoxide-formaldehyde-nitrogen resin of the primer is the reaction product of an epoxy resin and a urea-formaldehyde resin wherein the epoxy resin is a condensation product of epichlorohydrin and bisphenol "A" having an epoxy equivalent weight of 1700-2500 and the urea formaldehyde resin has a combined molar ratio of urea:formaldehyde:butanol of about 1:2:1; the polymethylphenylsiloxane resin of the intermediate coat has a hydroxyl content of about 5%; and the topcoat does not contain any pigment other than aluminum flake.
Claim 7
Dependent Claim
14 words
The article of claim 1 wherein the intermediate coat also contains titania-coated mica pigment.
References Cited (Backward Citations)
US2864722A
Cited
US3030234A
Cited
US2995467A
Cited
US3202542A
Cited
US3087828A
Cited
US3087829A
Cited
US3505099A
Cited
US3532528A
Cited
US3666138A
Cited
US3687879A
Cited
US3749593A
Cited
US4028339A
Cited
US4046937A
Cited
US4076676A
Cited
US4105613A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-16 | 1984-03-17 | 1984-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-16 | 1988-03-17 | 1988-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-16 | 1992-03-17 | 1992-09-16 | $7700.00 | Window Closed / Lapsed |